Ferronickel enrichment and extraction from nickel laterite ore were studied through reduction and magnetic separation. Reduction experiments were performed using hydrogen and carbon monoxide as reductants at different...Ferronickel enrichment and extraction from nickel laterite ore were studied through reduction and magnetic separation. Reduction experiments were performed using hydrogen and carbon monoxide as reductants at different temperatures （700-1000℃）. Magnetic separa- tion of the reduced products was conducted using a SLon-100 cycle pulsating magnetic separator （1.2 T）. Composition analysis indicates that the nickel laterite ore contains a total iron content of 22.50wt% and a total nickel content of 1.91wt%. Its mineral composition mainly con- sists of serpentine, hortonolite, and goethite. During the reduction process, the grade of nickel and iron in the products increases with in- creasing reduction temperature. Although a higher temperature is more favorable for reduction, the temperature exceeding 1000℃ results in sintering of the products, preventing magnetic separation. After magnetic separation, the maximum total nickel and iron concentrations are 5.43wt% and 56.86wt%, and the corresponding recovery rates are 84.38% and 53.76%, respectively.展开更多
文摘Ferronickel enrichment and extraction from nickel laterite ore were studied through reduction and magnetic separation. Reduction experiments were performed using hydrogen and carbon monoxide as reductants at different temperatures （700-1000℃）. Magnetic separa- tion of the reduced products was conducted using a SLon-100 cycle pulsating magnetic separator （1.2 T）. Composition analysis indicates that the nickel laterite ore contains a total iron content of 22.50wt% and a total nickel content of 1.91wt%. Its mineral composition mainly con- sists of serpentine, hortonolite, and goethite. During the reduction process, the grade of nickel and iron in the products increases with in- creasing reduction temperature. Although a higher temperature is more favorable for reduction, the temperature exceeding 1000℃ results in sintering of the products, preventing magnetic separation. After magnetic separation, the maximum total nickel and iron concentrations are 5.43wt% and 56.86wt%, and the corresponding recovery rates are 84.38% and 53.76%, respectively.