Calcium-magnesium-alumina-silicate (CMAS) corrosion is an important cause for thermal barrier coating (TBC) failure,which has attracted increased attentions.In this study,some thermal barrier coating (TBC) materials i...Calcium-magnesium-alumina-silicate (CMAS) corrosion is an important cause for thermal barrier coating (TBC) failure,which has attracted increased attentions.In this study,some thermal barrier coating (TBC) materials including YSZ (yttria partially stabilized zirconia),GdPO_(4),and LaPO_(4) were prepared into bulks,and the effects of their surface roughness on wettability and spreading characteristics of molten CMAS were investigated.As-fabricated and polished bulks with different surface roughness were exposed to CMAS corrosion at 1250 ℃ for 1 and 4 h,following by macro and micro observations.Results revealed that compared with the as-fabricated bulks,molten CMAS on the polished samples had lower wettability and a smaller spreading area,mainly attributable to the reduced capillary force to drive the melt spreading.Meanwhile,GdPO_(4) and LaPO_(4) bulks exhibited lower CMAS wettability than YSZ bulk.It is thus considered that reducing the surface roughness is beneficial to CMAS corrosion resistance of TBCs.展开更多
基金This research is sponsored by the National Natural Science Foundation of China(Grant No.51971156).
文摘Calcium-magnesium-alumina-silicate (CMAS) corrosion is an important cause for thermal barrier coating (TBC) failure,which has attracted increased attentions.In this study,some thermal barrier coating (TBC) materials including YSZ (yttria partially stabilized zirconia),GdPO_(4),and LaPO_(4) were prepared into bulks,and the effects of their surface roughness on wettability and spreading characteristics of molten CMAS were investigated.As-fabricated and polished bulks with different surface roughness were exposed to CMAS corrosion at 1250 ℃ for 1 and 4 h,following by macro and micro observations.Results revealed that compared with the as-fabricated bulks,molten CMAS on the polished samples had lower wettability and a smaller spreading area,mainly attributable to the reduced capillary force to drive the melt spreading.Meanwhile,GdPO_(4) and LaPO_(4) bulks exhibited lower CMAS wettability than YSZ bulk.It is thus considered that reducing the surface roughness is beneficial to CMAS corrosion resistance of TBCs.