To improve the interfacial conductivity and corrosion resistance of AISI430 stainless steel(430 SS)as bipolar plates for direct formic acid fuel cells(DFAFCs),a Nb_(0.8)Zr_(0.2) layer has been successfully synthesized...To improve the interfacial conductivity and corrosion resistance of AISI430 stainless steel(430 SS)as bipolar plates for direct formic acid fuel cells(DFAFCs),a Nb_(0.8)Zr_(0.2) layer has been successfully synthesized via the pulsed laser deposition(PLD)technique on the surface of 430 SS.This Nb_(0.8)Zr_(0.2) layer is smooth,uniform,and comparatively compact without any surface flaw and micropore.Investigation under the simulated anodic environment of DFAFCs(0.05 M H_(2)SO_(4)+2 ppm HF+10 M HCOOH at 70℃)shows that the corrosion resistance of 430 SS is obviously ameliorated after the PLD modification.In addition,the interfacial contact resistance of Nb_(0.8)Zr_(0.2)-430 SS(6.0 mΩcm^(2))is much smaller than that of bare 430 SS(151.3 mΩcm^(2))at the clamping force of 140 N cm^(-2).Besides,diff erent from the highly increased interfacial contact resistance of bare 430 SS,the Nb_(0.8)Zr_(0.2)-430 SS shows a minor increase resistance after potentiostatic tests in simulated anodic environment of DFAFCs.展开更多
基金financially supported by the National Natural Science Foundation of China(Nos.51962027,51974167,21968022,and 21868022)the Natural Science Foundation of Inner Mongolia(No.2019BS02002)+1 种基金the Project of Science Foundation of the Educational Department of Inner Mongolia(No.NJZY19135)the Inner Mongolia University of Science and Technology Innovation Fund(No.2019QDL-B23)。
文摘To improve the interfacial conductivity and corrosion resistance of AISI430 stainless steel(430 SS)as bipolar plates for direct formic acid fuel cells(DFAFCs),a Nb_(0.8)Zr_(0.2) layer has been successfully synthesized via the pulsed laser deposition(PLD)technique on the surface of 430 SS.This Nb_(0.8)Zr_(0.2) layer is smooth,uniform,and comparatively compact without any surface flaw and micropore.Investigation under the simulated anodic environment of DFAFCs(0.05 M H_(2)SO_(4)+2 ppm HF+10 M HCOOH at 70℃)shows that the corrosion resistance of 430 SS is obviously ameliorated after the PLD modification.In addition,the interfacial contact resistance of Nb_(0.8)Zr_(0.2)-430 SS(6.0 mΩcm^(2))is much smaller than that of bare 430 SS(151.3 mΩcm^(2))at the clamping force of 140 N cm^(-2).Besides,diff erent from the highly increased interfacial contact resistance of bare 430 SS,the Nb_(0.8)Zr_(0.2)-430 SS shows a minor increase resistance after potentiostatic tests in simulated anodic environment of DFAFCs.