A new co-precipitation route was proposed to synthesize LiNi0.8A10.2-xTixO2 （x=0.0-0.20） cathode materials for lithium ion batteries, with Ni（NO3）2, Al（NO3）3, LiOH·H2O, and TiO2 as the starting materials. U...A new co-precipitation route was proposed to synthesize LiNi0.8A10.2-xTixO2 （x=0.0-0.20） cathode materials for lithium ion batteries, with Ni（NO3）2, Al（NO3）3, LiOH·H2O, and TiO2 as the starting materials. Ultrasonic vibration was used during preparing the precursors, and the precursors were protected by absolute ethanol before calcination in the air. The influences of doped-Ti content, calcination temperature and time, additional Li content, and ultrasonic vibration on the structure and properties of LiNi0.8A10.2-xTixO2 were investigated by X-ray diffraction （XRD）, scanning electron microscopy （SEM）, and charge-discharge tests, respectively. The results show that the optimal molar fraction of Ti, calcination temperature and time, and additional molar fraction of Li for LiNi0.8A10.2-xTixO2 cathode materials are 0.1,700℃, 20 h, and 0.05, respectively. Ti doping facilitates the formation of the α-NaFeO2 layered structure, and ultrasonic vibration improves the electrochemical performance of LiNi0.8A10.2-xTixO2.展开更多
Properties, section structure and service results of recycled MgO-C bricks and new MgO-C bricks for ladle slag line of Baosteel were analyzed and compared, and the measures of improving stability and quality of recycl...Properties, section structure and service results of recycled MgO-C bricks and new MgO-C bricks for ladle slag line of Baosteel were analyzed and compared, and the measures of improving stability and quality of recycled MgO-C bricks were summarized. The results show that： （1） High quality recycled MgO-C materials can be produced by scientific, meticulous and strict management for every process such as dismantling furnace, selection, removing impurity and slag, stacking and homogenization ; （2） Using high quality recycled materials and reasonable production technique, recycled MgO-C bricks with better properties and service efficiency than those of new MgO-C brick can be produced; （3） Service efficiency of recycled MgO - C bricks is good because of its high density, good oxidation resistance and reasonable structure.展开更多
文摘A new co-precipitation route was proposed to synthesize LiNi0.8A10.2-xTixO2 （x=0.0-0.20） cathode materials for lithium ion batteries, with Ni（NO3）2, Al（NO3）3, LiOH·H2O, and TiO2 as the starting materials. Ultrasonic vibration was used during preparing the precursors, and the precursors were protected by absolute ethanol before calcination in the air. The influences of doped-Ti content, calcination temperature and time, additional Li content, and ultrasonic vibration on the structure and properties of LiNi0.8A10.2-xTixO2 were investigated by X-ray diffraction （XRD）, scanning electron microscopy （SEM）, and charge-discharge tests, respectively. The results show that the optimal molar fraction of Ti, calcination temperature and time, and additional molar fraction of Li for LiNi0.8A10.2-xTixO2 cathode materials are 0.1,700℃, 20 h, and 0.05, respectively. Ti doping facilitates the formation of the α-NaFeO2 layered structure, and ultrasonic vibration improves the electrochemical performance of LiNi0.8A10.2-xTixO2.
文摘Properties, section structure and service results of recycled MgO-C bricks and new MgO-C bricks for ladle slag line of Baosteel were analyzed and compared, and the measures of improving stability and quality of recycled MgO-C bricks were summarized. The results show that： （1） High quality recycled MgO-C materials can be produced by scientific, meticulous and strict management for every process such as dismantling furnace, selection, removing impurity and slag, stacking and homogenization ; （2） Using high quality recycled materials and reasonable production technique, recycled MgO-C bricks with better properties and service efficiency than those of new MgO-C brick can be produced; （3） Service efficiency of recycled MgO - C bricks is good because of its high density, good oxidation resistance and reasonable structure.
