Hot-dip galvanizing provides excellent corrosion and wear resistance for steels.However,the equipment itself,such as the steel roller,immerged in corrosive molten zinc suffers serious material loss during steel's ...Hot-dip galvanizing provides excellent corrosion and wear resistance for steels.However,the equipment itself,such as the steel roller,immerged in corrosive molten zinc suffers serious material loss during steel's production.Its protection has become the main technique problem in modern galvanizing line.In this study,an enamel coating was designed and prepared.Its tribo-corrosion in molten zinc alloy(Zn-0.2 wt%Al)at 460℃was investigated in comparison with the traditional WC-12 Co composite coating and the 316 stainless steel.Results indicate that the steel suffers serious material damage.Various corrosion products of Fe_(2) Al_(5) Znx form at the worn surface and the wear scar has reached 200μm deep after merely 5 h tribo-corrosion.Though the two coatings provide an improved tribo-corrosion resistance,for the WC-12 Co coating,its chemical reaction with the molten zinc increases brittleness and promotes cracking.The synergistic wear and corrosion cause its degradation.The enamel coating performs better during tribo-corrosion.It is chemically stable in molten zinc thus able to provide high corrosion resistance.In addition,the amorphous[Si04]network and the self-lubricating CaF_(2) crystallite help it to build up an intact amorphous glaze layer readily at surface on sliding,leading to a reduced wear loss.During the whole tribo-corrosion process,the enamel coating is completely free of cracking,and the Zn penetration is inhibited.展开更多
基金financially supported by the National Key R&D Program of China under Grant No.2017YFB0306100the National Natural Science Foundation of China under Grant No.51871051+2 种基金the Excellent Youth Foundation of Liaoning Province under Grant No.2019-YQ-03the Fundamental Research Funds for the Central Universities under Grant No.N180212008by the Ministry of Industry and Information Technology Project(No.MJ-2017-J-99)。
文摘Hot-dip galvanizing provides excellent corrosion and wear resistance for steels.However,the equipment itself,such as the steel roller,immerged in corrosive molten zinc suffers serious material loss during steel's production.Its protection has become the main technique problem in modern galvanizing line.In this study,an enamel coating was designed and prepared.Its tribo-corrosion in molten zinc alloy(Zn-0.2 wt%Al)at 460℃was investigated in comparison with the traditional WC-12 Co composite coating and the 316 stainless steel.Results indicate that the steel suffers serious material damage.Various corrosion products of Fe_(2) Al_(5) Znx form at the worn surface and the wear scar has reached 200μm deep after merely 5 h tribo-corrosion.Though the two coatings provide an improved tribo-corrosion resistance,for the WC-12 Co coating,its chemical reaction with the molten zinc increases brittleness and promotes cracking.The synergistic wear and corrosion cause its degradation.The enamel coating performs better during tribo-corrosion.It is chemically stable in molten zinc thus able to provide high corrosion resistance.In addition,the amorphous[Si04]network and the self-lubricating CaF_(2) crystallite help it to build up an intact amorphous glaze layer readily at surface on sliding,leading to a reduced wear loss.During the whole tribo-corrosion process,the enamel coating is completely free of cracking,and the Zn penetration is inhibited.