Titanium mineral was prepared from vanadium titanomagnetite concentrates by hydrogen reduction and acid leaching.The leaching behaviors of elements like Fe,V,Mn,Al,Mg,Ca,and Si were highly related to the reduction deg...Titanium mineral was prepared from vanadium titanomagnetite concentrates by hydrogen reduction and acid leaching.The leaching behaviors of elements like Fe,V,Mn,Al,Mg,Ca,and Si were highly related to the reduction degree.The phase compositions of the reduced materials and the leached residues were analyzed by XRD to identify the effect of reduction degree on the leaching mechanisms.The results showed that the concentrates were reduced to iron metal and titanomagnetite at 800-1000°C for 0.5 h,and the above elements of Fe and impurities were easily leached.Deeper reduction led to the formation of ilmenite and Mg-Al spinel,which hindered leaching.Mg-bearing anosovite appeared in the further reduced materials,and the leaching rates of impurities became much lower.An upgraded titanium mineral with a normalized TiO_(2) grade of 70.3%was achieved by H_(2) reduction at 850°C for 0.5 h and acid leaching,which is a satisfactory Ti resource for the preparation of titanium oxide by sulfate process.展开更多
基金financially supported by the Beijing Natural Science Foundation, China (No. 2192056)the National Natural Science Foundation of China (No. 51771179)+1 种基金the National Key R&D Program of China (No. 2018YFC1900505)The financial supports from the Youth Innovation Promotion Association CAS and the CAS Interdisciplinary Innovation Team
文摘Titanium mineral was prepared from vanadium titanomagnetite concentrates by hydrogen reduction and acid leaching.The leaching behaviors of elements like Fe,V,Mn,Al,Mg,Ca,and Si were highly related to the reduction degree.The phase compositions of the reduced materials and the leached residues were analyzed by XRD to identify the effect of reduction degree on the leaching mechanisms.The results showed that the concentrates were reduced to iron metal and titanomagnetite at 800-1000°C for 0.5 h,and the above elements of Fe and impurities were easily leached.Deeper reduction led to the formation of ilmenite and Mg-Al spinel,which hindered leaching.Mg-bearing anosovite appeared in the further reduced materials,and the leaching rates of impurities became much lower.An upgraded titanium mineral with a normalized TiO_(2) grade of 70.3%was achieved by H_(2) reduction at 850°C for 0.5 h and acid leaching,which is a satisfactory Ti resource for the preparation of titanium oxide by sulfate process.