Corn rod-like WO<sub>3</sub> nanomaterials were successfully synthesized by a simple hydrothermal method. The morphology, structure and optical absorption properties of the prepared samples were characteri...Corn rod-like WO<sub>3</sub> nanomaterials were successfully synthesized by a simple hydrothermal method. The morphology, structure and optical absorption properties of the prepared samples were characterized by SEM, XRD, FTIR and UV-Vis-DRS. The WO<sub>3</sub> materials were corn rod-like morphology with about 800 nm for length and 150 nm for diameter, especially there were plenty of corn particles (about 20 nm) on the surface of corn rods. The X-ray diffraction peaks of the products corresponded with WO<sub>3</sub> standard card, and the characteristic peak of W-O bond was found in the infrared spectrum. The absorption band edge of the products was about 480 nm, indicating their potential visible-light-induced photocatalytic activity. In situ FTIR technology research showed that the prepared WO<sub>3</sub> nanomaterials had visible photocatalytic activity to gas-phase toluene. After a photocatalytic reaction for 8 hours toluene was effectively degraded, and carboxylic acid and aldehyde could be regarded as the intermediate products, and CO<sub>2</sub> was produced as the final product during the reaction process.展开更多
教师专业自主是教师专业发展的重要内容。本文通过筛选Web of Science核心合集数据库中1985-2020年与教师专业自主相关的1286篇文献为研究对象,运用具有可视化功能Citespace V5.7.R4引文分析软件,以发文时序、发文期刊、主要发文国家与...教师专业自主是教师专业发展的重要内容。本文通过筛选Web of Science核心合集数据库中1985-2020年与教师专业自主相关的1286篇文献为研究对象,运用具有可视化功能Citespace V5.7.R4引文分析软件,以发文时序、发文期刊、主要发文国家与地区、高被引文献、高频突显关键词等视角,对精炼后的文献进行数据统计和可视化分析,厘清了教师专业自主的历史发展进程,突出了教师专业自主的研究重点,深入分析了教师专业自主的内涵演变历程,即从强调“独立自主”走向强调“合作自主”;从关注“教学自主”走向关注“多维自主”;从“自主作为权利”走向“自主作为责任”;从抵御“被动自主”走向呼吁“能动自主”。展开更多
Along with the popularity of environmental protection concepts, the environmental treatment of water pollution attracts widespread attention, among which, the research on Bi-based semiconductor photocatalytic degradat...Along with the popularity of environmental protection concepts, the environmental treatment of water pollution attracts widespread attention, among which, the research on Bi-based semiconductor photocatalytic degradation technology has made great progress. However, the development of such bismuth-based composites still remains a challenging task due to difficult recovery and low catalytic efficiency. Herein, a novel CC/BiPO4</sub>/Bi2</sub>WO6</sub> composite was successfully synthesized through two-step hydrothermal method using activated flexible carbon cloth as a substrate. The results of the photocatalytic degradation experiments showed that the obtained CC/BiPO<sub>4</sub>/Bi<sub>2</sub>WO<sub>6</sub> composites can degrade 92.1% RhB in 60 min under UV-visible light irradiation, which was much higher than that of unloaded BiPO4</sub> (24.4%) and BiPO4</sub>/Bi2</sub>WO6</sub> (52.9%), exhibiting a better adsorption-photocatalytic degradation performance than BiPO4</sub> and BiPO4</sub>/Bi2</sub>WO6</sub>. Photoluminescence spectra indicated that the improved photocatalytic activity was due to the more effective inhibition of photogenerated carrier complexation. Furthermore, the radical capture experiments confirmed that h<sup>+</sup>, ·OH and O<sub>2</sub>-</sup> were the main active substances in the photocatalytic degradation process of RhB by the CC/BiPO4</sub>/Bi2</sub>WO6</sub> composites. More importantly, the prepared CC/BiPO4</sub>/Bi2</sub>WO6</sub> composite had a simple separation process and good recycling stability, and its photocatalytic degradation efficiency can still reach 53.3% after six cycles of RhB degradation. .展开更多
文摘Corn rod-like WO<sub>3</sub> nanomaterials were successfully synthesized by a simple hydrothermal method. The morphology, structure and optical absorption properties of the prepared samples were characterized by SEM, XRD, FTIR and UV-Vis-DRS. The WO<sub>3</sub> materials were corn rod-like morphology with about 800 nm for length and 150 nm for diameter, especially there were plenty of corn particles (about 20 nm) on the surface of corn rods. The X-ray diffraction peaks of the products corresponded with WO<sub>3</sub> standard card, and the characteristic peak of W-O bond was found in the infrared spectrum. The absorption band edge of the products was about 480 nm, indicating their potential visible-light-induced photocatalytic activity. In situ FTIR technology research showed that the prepared WO<sub>3</sub> nanomaterials had visible photocatalytic activity to gas-phase toluene. After a photocatalytic reaction for 8 hours toluene was effectively degraded, and carboxylic acid and aldehyde could be regarded as the intermediate products, and CO<sub>2</sub> was produced as the final product during the reaction process.
文摘教师专业自主是教师专业发展的重要内容。本文通过筛选Web of Science核心合集数据库中1985-2020年与教师专业自主相关的1286篇文献为研究对象,运用具有可视化功能Citespace V5.7.R4引文分析软件,以发文时序、发文期刊、主要发文国家与地区、高被引文献、高频突显关键词等视角,对精炼后的文献进行数据统计和可视化分析,厘清了教师专业自主的历史发展进程,突出了教师专业自主的研究重点,深入分析了教师专业自主的内涵演变历程,即从强调“独立自主”走向强调“合作自主”;从关注“教学自主”走向关注“多维自主”;从“自主作为权利”走向“自主作为责任”;从抵御“被动自主”走向呼吁“能动自主”。
基金Postdoctoral Science Foundation of China(2012M520605)Research Foundation of Taiyuan University of Technology(tyut-rc201369a,2013Z040)+1 种基金Open Foundation of State Key Laboratory of Coal Conversion(09-102)Natural Science Foundation of Shanxi Province(2013011042-1)
文摘Along with the popularity of environmental protection concepts, the environmental treatment of water pollution attracts widespread attention, among which, the research on Bi-based semiconductor photocatalytic degradation technology has made great progress. However, the development of such bismuth-based composites still remains a challenging task due to difficult recovery and low catalytic efficiency. Herein, a novel CC/BiPO4</sub>/Bi2</sub>WO6</sub> composite was successfully synthesized through two-step hydrothermal method using activated flexible carbon cloth as a substrate. The results of the photocatalytic degradation experiments showed that the obtained CC/BiPO<sub>4</sub>/Bi<sub>2</sub>WO<sub>6</sub> composites can degrade 92.1% RhB in 60 min under UV-visible light irradiation, which was much higher than that of unloaded BiPO4</sub> (24.4%) and BiPO4</sub>/Bi2</sub>WO6</sub> (52.9%), exhibiting a better adsorption-photocatalytic degradation performance than BiPO4</sub> and BiPO4</sub>/Bi2</sub>WO6</sub>. Photoluminescence spectra indicated that the improved photocatalytic activity was due to the more effective inhibition of photogenerated carrier complexation. Furthermore, the radical capture experiments confirmed that h<sup>+</sup>, ·OH and O<sub>2</sub>-</sup> were the main active substances in the photocatalytic degradation process of RhB by the CC/BiPO4</sub>/Bi2</sub>WO6</sub> composites. More importantly, the prepared CC/BiPO4</sub>/Bi2</sub>WO6</sub> composite had a simple separation process and good recycling stability, and its photocatalytic degradation efficiency can still reach 53.3% after six cycles of RhB degradation. .