Photoconductive semiconductor switch(PCSS)can be applied in pulsed high power systems and microwave techniques.However,reducing the damage and increasing the lifetime of silicon carbide(SiC)PCSS are still faced severe...Photoconductive semiconductor switch(PCSS)can be applied in pulsed high power systems and microwave techniques.However,reducing the damage and increasing the lifetime of silicon carbide(SiC)PCSS are still faced severe challenges.In this study,PCSSs with various structures were prepared on 4-inch diameter,500μm thick high-purity semi-insulating 4H-SiC substrates and their on-state resistance and damage mechanisms were investigated.It was found that the PCSS of an Au/TiW/Ni electrode system annealed at 950℃had a minimum on-state resistance of 6.0Ωat 1 kV bias voltage with a 532 nm and 170 mJ pulsed laser by backside illumination single trigger.The backside illumination single trigger could reduce on-state resistance and alleviate the damage of PCSS compared to the frontside trigger when the diameter of the laser spot was larger than the channel length of PCSS.For the 200 s trigger test by a 10 Hz laser,the black branch-like ablation on Au/TiW/Ni PCSS was mainly caused by thermal stress owing to hot carriers.Replacing metal Ni with boron gallium co-doped zinc oxide(BGZO)thin films annealed at 400℃,black branch-like ablation was alleviated while concentric arc damage was obvious at the anode.The major causes of concentric arc are both pulsed laser diffraction and thermal effect.展开更多
Four manganese oxide (MnO_(x)) catalysts with different phases were prepared via a hydrothermal method, and the toluene oxidation over the four manganese dioxide (MnO_(x)) catalysts was studied. Among the catalysts, ...Four manganese oxide (MnO_(x)) catalysts with different phases were prepared via a hydrothermal method, and the toluene oxidation over the four manganese dioxide (MnO_(x)) catalysts was studied. Among the catalysts, δ-MnO_(2) exhibits the best performance, excellent stability, and reusability. Moreover, δ-MnO_(2) possesses the highest specific surface area, with more exposed active sites compared to the other catalysts with which to make contact with toluene, leading to it exhibiting excellent activity. Furthermore, δ-MnO_(2) shows more lattice defects, Mn^(3+)/(Mn^(3+) + Mn^(4+)), oxygen vacancies, and surface adsorbed oxygen than the other catalysts, resulting in its excellent redox properties and catalytic performance. In addition, oxygen molecules adsorb on the oxygen vacancies of δ-MnO_(2), which are beneficial to the adsorption and oxidation of toluene, with benzyl alcohol, benzaldehyde, benzoic acid, and benzoic acid ester detected as specific intermediate products.展开更多
基金National Key R&D Program of China(2021YFA0716304)Shanghai Science and Technology Programs(22511100300,23DZ2201500)。
文摘Photoconductive semiconductor switch(PCSS)can be applied in pulsed high power systems and microwave techniques.However,reducing the damage and increasing the lifetime of silicon carbide(SiC)PCSS are still faced severe challenges.In this study,PCSSs with various structures were prepared on 4-inch diameter,500μm thick high-purity semi-insulating 4H-SiC substrates and their on-state resistance and damage mechanisms were investigated.It was found that the PCSS of an Au/TiW/Ni electrode system annealed at 950℃had a minimum on-state resistance of 6.0Ωat 1 kV bias voltage with a 532 nm and 170 mJ pulsed laser by backside illumination single trigger.The backside illumination single trigger could reduce on-state resistance and alleviate the damage of PCSS compared to the frontside trigger when the diameter of the laser spot was larger than the channel length of PCSS.For the 200 s trigger test by a 10 Hz laser,the black branch-like ablation on Au/TiW/Ni PCSS was mainly caused by thermal stress owing to hot carriers.Replacing metal Ni with boron gallium co-doped zinc oxide(BGZO)thin films annealed at 400℃,black branch-like ablation was alleviated while concentric arc damage was obvious at the anode.The major causes of concentric arc are both pulsed laser diffraction and thermal effect.
基金supported by the National Natural Science Foundation of China (No. 21872096)the Natural Science Youth Fund of Henan Province (No. 202300410034)+3 种基金the Young Teacher Foundation of Henan University of Urban Construction (No. YCJQNGGJS201903)the Key Scientific and Technological Project of Henan Province (No. 182102311016)the Henan Key Scientific Research Projects (No. 20A610003)the Doctoral Research Start-up Project of Henan University of Urban Construction (No. 990/Q2017011)
文摘Four manganese oxide (MnO_(x)) catalysts with different phases were prepared via a hydrothermal method, and the toluene oxidation over the four manganese dioxide (MnO_(x)) catalysts was studied. Among the catalysts, δ-MnO_(2) exhibits the best performance, excellent stability, and reusability. Moreover, δ-MnO_(2) possesses the highest specific surface area, with more exposed active sites compared to the other catalysts with which to make contact with toluene, leading to it exhibiting excellent activity. Furthermore, δ-MnO_(2) shows more lattice defects, Mn^(3+)/(Mn^(3+) + Mn^(4+)), oxygen vacancies, and surface adsorbed oxygen than the other catalysts, resulting in its excellent redox properties and catalytic performance. In addition, oxygen molecules adsorb on the oxygen vacancies of δ-MnO_(2), which are beneficial to the adsorption and oxidation of toluene, with benzyl alcohol, benzaldehyde, benzoic acid, and benzoic acid ester detected as specific intermediate products.