Texture regulation is a prominent method to modify the mechanical properties and anisotropy of magnesium alloy.In this work,the Mg-1Al-0.3Ca-0.5Mn-0.2Gd(wt.%)alloy sheet with TD-tilted and circular texture was fabrica...Texture regulation is a prominent method to modify the mechanical properties and anisotropy of magnesium alloy.In this work,the Mg-1Al-0.3Ca-0.5Mn-0.2Gd(wt.%)alloy sheet with TD-tilted and circular texture was fabricated by unidirectional rolling(UR)and multidirectional rolling(MR)method,respectively.Unlike generating a strong in-plane mechanical anisotropy in conventional TD-tilted texture,the novel circular texture sample possessed a weak in-plane yield anisotropy.This can be rationalized by the similar proportion of soft grains with favorable orientation for basalslip and{10.12}tensile twinning during the uniaxial tension of circular-texture sample along different directions.Moreover,compared with the TD-tilted texture,the circular texture improved the elongation to failure both along the rolling direction(RD)and transverse direction(TD).By quasi-in-situ EBSD-assisted slip trace analysis,higher activation of basal slip was observed in the circular-texture sample during RD tension,contributing to its excellent ductility.When loading along the TD,the TD-tilted texture promoted the activation of{10.12}tensile twins significantly,thus providing nucleation sites for cracks and deteriorating the ductility.This research may shed new insights into the development of formable and ductile Mg alloy sheets by texture modification.展开更多
In order to obtain the sharp cube texture,a new process,the intermediate annealing rolling technique,has been introduced to prepare the Ni7W substrate.In this paper,a cubic texture content up to 98.5%within 10°of...In order to obtain the sharp cube texture,a new process,the intermediate annealing rolling technique,has been introduced to prepare the Ni7W substrate.In this paper,a cubic texture content up to 98.5%within 10°of the standard cubic orientation is obtained in the final substrate and the influence of this improved rolling technique on the cube texture formation has been discussed.The results show that the increased cube texture in the Ni7W substrate is caused by the optimized deformation texture and the increased nucleated fraction of the cube grains.展开更多
Recently,various slippery liquid-infused porous surfaces(SLIPS)have been fabricated for the protection of various materials.However,these SLIPSs are limited by their underlying storage structure and superficial lubric...Recently,various slippery liquid-infused porous surfaces(SLIPS)have been fabricated for the protection of various materials.However,these SLIPSs are limited by their underlying storage structure and superficial lubricant layer,showing poor durability.Herein,inspired by the high-strength structure of Shell nacre’s“brick-mud”layer,we fabricated an all-inorganic composite coating by using wet chemically etched MXene as a brick and an aluminum phosphate binder(AP)as mud.Then,a series of microwell-array structures were designed and prepared on the coating via nanosecond ultrafast laser writing ablation technology.Subsequently,the textured surface was modified by a silane coupling agent.Vinyl-terminated polydimethylsiloxane(PDMS)was tightly grafted onto the porous surface through a thiol-ene click reaction to obtain lubricant grafted texture surface(LGTS).The prepared LGTS showed good lubrication properties for multiple phases,including various liquids,ice crystals,and solids.It exhibits excellent chemical stability and mechanical durability under deionized water impact,centrifugal test,strong acid solutions,anti/de-icing cycles,and high-intensity friction.Thus,the proposed strategy for constructing robust LGTS will greatly promote theoretical research on super wetting interfacial materials and their applications in the fields of antifouling,anti/de-icing,and lubricating protection.展开更多
The mechanical properties of an extruded Mg-10Gd sample, specifically designed for vascular stents, are crucial for predicting its behavior under service conditions. Achieving homogeneous stresses in the hoop directio...The mechanical properties of an extruded Mg-10Gd sample, specifically designed for vascular stents, are crucial for predicting its behavior under service conditions. Achieving homogeneous stresses in the hoop direction, essential for characterizing vascular stents, poses challenges in experimental testing based on standard specimens featuring a reduced cross section. This study utilizes an elasto-visco-plastic self-consistent polycrystal model(ΔEVPSC) with the predominant twinning reorientation(PTR) scheme as a numerical tool, offering an alternative to mechanical testing. For verification, various mechanical experiments, such as uniaxial tension, compression, notched-bar tension, three-point bending, and C-ring compression tests, were conducted. The resulting force vs. displacement curves and textures were then compared with those based on the ΔEVPSC model. The computational model's significance is highlighted by simulation results demonstrating that the differential hardening along with a weak strength differential effect observed in the Mg-10Gd sample is a result of the interplay between micromechanical deformation mechanisms and deformation-induced texture evolution. Furthermore, the study highlights that incorporating the axisymmetric texture from the as-received material incorporating the measured texture gradient significantly improves predictive accuracy on the strength in the hoop direction. Ultimately, the findings suggest that the ΔEVPSC model can effectively predict the mechanical behavior resulting from loading scenarios that are impossible to realize experimentally, emphasizing its valuable contribution as a digital twin.展开更多
LZ91 Mg-Li alloy plates with three types of initial texture were rolled by 70%reduction at both room temperature and 200℃to explore the rolling texture formation ofα-Mg phase.The results showed that the rolling text...LZ91 Mg-Li alloy plates with three types of initial texture were rolled by 70%reduction at both room temperature and 200℃to explore the rolling texture formation ofα-Mg phase.The results showed that the rolling texture is largely affected by the initial texture.All the samples exhibited two main texture components as RD-split double peaks texture and TD-split double peaks texture after large strain rolling.The intensity of the two texture components was strongly influenced by the initial orientation and rolling temperature.Extension twinning altered the large-split non-basal orientation to a near basal one at low rolling strain.The basal orientation induced by twinning is unstable,which finally transmitted to the RD-split texture.The strong TD-split texture formed due to slip-induced orientation transition from its initial orientation.The competition between prismatic and basal slip determined the intensity and tilt angle of the TD-split texture.By increasing the rolling temperature,the TD-split texture component was enhanced in all three samples.Limitation of extension twinning behavior and the promotion of prismatic slip at elevated temperature are the main reasons for the difference in hot and cold rolling texture.展开更多
Dysphagia is commonly associated with malnutrition and an increased choking risk.To overcome these complications,food designed for people with dysphagia should have an appropriate texture and a high nutritional value....Dysphagia is commonly associated with malnutrition and an increased choking risk.To overcome these complications,food designed for people with dysphagia should have an appropriate texture and a high nutritional value.In this study,six formulations of a strawberry dessert enriched in protein(calcium caseinate)and fiber(wheat dextrin or inulin)were developed using different hydrocolloids(xanthan gum,carboxymethyl cellulose or modified starch)to provide desirable texture and stability.Nutritional value was calculated and total phenolic content and antioxidant activity of the samples were analyzed.Back-extrusion test,rheological measurements and sensory analysis were performed in refrigerated and frozen samples to characterize their textural and viscoelastic properties.The high content in protein(14.7 g/100 g)and fiber(7.9-8.7 g/100 g)made possible to use the claims“high protein”and“high fiber”.Phytochemicals supplied by strawberries contributed to the antioxidant properties of the dessert.Loss tangent ranged 0.28-0.35 for all the formulations,indicating a weak gel behavior,which could be considered safe to swallow.The formulations with dextrin in combination with carboxymethyl cellulose or xanthan gum seemed to be less susceptible to structural changes during frozen storage.This work provides insights for the development of a nutrient-dense dessert that meets the requirements of people with dysphagia.展开更多
Hot torsion tests for AZ80 magnesium alloy were carried out in the temperature range of 380℃-260℃,with a constant decreasing temperature rate of 10℃/s in order to weaken the basal texture and refine the grains.The ...Hot torsion tests for AZ80 magnesium alloy were carried out in the temperature range of 380℃-260℃,with a constant decreasing temperature rate of 10℃/s in order to weaken the basal texture and refine the grains.The results indicated that the average grain sizes were refined forming gradient structure with increasing specimen radial position from center(12.2-5.4μm),and that the initial basal texture intensity of the extruded magnesium alloy was weakened from 46.2 to 8.3.Furthermore,the extension twins(ETs)could be disintegrated from the twins forming separated twins with smaller sizes.Interestingly,ETs with the same twin variant intersecting with each other could be coalesced forming grains with similar orientation,while ETs with different twin variants were separated by twins boundaries contributing to grain refinement.Moreover,in addition to the conventional continuous dynamic recrystallized(CDRX)grains with 30˚orientation rotated around C-axis of the parent grains,CDRXed grains with 30˚rotation around a-axis and random rotation axis were also discerned.Besides,the CDRX evolution induced twins were also elaborated,exhibiting the complex competition between CDRX and twining.Hot torsion deformation with constant decreasing temperatures rate is an effective way of grain refinement and texture modification.展开更多
Magnesium alloys have many advantages as lightweight materials for engineering applications,especially in the fields of automotive and aerospace.They undergo extensive cutting or machining while making products out of...Magnesium alloys have many advantages as lightweight materials for engineering applications,especially in the fields of automotive and aerospace.They undergo extensive cutting or machining while making products out of them.Dry cutting,a sustainable machining method,causes more friction and adhesion at the tool-chip interface.One of the promising solutions to this problem is cutting tool surface texturing,which can reduce tool wear and friction in dry cutting and improve machining performance.This paper aims to investigate the impact of dimple textures(made on the flank face of cutting inserts)on tool wear and chip morphology in the dry machining of AZ31B magnesium alloy.The results show that the cutting speed was the most significant factor affecting tool flank wear,followed by feed rate and cutting depth.The tool wear mechanism was examined using scanning electron microscope(SEM)images and energy dispersive X-ray spectroscopy(EDS)analysis reports,which showed that at low cutting speed,the main wear mechanism was abrasion,while at high speed,it was adhesion.The chips are discontinuous at low cutting speeds,while continuous at high cutting speeds.The dimple textured flank face cutting tools facilitate the dry machining of AZ31B magnesium alloy and contribute to ecological benefits.展开更多
Twisted bilayer graphene(TBG) has been extensively studied because of its novel physical properties and potential application in electronic devices.Here we report the synthesis and characterization of 300 TBG naturall...Twisted bilayer graphene(TBG) has been extensively studied because of its novel physical properties and potential application in electronic devices.Here we report the synthesis and characterization of 300 TBG naturally grown on Cu_(0.75)Ni_(0.25)(111) film and investigate the electronic structure by angle-resolved photoemission spectroscopy.Compared with other substrates,our TBG with a wafer scale is acquired with a shorter growth time.The Fermi velocity and energy gap of Dirac cones of TBG are comparable with those of a monolayer on Cu_(0.85)Ni_(0.15)(111).The signature of moré lattices has not been observed in either the low-energy electron diffraction patterns or the Fermi surface map within experimental resolution,possibly due to different Cu and Ni contents in the substrates enhancing the different couplings between the substrate and the first/second layers and hindering the formation of a quasiperiodic structure.展开更多
Algal blooms,the spread of algae on the surface of water bodies,have adverse effects not only on aquatic ecosystems but also on human life.The adverse effects of harmful algal blooms(HABs)necessitate a convenient solu...Algal blooms,the spread of algae on the surface of water bodies,have adverse effects not only on aquatic ecosystems but also on human life.The adverse effects of harmful algal blooms(HABs)necessitate a convenient solution for detection and monitoring.Unmanned aerial vehicles(UAVs)have recently emerged as a tool for algal bloom detection,efficiently providing on-demand images at high spatiotemporal resolutions.This study developed an image processing method for algal bloom area estimation from the aerial images(obtained from the internet)captured using UAVs.As a remote sensing method of HAB detection,analysis,and monitoring,a combination of histogram and texture analyses was used to efficiently estimate the area of HABs.Statistical features like entropy(using the Kullback-Leibler method)were emphasized with the aid of a gray-level co-occurrence matrix.The results showed that the orthogonal images demonstrated fewer errors,and the morphological filter best detected algal blooms in real time,with a precision of 80%.This study provided efficient image processing approaches using on-board UAVs for HAB monitoring.展开更多
3%Y_(2)O_(3)p/ZGK200 composites were subjected to unidirectional rolling(UR)and cross rolling(CR)at 400℃and 350℃followed by annealing at 300℃for 1 h.The microstructure,texture and mechanical properties of rolled an...3%Y_(2)O_(3)p/ZGK200 composites were subjected to unidirectional rolling(UR)and cross rolling(CR)at 400℃and 350℃followed by annealing at 300℃for 1 h.The microstructure,texture and mechanical properties of rolled and annealed composites were systematically studied.The rolled composites exhibited a heterogeneous microstructure,consisting of deformed grains elongated along rolling direction(RD)and Y_(2)O_(3)particles bands distributed along RD.After annealing,static recrystallization(SRX)occurred and most deformed grains transformed into equiaxed grains.A non-basal texture with two strong T-texture components was obtained after UR while a non-basal elliptical/circle texture with circle multi-peaks was obtained after CR,indicating that rolling path had great influences on texture of the composites.After annealing process,R-texture component disappeared or weakened,as results,a non-basal texture with double peaks tilting from normal direction(ND)to transverse direction(TD)and a more random non-basal texture with circle multi-peaks were obtained for UR and CR composites,respectively.The yield strength of rolled composites after UR showed obvious anisotropy along RD and TD while a low anisotropic yield strength was obtained after CR.Some Y_(2)O_(3)particles broke during rolling.The fracture of the composites was attributed to the existence of Y_(2)O_(3)clusters and interfacial debonding between particles and matrix during tension,as a result,the ductility was not as superior as matrix alloy.展开更多
The effect of forging on the microstructure and texture evolution of a high Nb containing Ti-45Al-7Nb-0.3W(at.%)alloy was investigated by X-ray diffractometer(XRD),scanning electron microscopy(SEM),and transmission el...The effect of forging on the microstructure and texture evolution of a high Nb containing Ti-45Al-7Nb-0.3W(at.%)alloy was investigated by X-ray diffractometer(XRD),scanning electron microscopy(SEM),and transmission electron microscopy(TEM).The results show that the as-cast alloy is mainly composed of α_(2)/γ lamellar colonies with a mean size of 70μm,but the hot-forged pancake displays a near duplex microstructure(DP).Kinking and bending of lamellar colonies,deformation twinning and dynamic recrystallization(DRX)occur during hot forging.Meanwhile,dense dislocations in theβphase after forging suggest that the high-temperature β phase with a disordered structure is favorable for improving the hot-workability of the alloy.Unlike the common TiAl casting texture,the solidification process of the investigated as-cast alloy with high Nb content is completely via the β phase region,resulting in the formation of a<110>γ fiber texture where the<110>γ aligns parallel to the heat-flow direction.In comparison,the relatively strong<001>and weak<302>texture components in the as-forged alloy are attributed to the deformation twinning.After annealing,static recrystallization occurs at the twin boundary and intersections,which weakens the deformation texture.展开更多
Purpose: This review examines the diagnostic value of transvaginal 3D ultrasound image texture analysis for the diagnosis of uterine adhesions. Materials and Methods: The total clinical data of 53 patients with uterin...Purpose: This review examines the diagnostic value of transvaginal 3D ultrasound image texture analysis for the diagnosis of uterine adhesions. Materials and Methods: The total clinical data of 53 patients with uterine adhesions diagnosed by hysteroscopy and the imaging data of transvaginal three-dimensional ultrasound from the Second Affiliated Hospital of Chongqing Medical University from June 2022 to August 2023 were retrospectively analysed. Based on hysteroscopic surgical records, patients were divided into two independent groups: normal endometrium and uterine adhesion sites. The samples were divided into a training set and a test set, and the transvaginal 3D ultrasound was used to outline the region of interest (ROI) and extract texture features for normal endometrium and uterine adhesions based on hysteroscopic surgical recordings, the training set data were feature screened and modelled using lasso regression and cross-validation, and the diagnostic efficacy of the model was assessed by applying the subjects’ operating characteristic (ROC) curves. Results: For each group, 290 texture feature parameters were extracted and three higher values were screened out, and the area under the curve of the constructed ultrasonographic scoring model was 0.658 and 0.720 in the training and test sets, respectively. Conclusion Relative clinical value of transvaginal three-dimensional ultrasound image texture analysis for the diagnosis of uterine adhesions.展开更多
BACKGROUND Despite continuous changes in treatment methods,the survival rate for advanced hepatocellular carcinoma(HCC)patients remains low,highlighting the importance of diagnostic methods for HCC.AIM To explore the ...BACKGROUND Despite continuous changes in treatment methods,the survival rate for advanced hepatocellular carcinoma(HCC)patients remains low,highlighting the importance of diagnostic methods for HCC.AIM To explore the efficacy of texture analysis based on multi-parametric magnetic resonance(MR)imaging(MRI)in predicting microvascular invasion(MVI)in preoperative HCC.METHODS This study included 105 patients with pathologically confirmed HCC,categorized into MVI-positive and MVI-negative groups.We employed Original Data Analysis,Principal Component Analysis,Linear Discriminant Analysis(LDA),and Non-LDA(NDA)for texture analysis using multi-parametric MR images to predict preoperative MVI.The effectiveness of texture analysis was determined using the B11 program of the MaZda4.6 software,with results expressed as the misjudgment rate(MCR).RESULTS Texture analysis using multi-parametric MRI,particularly the MI+PA+F dimensionality reduction method combined with NDA discrimination,demonstrated the most effective prediction of MVI in HCC.Prediction accuracy in the pulse and equilibrium phases was 83.81%.MCRs for the combination of T2-weighted imaging(T2WI),arterial phase,portal venous phase,and equilibrium phase were 22.86%,16.19%,20.95%,and 20.95%,respectively.The area under the curve for predicting MVI positivity was 0.844,with a sensitivity of 77.19%and specificity of 91.67%.CONCLUSION Texture analysis of arterial phase images demonstrated superior predictive efficacy for MVI in HCC compared to T2WI,portal venous,and equilibrium phases.This study provides an objective,non-invasive method for preoperative prediction of MVI,offering a theoretical foundation for the selection of clinical therapy.展开更多
Hot torsion tests were performed on the Al-7Mg alloy at the temperature ranging from 300 to 500℃ and strain rates between 0.05 and 5 s^(-1) to explore the progressive dynamic recrystallization(DRX)and texture behavio...Hot torsion tests were performed on the Al-7Mg alloy at the temperature ranging from 300 to 500℃ and strain rates between 0.05 and 5 s^(-1) to explore the progressive dynamic recrystallization(DRX)and texture behaviors.The DRX behavior of the alloy manifested two distinct stages:Stage 1 at strain of≤2 and Stage 2 at strains of≥2.In Stage 1,there was a slight increase in the DRXed grain fraction(X_(DRX))with predominance of discontinuous DRX(DDRX),followed by a modest change in X_(DRX) until the transition to Stage 2.Stage 2 was marked by an accelerated rate of DRX,culminating in a substantial final X_(DRX) of~0.9.Electron backscattered diffraction(EBSD)analysis on a sample in Stage 2 revealed that continuous DRX(CDRX)predominantly occurred within the(121)[001]grains,whereas the(111)[110]grains underwent a geometric DRX(GDRX)evolution without a noticeable sub-grain structure.Furthermore,a modified Avrami’s DRX kinetics model was utilized to predict the microstructural refinement in the Al-7Mg alloy during the DRX evolution.Although this kinetics model did not accurately capture the DDRX behavior in Stage 1,it effectively simulated the DRX rate in Stage 2.The texture index was employed to assess the evolution of the texture isotropy during hot-torsion test,demonstrating significant improvement(>75%)in texture randomness before the commencement of Stage 2.This initial texture evolution is attributed to the rotation of parent grains and the substructure evolution,rather than to an increase in X_(DRX).展开更多
基金supports from The National Natural Science Foundation of China(nos.52222409,52074132,and U19A2084)The National Key Research and Development Program(no.2022YFE0122000)are greatly acknowledgedsupport from The Science and Technology Development Program of Jilin Province(no.20210301025GX).
文摘Texture regulation is a prominent method to modify the mechanical properties and anisotropy of magnesium alloy.In this work,the Mg-1Al-0.3Ca-0.5Mn-0.2Gd(wt.%)alloy sheet with TD-tilted and circular texture was fabricated by unidirectional rolling(UR)and multidirectional rolling(MR)method,respectively.Unlike generating a strong in-plane mechanical anisotropy in conventional TD-tilted texture,the novel circular texture sample possessed a weak in-plane yield anisotropy.This can be rationalized by the similar proportion of soft grains with favorable orientation for basalslip and{10.12}tensile twinning during the uniaxial tension of circular-texture sample along different directions.Moreover,compared with the TD-tilted texture,the circular texture improved the elongation to failure both along the rolling direction(RD)and transverse direction(TD).By quasi-in-situ EBSD-assisted slip trace analysis,higher activation of basal slip was observed in the circular-texture sample during RD tension,contributing to its excellent ductility.When loading along the TD,the TD-tilted texture promoted the activation of{10.12}tensile twins significantly,thus providing nucleation sites for cracks and deteriorating the ductility.This research may shed new insights into the development of formable and ductile Mg alloy sheets by texture modification.
基金Funded by the Beijing Municipal Natural Science Foundation(No.2212025)National Natural Science Foundation of China(No.12042506)+1 种基金Magnetic Resonance Union of Chinese Academy of Sciences(No.2020GZL001)the General Program of Science and Technology Development Project of Beijing Municipal Education Commission(No.KM202010005007)。
文摘In order to obtain the sharp cube texture,a new process,the intermediate annealing rolling technique,has been introduced to prepare the Ni7W substrate.In this paper,a cubic texture content up to 98.5%within 10°of the standard cubic orientation is obtained in the final substrate and the influence of this improved rolling technique on the cube texture formation has been discussed.The results show that the increased cube texture in the Ni7W substrate is caused by the optimized deformation texture and the increased nucleated fraction of the cube grains.
基金supported by the National Natural Science Foundation of China(No.52205313)Natural Science Foundation of Shandong Province(ZR2022QE161),China Postdoctoral Science Foundation(2023M734093)+1 种基金the Tribology Science Fund of State Key Laboratory of Solid Lubrication(LSL-2312)Scientific Innovation Project for Young Scientists in Shandong Provincial Universities(2023KJ145,2023KJ148).
文摘Recently,various slippery liquid-infused porous surfaces(SLIPS)have been fabricated for the protection of various materials.However,these SLIPSs are limited by their underlying storage structure and superficial lubricant layer,showing poor durability.Herein,inspired by the high-strength structure of Shell nacre’s“brick-mud”layer,we fabricated an all-inorganic composite coating by using wet chemically etched MXene as a brick and an aluminum phosphate binder(AP)as mud.Then,a series of microwell-array structures were designed and prepared on the coating via nanosecond ultrafast laser writing ablation technology.Subsequently,the textured surface was modified by a silane coupling agent.Vinyl-terminated polydimethylsiloxane(PDMS)was tightly grafted onto the porous surface through a thiol-ene click reaction to obtain lubricant grafted texture surface(LGTS).The prepared LGTS showed good lubrication properties for multiple phases,including various liquids,ice crystals,and solids.It exhibits excellent chemical stability and mechanical durability under deionized water impact,centrifugal test,strong acid solutions,anti/de-icing cycles,and high-intensity friction.Thus,the proposed strategy for constructing robust LGTS will greatly promote theoretical research on super wetting interfacial materials and their applications in the fields of antifouling,anti/de-icing,and lubricating protection.
基金supports from the National Research Foundation of Korea funded by the Ministry of Education (No. 2018R1A6A1A03024509, NRF-2023R1A2C1005121)
文摘The mechanical properties of an extruded Mg-10Gd sample, specifically designed for vascular stents, are crucial for predicting its behavior under service conditions. Achieving homogeneous stresses in the hoop direction, essential for characterizing vascular stents, poses challenges in experimental testing based on standard specimens featuring a reduced cross section. This study utilizes an elasto-visco-plastic self-consistent polycrystal model(ΔEVPSC) with the predominant twinning reorientation(PTR) scheme as a numerical tool, offering an alternative to mechanical testing. For verification, various mechanical experiments, such as uniaxial tension, compression, notched-bar tension, three-point bending, and C-ring compression tests, were conducted. The resulting force vs. displacement curves and textures were then compared with those based on the ΔEVPSC model. The computational model's significance is highlighted by simulation results demonstrating that the differential hardening along with a weak strength differential effect observed in the Mg-10Gd sample is a result of the interplay between micromechanical deformation mechanisms and deformation-induced texture evolution. Furthermore, the study highlights that incorporating the axisymmetric texture from the as-received material incorporating the measured texture gradient significantly improves predictive accuracy on the strength in the hoop direction. Ultimately, the findings suggest that the ΔEVPSC model can effectively predict the mechanical behavior resulting from loading scenarios that are impossible to realize experimentally, emphasizing its valuable contribution as a digital twin.
基金supported by Research Program of Chongqing Municipal Education Commission(KJQN201901127)University Innovation Research Group of Chongqing(CXQT20023)+2 种基金Natural Science Foundation of Chongqing(cstc2021ycjh-bgzxm0184)support by the Research Program of Chongqing Municipal Education Commission(KJQN202201151)National Natural Science Foundation of China(52201107).
文摘LZ91 Mg-Li alloy plates with three types of initial texture were rolled by 70%reduction at both room temperature and 200℃to explore the rolling texture formation ofα-Mg phase.The results showed that the rolling texture is largely affected by the initial texture.All the samples exhibited two main texture components as RD-split double peaks texture and TD-split double peaks texture after large strain rolling.The intensity of the two texture components was strongly influenced by the initial orientation and rolling temperature.Extension twinning altered the large-split non-basal orientation to a near basal one at low rolling strain.The basal orientation induced by twinning is unstable,which finally transmitted to the RD-split texture.The strong TD-split texture formed due to slip-induced orientation transition from its initial orientation.The competition between prismatic and basal slip determined the intensity and tilt angle of the TD-split texture.By increasing the rolling temperature,the TD-split texture component was enhanced in all three samples.Limitation of extension twinning behavior and the promotion of prismatic slip at elevated temperature are the main reasons for the difference in hot and cold rolling texture.
基金Gobierno de Navarra(Proyectos Estratégicos para Navarra 2020)the FEDER program for the financial support of project NUTRI+。
文摘Dysphagia is commonly associated with malnutrition and an increased choking risk.To overcome these complications,food designed for people with dysphagia should have an appropriate texture and a high nutritional value.In this study,six formulations of a strawberry dessert enriched in protein(calcium caseinate)and fiber(wheat dextrin or inulin)were developed using different hydrocolloids(xanthan gum,carboxymethyl cellulose or modified starch)to provide desirable texture and stability.Nutritional value was calculated and total phenolic content and antioxidant activity of the samples were analyzed.Back-extrusion test,rheological measurements and sensory analysis were performed in refrigerated and frozen samples to characterize their textural and viscoelastic properties.The high content in protein(14.7 g/100 g)and fiber(7.9-8.7 g/100 g)made possible to use the claims“high protein”and“high fiber”.Phytochemicals supplied by strawberries contributed to the antioxidant properties of the dessert.Loss tangent ranged 0.28-0.35 for all the formulations,indicating a weak gel behavior,which could be considered safe to swallow.The formulations with dextrin in combination with carboxymethyl cellulose or xanthan gum seemed to be less susceptible to structural changes during frozen storage.This work provides insights for the development of a nutrient-dense dessert that meets the requirements of people with dysphagia.
基金supported by key technology research and development project of ShanXi province(20201102019)Natural science foundation of Shanxi Province(201901D111167)+2 种基金Shanxi Scholarship Council of China(2020-117)JCKY2018408B003Magnesium alloy high-performance XXX multi-directional extrusion technologyXX supporting scientific research project(xxxx-2019-021).
文摘Hot torsion tests for AZ80 magnesium alloy were carried out in the temperature range of 380℃-260℃,with a constant decreasing temperature rate of 10℃/s in order to weaken the basal texture and refine the grains.The results indicated that the average grain sizes were refined forming gradient structure with increasing specimen radial position from center(12.2-5.4μm),and that the initial basal texture intensity of the extruded magnesium alloy was weakened from 46.2 to 8.3.Furthermore,the extension twins(ETs)could be disintegrated from the twins forming separated twins with smaller sizes.Interestingly,ETs with the same twin variant intersecting with each other could be coalesced forming grains with similar orientation,while ETs with different twin variants were separated by twins boundaries contributing to grain refinement.Moreover,in addition to the conventional continuous dynamic recrystallized(CDRX)grains with 30˚orientation rotated around C-axis of the parent grains,CDRXed grains with 30˚rotation around a-axis and random rotation axis were also discerned.Besides,the CDRX evolution induced twins were also elaborated,exhibiting the complex competition between CDRX and twining.Hot torsion deformation with constant decreasing temperatures rate is an effective way of grain refinement and texture modification.
文摘Magnesium alloys have many advantages as lightweight materials for engineering applications,especially in the fields of automotive and aerospace.They undergo extensive cutting or machining while making products out of them.Dry cutting,a sustainable machining method,causes more friction and adhesion at the tool-chip interface.One of the promising solutions to this problem is cutting tool surface texturing,which can reduce tool wear and friction in dry cutting and improve machining performance.This paper aims to investigate the impact of dimple textures(made on the flank face of cutting inserts)on tool wear and chip morphology in the dry machining of AZ31B magnesium alloy.The results show that the cutting speed was the most significant factor affecting tool flank wear,followed by feed rate and cutting depth.The tool wear mechanism was examined using scanning electron microscope(SEM)images and energy dispersive X-ray spectroscopy(EDS)analysis reports,which showed that at low cutting speed,the main wear mechanism was abrasion,while at high speed,it was adhesion.The chips are discontinuous at low cutting speeds,while continuous at high cutting speeds.The dimple textured flank face cutting tools facilitate the dry machining of AZ31B magnesium alloy and contribute to ecological benefits.
基金Project supported by the National Key R&D Program of China (Grant Nos. 2022YFB3608000 and 2022YFA1204900)the National Natural Science Foundation of China (Grant Nos. 12222413 and 12074205)+2 种基金the Natural Science Foundation of Shanghai (Grant Nos. 23ZR1482200 and 22ZR1473300)the Natural Science Foundation of Zhejiang Province (Grant No. LQ21A040004)the funding of Ningbo University (Grant No. LJ2024003)。
文摘Twisted bilayer graphene(TBG) has been extensively studied because of its novel physical properties and potential application in electronic devices.Here we report the synthesis and characterization of 300 TBG naturally grown on Cu_(0.75)Ni_(0.25)(111) film and investigate the electronic structure by angle-resolved photoemission spectroscopy.Compared with other substrates,our TBG with a wafer scale is acquired with a shorter growth time.The Fermi velocity and energy gap of Dirac cones of TBG are comparable with those of a monolayer on Cu_(0.85)Ni_(0.15)(111).The signature of moré lattices has not been observed in either the low-energy electron diffraction patterns or the Fermi surface map within experimental resolution,possibly due to different Cu and Ni contents in the substrates enhancing the different couplings between the substrate and the first/second layers and hindering the formation of a quasiperiodic structure.
文摘Algal blooms,the spread of algae on the surface of water bodies,have adverse effects not only on aquatic ecosystems but also on human life.The adverse effects of harmful algal blooms(HABs)necessitate a convenient solution for detection and monitoring.Unmanned aerial vehicles(UAVs)have recently emerged as a tool for algal bloom detection,efficiently providing on-demand images at high spatiotemporal resolutions.This study developed an image processing method for algal bloom area estimation from the aerial images(obtained from the internet)captured using UAVs.As a remote sensing method of HAB detection,analysis,and monitoring,a combination of histogram and texture analyses was used to efficiently estimate the area of HABs.Statistical features like entropy(using the Kullback-Leibler method)were emphasized with the aid of a gray-level co-occurrence matrix.The results showed that the orthogonal images demonstrated fewer errors,and the morphological filter best detected algal blooms in real time,with a precision of 80%.This study provided efficient image processing approaches using on-board UAVs for HAB monitoring.
基金financial supports from the Natural Science Foundation of Shandong Province(ZR2021ME241)the Natural Science Foundation of Liaoning Province(No.2020-MS-004)+2 种基金the National Natural Science Foundation of China(NSFC,Nos.51601193 and 51701218)State Key Program of National Natural Science of China(No.51531002)National Key Research and Development Program of China(No.2016YFB0301104).
文摘3%Y_(2)O_(3)p/ZGK200 composites were subjected to unidirectional rolling(UR)and cross rolling(CR)at 400℃and 350℃followed by annealing at 300℃for 1 h.The microstructure,texture and mechanical properties of rolled and annealed composites were systematically studied.The rolled composites exhibited a heterogeneous microstructure,consisting of deformed grains elongated along rolling direction(RD)and Y_(2)O_(3)particles bands distributed along RD.After annealing,static recrystallization(SRX)occurred and most deformed grains transformed into equiaxed grains.A non-basal texture with two strong T-texture components was obtained after UR while a non-basal elliptical/circle texture with circle multi-peaks was obtained after CR,indicating that rolling path had great influences on texture of the composites.After annealing process,R-texture component disappeared or weakened,as results,a non-basal texture with double peaks tilting from normal direction(ND)to transverse direction(TD)and a more random non-basal texture with circle multi-peaks were obtained for UR and CR composites,respectively.The yield strength of rolled composites after UR showed obvious anisotropy along RD and TD while a low anisotropic yield strength was obtained after CR.Some Y_(2)O_(3)particles broke during rolling.The fracture of the composites was attributed to the existence of Y_(2)O_(3)clusters and interfacial debonding between particles and matrix during tension,as a result,the ductility was not as superior as matrix alloy.
基金Projects(52274402,52174381)supported by the National Natural Science Foundation of China。
文摘The effect of forging on the microstructure and texture evolution of a high Nb containing Ti-45Al-7Nb-0.3W(at.%)alloy was investigated by X-ray diffractometer(XRD),scanning electron microscopy(SEM),and transmission electron microscopy(TEM).The results show that the as-cast alloy is mainly composed of α_(2)/γ lamellar colonies with a mean size of 70μm,but the hot-forged pancake displays a near duplex microstructure(DP).Kinking and bending of lamellar colonies,deformation twinning and dynamic recrystallization(DRX)occur during hot forging.Meanwhile,dense dislocations in theβphase after forging suggest that the high-temperature β phase with a disordered structure is favorable for improving the hot-workability of the alloy.Unlike the common TiAl casting texture,the solidification process of the investigated as-cast alloy with high Nb content is completely via the β phase region,resulting in the formation of a<110>γ fiber texture where the<110>γ aligns parallel to the heat-flow direction.In comparison,the relatively strong<001>and weak<302>texture components in the as-forged alloy are attributed to the deformation twinning.After annealing,static recrystallization occurs at the twin boundary and intersections,which weakens the deformation texture.
文摘Purpose: This review examines the diagnostic value of transvaginal 3D ultrasound image texture analysis for the diagnosis of uterine adhesions. Materials and Methods: The total clinical data of 53 patients with uterine adhesions diagnosed by hysteroscopy and the imaging data of transvaginal three-dimensional ultrasound from the Second Affiliated Hospital of Chongqing Medical University from June 2022 to August 2023 were retrospectively analysed. Based on hysteroscopic surgical records, patients were divided into two independent groups: normal endometrium and uterine adhesion sites. The samples were divided into a training set and a test set, and the transvaginal 3D ultrasound was used to outline the region of interest (ROI) and extract texture features for normal endometrium and uterine adhesions based on hysteroscopic surgical recordings, the training set data were feature screened and modelled using lasso regression and cross-validation, and the diagnostic efficacy of the model was assessed by applying the subjects’ operating characteristic (ROC) curves. Results: For each group, 290 texture feature parameters were extracted and three higher values were screened out, and the area under the curve of the constructed ultrasonographic scoring model was 0.658 and 0.720 in the training and test sets, respectively. Conclusion Relative clinical value of transvaginal three-dimensional ultrasound image texture analysis for the diagnosis of uterine adhesions.
基金Supported by National Natural Science Foundation of China,No.81560278the Health Commission of Guangxi Zhuang Autonomous Region,No.Z-A20221157,No.Z20200953,and No.G201903023.
文摘BACKGROUND Despite continuous changes in treatment methods,the survival rate for advanced hepatocellular carcinoma(HCC)patients remains low,highlighting the importance of diagnostic methods for HCC.AIM To explore the efficacy of texture analysis based on multi-parametric magnetic resonance(MR)imaging(MRI)in predicting microvascular invasion(MVI)in preoperative HCC.METHODS This study included 105 patients with pathologically confirmed HCC,categorized into MVI-positive and MVI-negative groups.We employed Original Data Analysis,Principal Component Analysis,Linear Discriminant Analysis(LDA),and Non-LDA(NDA)for texture analysis using multi-parametric MR images to predict preoperative MVI.The effectiveness of texture analysis was determined using the B11 program of the MaZda4.6 software,with results expressed as the misjudgment rate(MCR).RESULTS Texture analysis using multi-parametric MRI,particularly the MI+PA+F dimensionality reduction method combined with NDA discrimination,demonstrated the most effective prediction of MVI in HCC.Prediction accuracy in the pulse and equilibrium phases was 83.81%.MCRs for the combination of T2-weighted imaging(T2WI),arterial phase,portal venous phase,and equilibrium phase were 22.86%,16.19%,20.95%,and 20.95%,respectively.The area under the curve for predicting MVI positivity was 0.844,with a sensitivity of 77.19%and specificity of 91.67%.CONCLUSION Texture analysis of arterial phase images demonstrated superior predictive efficacy for MVI in HCC compared to T2WI,portal venous,and equilibrium phases.This study provides an objective,non-invasive method for preoperative prediction of MVI,offering a theoretical foundation for the selection of clinical therapy.
基金partly supported by the National Research Foundation of Korea (NRF) grant funded by the Korea government (MSIT) (No. 2020R1C1C1005726)Technology development Program (No. RS-2023-00220823) funded by the Ministry of SMEs and Startups (MSS, Korea)+1 种基金the Electronics Technology Development Project (No. 20026289) funded By the Ministry of Trade, Industry & Energy (MOTIE, Korea)partly supported by the research grant of the Kongju National University in 2022
文摘Hot torsion tests were performed on the Al-7Mg alloy at the temperature ranging from 300 to 500℃ and strain rates between 0.05 and 5 s^(-1) to explore the progressive dynamic recrystallization(DRX)and texture behaviors.The DRX behavior of the alloy manifested two distinct stages:Stage 1 at strain of≤2 and Stage 2 at strains of≥2.In Stage 1,there was a slight increase in the DRXed grain fraction(X_(DRX))with predominance of discontinuous DRX(DDRX),followed by a modest change in X_(DRX) until the transition to Stage 2.Stage 2 was marked by an accelerated rate of DRX,culminating in a substantial final X_(DRX) of~0.9.Electron backscattered diffraction(EBSD)analysis on a sample in Stage 2 revealed that continuous DRX(CDRX)predominantly occurred within the(121)[001]grains,whereas the(111)[110]grains underwent a geometric DRX(GDRX)evolution without a noticeable sub-grain structure.Furthermore,a modified Avrami’s DRX kinetics model was utilized to predict the microstructural refinement in the Al-7Mg alloy during the DRX evolution.Although this kinetics model did not accurately capture the DDRX behavior in Stage 1,it effectively simulated the DRX rate in Stage 2.The texture index was employed to assess the evolution of the texture isotropy during hot-torsion test,demonstrating significant improvement(>75%)in texture randomness before the commencement of Stage 2.This initial texture evolution is attributed to the rotation of parent grains and the substructure evolution,rather than to an increase in X_(DRX).