The fatigue damage accumulation of [±20°] laminated steel cord reinforced rubber composite under T-T loading was studied. Results indicate that the increase in the cyclic maximum strain exhibits three-stage ...The fatigue damage accumulation of [±20°] laminated steel cord reinforced rubber composite under T-T loading was studied. Results indicate that the increase in the cyclic maximum strain exhibits three-stage tendency in the process of fatigue. The macroscopic fatigue damage initiates from the ends of steel cords in the form of cylindrical crack. Damage propagates along with the increase in crack numbers, the cord/matrix interface debonding and the growth of interply cracks. By using the dynamic creep as parameter, a linear fatigue damage accumulation model was established. This model can be used under dual loading conditions to estimate the residual fatigue life of the specimen.展开更多
基金The authors gratefully acknowledge the financial support by the National Natural Sciece Foundation of China under grant No. 10302008the Science Foundation of Heilongjiang Province under project No. A0309.
文摘The fatigue damage accumulation of [±20°] laminated steel cord reinforced rubber composite under T-T loading was studied. Results indicate that the increase in the cyclic maximum strain exhibits three-stage tendency in the process of fatigue. The macroscopic fatigue damage initiates from the ends of steel cords in the form of cylindrical crack. Damage propagates along with the increase in crack numbers, the cord/matrix interface debonding and the growth of interply cracks. By using the dynamic creep as parameter, a linear fatigue damage accumulation model was established. This model can be used under dual loading conditions to estimate the residual fatigue life of the specimen.