The massive stacking of the coal gangue (CG) in the coal mining process, discarded industrial zeolite waste (IZW) and agricultural corn straw (CS) has caused serious environmental pollution and resource waste. To achi...The massive stacking of the coal gangue (CG) in the coal mining process, discarded industrial zeolite waste (IZW) and agricultural corn straw (CS) has caused serious environmental pollution and resource waste. To achieve the recycling of solid waste, an economical method for synthesizing ultramarine blue pigment using a two-step calcination process of the CG/IZW/Na_(2)CO_(3)/S/CS with the mass rates of 1.50: 0.50: 2.50: 3.50: 1.00 (the first stage at 400℃ for 0.50 h and the second stage at 900℃ for 2.00 h) is proposed in this paper. The structure and composition of the synthesis ultramarine blue pigment were characterized by XRD, FT-IR, Raman, as well as SEM technologies, and results showed it had a sodalite structure containing S_(3)^(−) and S_(2)^(−) radicals. Furthermore, SiO2 (1.20 mL of tetraethyl orthosilicate (TEOS) as the precursor and 4.50 mL of NH_(3)·H_(2)O as the catalyst) coated the synthesis ultramarine blue pigment (1.00 g) was successfully synthesized by sol-gel technique to improve the acid resistance of the pigment (pH=2.50-3.00). This new method of preparing ultramarine blue pigments not only achieves resource reuse at a low cost but also improves the acid rain resistance of the pigments.展开更多
基金supported by the National Key Research and Development Program of China(2017YFD0800301)Liaoning Province Education Administration(No.LJ2020008,LQ2020023,and LQ2020027)Program for Liaoning Innovative Research Team in University(LT2020016).
文摘The massive stacking of the coal gangue (CG) in the coal mining process, discarded industrial zeolite waste (IZW) and agricultural corn straw (CS) has caused serious environmental pollution and resource waste. To achieve the recycling of solid waste, an economical method for synthesizing ultramarine blue pigment using a two-step calcination process of the CG/IZW/Na_(2)CO_(3)/S/CS with the mass rates of 1.50: 0.50: 2.50: 3.50: 1.00 (the first stage at 400℃ for 0.50 h and the second stage at 900℃ for 2.00 h) is proposed in this paper. The structure and composition of the synthesis ultramarine blue pigment were characterized by XRD, FT-IR, Raman, as well as SEM technologies, and results showed it had a sodalite structure containing S_(3)^(−) and S_(2)^(−) radicals. Furthermore, SiO2 (1.20 mL of tetraethyl orthosilicate (TEOS) as the precursor and 4.50 mL of NH_(3)·H_(2)O as the catalyst) coated the synthesis ultramarine blue pigment (1.00 g) was successfully synthesized by sol-gel technique to improve the acid resistance of the pigment (pH=2.50-3.00). This new method of preparing ultramarine blue pigments not only achieves resource reuse at a low cost but also improves the acid rain resistance of the pigments.