Compression tests were performed at room temperature to investigate the effects of hydrogenation temperature on compressive properties of Ti6 Al4 V alloy treated by continuous multistep hydrogenation treatment(CMHT).P...Compression tests were performed at room temperature to investigate the effects of hydrogenation temperature on compressive properties of Ti6 Al4 V alloy treated by continuous multistep hydrogenation treatment(CMHT).Pressure-composition isotherms and micro structures were also studied.Results showed that the equilibrium hydrogen pressure increased,and the hydrogen absorption rate decreased with the increase of hydrogenation temperature.The amounts ofβphase andα"martensite increased first and then decreased when Ti6 Al4 V alloy was treated by four times CMHT with the increase of hydrogenation temperature.Hydrogenation temperature played a different role on the compressive properties of CMHT-treated Ti6 Al4 V alloy.The ultimate compression of Ti6 Al4 V alloy treated by 11 times CMHT at850℃increased by 83.3%as compared to the as-received Ti6 Al4 V alloy.The compressive properties of Ti6 Al4 V alloy were dependent on the amounts of different phases and microstructures when Ti6 Al4 V alloy was treated by CMHT at different temperatures.展开更多
基金financially supported by the National Natural Science Foundation of China(No.51875157)the University Natural Science Research Project of Anhui Province(No.KJ2019A0894)the Fundamental Research Funds for the Central Universities(No.JD2019JGPY0016)。
文摘Compression tests were performed at room temperature to investigate the effects of hydrogenation temperature on compressive properties of Ti6 Al4 V alloy treated by continuous multistep hydrogenation treatment(CMHT).Pressure-composition isotherms and micro structures were also studied.Results showed that the equilibrium hydrogen pressure increased,and the hydrogen absorption rate decreased with the increase of hydrogenation temperature.The amounts ofβphase andα"martensite increased first and then decreased when Ti6 Al4 V alloy was treated by four times CMHT with the increase of hydrogenation temperature.Hydrogenation temperature played a different role on the compressive properties of CMHT-treated Ti6 Al4 V alloy.The ultimate compression of Ti6 Al4 V alloy treated by 11 times CMHT at850℃increased by 83.3%as compared to the as-received Ti6 Al4 V alloy.The compressive properties of Ti6 Al4 V alloy were dependent on the amounts of different phases and microstructures when Ti6 Al4 V alloy was treated by CMHT at different temperatures.