In order to study the effect of fused spinel on the properties of phosphoricacid bonded high alumina castables, samples with different contents of fused spinel were prepared.The results show that when the contents of ...In order to study the effect of fused spinel on the properties of phosphoricacid bonded high alumina castables, samples with different contents of fused spinel were prepared.The results show that when the contents of the fused spinel are between 8% and 16% (mass fraction),the castables have good properties. The castables overcome the shortages of the phosphoric acidbonded high alumina castables with bauxite cement as a hardening promoter. The experimentsdemonstrate that most of the service properties of the castables with fused spinel are better thanthose of the normal phosphoric acid bonded castables which use bauxite cement as a hardeningpromoter. The examination of the materials indicates that free MgO inclusions in the spinel powdercan promote the hardening of the castables.展开更多
A low cost thermal insulating material can be produced by compounding anactive xonotlite slurry, fired-perlite, HOMO PAN fibers and glass fibers. The maximum servicetemperature of the product is 800 deg C; linear shri...A low cost thermal insulating material can be produced by compounding anactive xonotlite slurry, fired-perlite, HOMO PAN fibers and glass fibers. The maximum servicetemperature of the product is 800 deg C; linear shrinkage after 800 deg C X 16 h firing is 0.9percent; the cold crushing strength is 1.56 MPa; the flexural strength at ambient temperature is0.81 MPa; the thermal conductivity at ambient temperature (25 deg C) is 0.056 and 0.128 W/(m centredot K) at 800 deg C. The production cost of such a composite is only 1/3 of that of the normalxonotlite thermal insulators. It can substitute the normal xonotlite thermal insulators on mostoccasions with a similar cost to that of normal perlite products.展开更多
文摘In order to study the effect of fused spinel on the properties of phosphoricacid bonded high alumina castables, samples with different contents of fused spinel were prepared.The results show that when the contents of the fused spinel are between 8% and 16% (mass fraction),the castables have good properties. The castables overcome the shortages of the phosphoric acidbonded high alumina castables with bauxite cement as a hardening promoter. The experimentsdemonstrate that most of the service properties of the castables with fused spinel are better thanthose of the normal phosphoric acid bonded castables which use bauxite cement as a hardeningpromoter. The examination of the materials indicates that free MgO inclusions in the spinel powdercan promote the hardening of the castables.
基金This work was supported by "Supporting Scheme for Backbone Young Staffs in High Education".]
文摘A low cost thermal insulating material can be produced by compounding anactive xonotlite slurry, fired-perlite, HOMO PAN fibers and glass fibers. The maximum servicetemperature of the product is 800 deg C; linear shrinkage after 800 deg C X 16 h firing is 0.9percent; the cold crushing strength is 1.56 MPa; the flexural strength at ambient temperature is0.81 MPa; the thermal conductivity at ambient temperature (25 deg C) is 0.056 and 0.128 W/(m centredot K) at 800 deg C. The production cost of such a composite is only 1/3 of that of the normalxonotlite thermal insulators. It can substitute the normal xonotlite thermal insulators on mostoccasions with a similar cost to that of normal perlite products.