A sulfonated poly(ether ether ketone)(SPEEK) membrane with a fairly high degree of sulfonation(DS) can swell excessively and even dissolve at high temperature.To solve these problems,insolvable functionalized silica p...A sulfonated poly(ether ether ketone)(SPEEK) membrane with a fairly high degree of sulfonation(DS) can swell excessively and even dissolve at high temperature.To solve these problems,insolvable functionalized silica powder with sulfonic acid groups(SiOx-S) was added into the SPEEK matrix(DS = 55.1%) to prepare SPEEK/SiOx-S composite membranes.The decrease in both the swelling degree and the methanol permeability of the membranes was a dose-dependent result of addition of the SiOx-S powder.Pure SPEEK membrane swelled 52.6% at 80°C,whereas the SPEEK/SiOx-S(15%,by mass) membrane swelled only 27.3% at the same temperature.From room temperature to 80℃,all SPEEK/SPEEK/SiOx-S composite membranes had methanol permeability of about o ne order of magnitude lower than that of Nafion?115.Compared with pure SPEEK membranes,the addition of the SiOx-S powder not only leads to higher proton conductivity,but also increases the dimensional stability at higher temperatures,and greater proton conductivity can be achieved at higher temperature.The SPEEK/SiOx-S(20%,by mass) membrane could withstand temperature up to 145°C,at which in 100% relative humidity(RH) its proton conductivity exceeded slightly that of Nafion?115 membrane and reached 0.17 S·cm-1,while pure SPEEK membrane dissolved at 90°C.The SPEEK/SiOx-S composite membranes are promising for use in direct methanol fuel cells because of their good dimensional stability,high proton conductivity,and low methanol permeability.展开更多
基金Supported by the State Key Development Program for Basic Research of China （2008CB617502）, the National Natural Science Foundation of China （20606025）, and Program for Changjiang Scholars and Innovative Research Team in University of China （IRT0641）.
文摘A sulfonated poly(ether ether ketone)(SPEEK) membrane with a fairly high degree of sulfonation(DS) can swell excessively and even dissolve at high temperature.To solve these problems,insolvable functionalized silica powder with sulfonic acid groups(SiOx-S) was added into the SPEEK matrix(DS = 55.1%) to prepare SPEEK/SiOx-S composite membranes.The decrease in both the swelling degree and the methanol permeability of the membranes was a dose-dependent result of addition of the SiOx-S powder.Pure SPEEK membrane swelled 52.6% at 80°C,whereas the SPEEK/SiOx-S(15%,by mass) membrane swelled only 27.3% at the same temperature.From room temperature to 80℃,all SPEEK/SPEEK/SiOx-S composite membranes had methanol permeability of about o ne order of magnitude lower than that of Nafion?115.Compared with pure SPEEK membranes,the addition of the SiOx-S powder not only leads to higher proton conductivity,but also increases the dimensional stability at higher temperatures,and greater proton conductivity can be achieved at higher temperature.The SPEEK/SiOx-S(20%,by mass) membrane could withstand temperature up to 145°C,at which in 100% relative humidity(RH) its proton conductivity exceeded slightly that of Nafion?115 membrane and reached 0.17 S·cm-1,while pure SPEEK membrane dissolved at 90°C.The SPEEK/SiOx-S composite membranes are promising for use in direct methanol fuel cells because of their good dimensional stability,high proton conductivity,and low methanol permeability.
