In this study, a series of tests were conducted by using aluminum-based alloy to determine the formation of grain refining structure based on the ultrasonic vibration (UV). Furthermore, the simulation test and effect ...In this study, a series of tests were conducted by using aluminum-based alloy to determine the formation of grain refining structure based on the ultrasonic vibration (UV). Furthermore, the simulation test and effect of ultrasonic output power were studied using ammonium chloride. Finally, the mechanism of grain refinement was investigated. The results show that: (1) By applying the UV to aluminum-base alloy, the grain refining rate of ingots tended to increase with the increase of the output value of UV. (2) It was confirmed that time from after the pour to the beginning of crystallization as well as cloudiness tended to decrease with increasing the ultrasonic power value of UV. Moreover, it can be seen from each cooling curve that a uniform temperature gradient existed in the melt as the power of UV increased, that made the melt strongly stirred. (3) It was also considered that the grain refining effect of ingots, which was observed from the simulation tests, resulted from nucleation action and stirring division action by applying the UV.展开更多
文摘In this study, a series of tests were conducted by using aluminum-based alloy to determine the formation of grain refining structure based on the ultrasonic vibration (UV). Furthermore, the simulation test and effect of ultrasonic output power were studied using ammonium chloride. Finally, the mechanism of grain refinement was investigated. The results show that: (1) By applying the UV to aluminum-base alloy, the grain refining rate of ingots tended to increase with the increase of the output value of UV. (2) It was confirmed that time from after the pour to the beginning of crystallization as well as cloudiness tended to decrease with increasing the ultrasonic power value of UV. Moreover, it can be seen from each cooling curve that a uniform temperature gradient existed in the melt as the power of UV increased, that made the melt strongly stirred. (3) It was also considered that the grain refining effect of ingots, which was observed from the simulation tests, resulted from nucleation action and stirring division action by applying the UV.