Developing efficient and stable cathodes for low-temperature solid oxide fuel cells(LT-SOFCs) is of great importance for the practical commercialization.Herein,we propose a series of Sm-modified Bi_(0.7-x)Sm_xSr_(0.3)...Developing efficient and stable cathodes for low-temperature solid oxide fuel cells(LT-SOFCs) is of great importance for the practical commercialization.Herein,we propose a series of Sm-modified Bi_(0.7-x)Sm_xSr_(0.3)FeO_(3-δ) perovskites as highly-active catalysts for LT-SOFCs.Sm doping can significantly enhance the electrocata lytic activity and chemical stability of cathode.At 600℃,Bi_(0.675)Sm_(0.025)Sr_(0.3)FeO_(3-δ)(BSSF25) cathode has been found to be the optimum composition with a polarization resistance of 0.098 Ω cm^2,which is only around 22.8% of Bi_(0.7)Sr_(0.3)FeO_(3-δ)(BSF).A full cell utilizing BSSF25 displays an exceptional output density of 790 mW cm^(-2),which can operate continuously over100 h without obvious degradation.The remarkable electrochemical performance observed can be attributed to the improved O_(2) transport kinetics,superior surface oxygen adsorption capacity,as well as O_(2)p band centers in close proximity to the Fermi level.Moreover,larger average bonding energy(ABE) and the presence of highly acidic Bi,Sm,and Fe ions restrict the adsorption of CO_(2) on the cathode surface,resulting in excellent CO_(2) resistivity.This work provides valuable guidance for systematic design of efficient and durable catalysts for LT-SOFCs.展开更多
In this work,La_(2)NiO_(4+δ)-Ce_(0.55)La_(0.45)O_(2−δ)(denoted as LNO-xLDC)with various LDC contents(x=0,10,20,30,and 40 wt%)were prepared and evaluated as bifunctional oxygen electrodes for reversible solid oxide c...In this work,La_(2)NiO_(4+δ)-Ce_(0.55)La_(0.45)O_(2−δ)(denoted as LNO-xLDC)with various LDC contents(x=0,10,20,30,and 40 wt%)were prepared and evaluated as bifunctional oxygen electrodes for reversible solid oxide cells(RSOCs).Compared with the pure LNO,the optimum composition of LNO-30LDC exhibited the lowest polarization resistance(Rp)of 0.53 and 0.12Ω·cm^(2)in air at 650 and 750℃,respectively.The enhanced electrochemical performance of LNO-30LDC oxygen electrode was mainly attributed to the extended triple phase boundary and more oxygen ionic transfer channels.The hydrogen electrode supported single cell with LNO-30LDC oxygen electrode displayed peak power densities of 276,401,and 521 mW·cm^(−2)at 700,750,and 800℃,respectively.Moreover,the electrolysis current density of the single cell demonstrated 526.39 mA·cm^(−2) under 1.5 V at 800℃,and the corresponding hydrogen production rate was 220.03 mL·cm^(−2)·h^(−1).The encouraging results indicated that LNO-30LDC was a promising bifunctional oxygen electrode material for RSOCs.展开更多
基金supported by the National Natural Science Foundation of China(22279025,21773048)the Natural Science Foundation of Heilongjiang Province(LH2021A013)+1 种基金the Sichuan Science and Technology Program(2021YFSY0022)the Fundamental Research Funds for the Central Universities(2023FRFK06005,HIT.NSRIF202204)。
文摘Developing efficient and stable cathodes for low-temperature solid oxide fuel cells(LT-SOFCs) is of great importance for the practical commercialization.Herein,we propose a series of Sm-modified Bi_(0.7-x)Sm_xSr_(0.3)FeO_(3-δ) perovskites as highly-active catalysts for LT-SOFCs.Sm doping can significantly enhance the electrocata lytic activity and chemical stability of cathode.At 600℃,Bi_(0.675)Sm_(0.025)Sr_(0.3)FeO_(3-δ)(BSSF25) cathode has been found to be the optimum composition with a polarization resistance of 0.098 Ω cm^2,which is only around 22.8% of Bi_(0.7)Sr_(0.3)FeO_(3-δ)(BSF).A full cell utilizing BSSF25 displays an exceptional output density of 790 mW cm^(-2),which can operate continuously over100 h without obvious degradation.The remarkable electrochemical performance observed can be attributed to the improved O_(2) transport kinetics,superior surface oxygen adsorption capacity,as well as O_(2)p band centers in close proximity to the Fermi level.Moreover,larger average bonding energy(ABE) and the presence of highly acidic Bi,Sm,and Fe ions restrict the adsorption of CO_(2) on the cathode surface,resulting in excellent CO_(2) resistivity.This work provides valuable guidance for systematic design of efficient and durable catalysts for LT-SOFCs.
基金Science and Technology Project of Jiangxi Provincial Education Department(GJJ190734)The National Natural Science Foundation of China(51962015)。
文摘In this work,La_(2)NiO_(4+δ)-Ce_(0.55)La_(0.45)O_(2−δ)(denoted as LNO-xLDC)with various LDC contents(x=0,10,20,30,and 40 wt%)were prepared and evaluated as bifunctional oxygen electrodes for reversible solid oxide cells(RSOCs).Compared with the pure LNO,the optimum composition of LNO-30LDC exhibited the lowest polarization resistance(Rp)of 0.53 and 0.12Ω·cm^(2)in air at 650 and 750℃,respectively.The enhanced electrochemical performance of LNO-30LDC oxygen electrode was mainly attributed to the extended triple phase boundary and more oxygen ionic transfer channels.The hydrogen electrode supported single cell with LNO-30LDC oxygen electrode displayed peak power densities of 276,401,and 521 mW·cm^(−2)at 700,750,and 800℃,respectively.Moreover,the electrolysis current density of the single cell demonstrated 526.39 mA·cm^(−2) under 1.5 V at 800℃,and the corresponding hydrogen production rate was 220.03 mL·cm^(−2)·h^(−1).The encouraging results indicated that LNO-30LDC was a promising bifunctional oxygen electrode material for RSOCs.