In situ melt polycondensation was proposed to prepare biodegradable aliphatic-aromatic copolyesters/nano-SiO2 hybrids based on terephthalic acid （TPA）, poly（L-lactic acid） oligomer （OLLA）, 1,4-butanediol （BDO）...In situ melt polycondensation was proposed to prepare biodegradable aliphatic-aromatic copolyesters/nano-SiO2 hybrids based on terephthalic acid （TPA）, poly（L-lactic acid） oligomer （OLLA）, 1,4-butanediol （BDO） and nano-SiO2. TEM and FT-IR characterizations confirmed that TPA, OLLA and BDO copolymerized to obtain biodegradable copolyesters, poly（butylene terepbthalate-co-lactate） （PBTL）, and the abundant hydroxyl groups on the surface of nano-SiO2 provided potential sites for in situ grafting with the simultaneous resulted PBTL. The nano-SiO2 particles were chemically wrapped with PBTL to form PBTL/nano- SiO2 hybrids. Due to the good dispersion and interfacial adhesion of nano-SiO2 particles with the copolyester matrix, the tensile strength and the Young＇s modulus increased from 5.4 and 5.6 MPa for neat PBTL to 16 and 390 MPa for PBTL/nano-SiO2 hybrids with 5 wt.% nano-SiO2, respectively. The mechanical properties of PBTL/nano-SiO2 hybrids were substantially improved.展开更多
基金support from the Natural Science Foundation of Ningbo(No.2007A610030)Science and Technology Department of Zhejiang Province(No.2008C11092-2)
文摘In situ melt polycondensation was proposed to prepare biodegradable aliphatic-aromatic copolyesters/nano-SiO2 hybrids based on terephthalic acid （TPA）, poly（L-lactic acid） oligomer （OLLA）, 1,4-butanediol （BDO） and nano-SiO2. TEM and FT-IR characterizations confirmed that TPA, OLLA and BDO copolymerized to obtain biodegradable copolyesters, poly（butylene terepbthalate-co-lactate） （PBTL）, and the abundant hydroxyl groups on the surface of nano-SiO2 provided potential sites for in situ grafting with the simultaneous resulted PBTL. The nano-SiO2 particles were chemically wrapped with PBTL to form PBTL/nano- SiO2 hybrids. Due to the good dispersion and interfacial adhesion of nano-SiO2 particles with the copolyester matrix, the tensile strength and the Young＇s modulus increased from 5.4 and 5.6 MPa for neat PBTL to 16 and 390 MPa for PBTL/nano-SiO2 hybrids with 5 wt.% nano-SiO2, respectively. The mechanical properties of PBTL/nano-SiO2 hybrids were substantially improved.