Mesoporous silica materials with high pore volume were successfully prepared by the chemical precipitation method, with water glass and a biodegradable nonionic surfactant polyethylene glycol （PEG）. The obtained mat...Mesoporous silica materials with high pore volume were successfully prepared by the chemical precipitation method, with water glass and a biodegradable nonionic surfactant polyethylene glycol （PEG）. The obtained materials were characterized by transmission electron microscopy （TEM）, scanning electron microscopy （SEM）, thermo gravimetric analyzer and differential scanning calorimetry （TG-DSC）, nitrogen adsorption-desorption measurements, and X-ray diffraction （XRD）. The results showed that the changes of the pore parameters depended on both the surfactant content and heat treatment temperature. When the content of PEG was 10wt% and the obtained PEG/SiO2 composite was heated at 600℃, the mesoporous silica with a pore volume of 2.2 cma/g, a BET specific surface area of 361.55 m^2/g, and a diameter of 2-4 μm could be obtained. The obtained mesoporous silica materials have potential applications in the fields of paint and plastic, as thickening, reinforcing, and flatting agents.展开更多
基金the National Natural Science Foundation of China (No.20671010, 20236020, 20325621, 50642042).
文摘Mesoporous silica materials with high pore volume were successfully prepared by the chemical precipitation method, with water glass and a biodegradable nonionic surfactant polyethylene glycol （PEG）. The obtained materials were characterized by transmission electron microscopy （TEM）, scanning electron microscopy （SEM）, thermo gravimetric analyzer and differential scanning calorimetry （TG-DSC）, nitrogen adsorption-desorption measurements, and X-ray diffraction （XRD）. The results showed that the changes of the pore parameters depended on both the surfactant content and heat treatment temperature. When the content of PEG was 10wt% and the obtained PEG/SiO2 composite was heated at 600℃, the mesoporous silica with a pore volume of 2.2 cma/g, a BET specific surface area of 361.55 m^2/g, and a diameter of 2-4 μm could be obtained. The obtained mesoporous silica materials have potential applications in the fields of paint and plastic, as thickening, reinforcing, and flatting agents.