The effect of aging temperature on stress corrosion crocking of 17-4 precipitation-hardened(PH)stainless steel in simulated stimulant oil well environment was studied by the method B-NACE standard bent-beam test.It is...The effect of aging temperature on stress corrosion crocking of 17-4 precipitation-hardened(PH)stainless steel in simulated stimulant oil well environment was studied by the method B-NACE standard bent-beam test.It is found that when aging temperature ranges from 480 to 610℃,the sensitivity of hydrogen embrittlement decreases significantly.展开更多
文摘The effect of aging temperature on stress corrosion crocking of 17-4 precipitation-hardened(PH)stainless steel in simulated stimulant oil well environment was studied by the method B-NACE standard bent-beam test.It is found that when aging temperature ranges from 480 to 610℃,the sensitivity of hydrogen embrittlement decreases significantly.