After different heat treatment processes,the metal compound,the microstructure and the hardness of the C-Cr-W-Mo-V-RE Fe-based hardfacing layers are investigated by means of metallographic microscope,X-ray diffraction...After different heat treatment processes,the metal compound,the microstructure and the hardness of the C-Cr-W-Mo-V-RE Fe-based hardfacing layers are investigated by means of metallographic microscope,X-ray diffraction(XRD), energy dispersive spectrum(EDS),transmission electron microscope(TEM) and hardness tester. The results show that the hardfacing layers have higher tempering stability and secondary hardening property. After quenching at 820℃,the hardness value(HRC37)and the microstructure of the layers are similar to that normalized at 820-1000℃. The tempering stability and the hardness increases with increasing quench temperature,which is attributed to the amount of the alloy element in the matrix. These results are very helpful for improving the mechanical properties of the hardfacing layers.展开更多
Fe C Cr weld surfacing layers with different compositions and microstructures can be obtained by submerged arc welding with welding wire of the low carbon steel and high alloy bonded flux. With the increase of Cr and ...Fe C Cr weld surfacing layers with different compositions and microstructures can be obtained by submerged arc welding with welding wire of the low carbon steel and high alloy bonded flux. With the increase of Cr and C in the layers the microstructures are changed from hypoeutectoid steel, hypereutectoid steel to hypoeutectic iron and hypereutectic iron. When the weld surfacing layers belong to the alloyed cast irons the erosion resistance can be raised with the eutectic increase and the austenite decrease. Good erosion resistance can be obtained when the proportion of the primary carbides is within 10 %. The experimental results lay a foundation to make double metal percussive plates by surfacing wear resistant layers on the substrates of the low carbon steels.展开更多
The scarcity of housing increases as population continues to rise all over the world. Despite government efforts at providing houses, yearly demand keeps on exceeding available houses and hence the hike in rent, the c...The scarcity of housing increases as population continues to rise all over the world. Despite government efforts at providing houses, yearly demand keeps on exceeding available houses and hence the hike in rent, the cost of erecting houses and the cost of building materials. This ultimately calls for a decisive solution. This study therefore applied compliance to cost ratio (C-CR) analysis in evaluating the optimum properties of fired ceramic bricks. The optimum mix proportions of waste glass (WG) and wood saw dust (WSD) in fired bricks, that will be suitable for housing constructions were hence determined. Fired clay brick samples which contained varied proportions of WG and WSD were examined for physical, mechanical and thermal properties in line with standard procedures. The results were compared with existing standards and property evaluation index, compliance level and C-CR were applied in analyzing the results obtained. It was observed that with increasing WG content, compliance level increased. Also, cost ratio and experimental cost of each brick sample trended upward. Sample with mix proportion;20 wt% WG, 5 wt% WSD and 75 wt% clay had compliance level of 94% and C-CR index of 7.81, hence chosen as optimum mix proportion for masonry bricks.展开更多
Based on the current situation of studying the thermodynamic property of Fe-C-Cr melt using the carbon saturated solubility, an experimental data treatment method of the carbon saturated solubility was put forward. Wi...Based on the current situation of studying the thermodynamic property of Fe-C-Cr melt using the carbon saturated solubility, an experimental data treatment method of the carbon saturated solubility was put forward. With this method a linear relationship ex- pression of the carbon saturated solubility in Fe-C-Cr melt was obtained, which intercept is dependent on temperature and independent of third component [Cr], but which slope is dependent on third component [Cr] and independent of temperature. Through this expression activity interaction coefficients at different temperatures were calculated and the relationship between activity interaction coefficients and temperature is also obtained.展开更多
文摘After different heat treatment processes,the metal compound,the microstructure and the hardness of the C-Cr-W-Mo-V-RE Fe-based hardfacing layers are investigated by means of metallographic microscope,X-ray diffraction(XRD), energy dispersive spectrum(EDS),transmission electron microscope(TEM) and hardness tester. The results show that the hardfacing layers have higher tempering stability and secondary hardening property. After quenching at 820℃,the hardness value(HRC37)and the microstructure of the layers are similar to that normalized at 820-1000℃. The tempering stability and the hardness increases with increasing quench temperature,which is attributed to the amount of the alloy element in the matrix. These results are very helpful for improving the mechanical properties of the hardfacing layers.
文摘Fe C Cr weld surfacing layers with different compositions and microstructures can be obtained by submerged arc welding with welding wire of the low carbon steel and high alloy bonded flux. With the increase of Cr and C in the layers the microstructures are changed from hypoeutectoid steel, hypereutectoid steel to hypoeutectic iron and hypereutectic iron. When the weld surfacing layers belong to the alloyed cast irons the erosion resistance can be raised with the eutectic increase and the austenite decrease. Good erosion resistance can be obtained when the proportion of the primary carbides is within 10 %. The experimental results lay a foundation to make double metal percussive plates by surfacing wear resistant layers on the substrates of the low carbon steels.
文摘The scarcity of housing increases as population continues to rise all over the world. Despite government efforts at providing houses, yearly demand keeps on exceeding available houses and hence the hike in rent, the cost of erecting houses and the cost of building materials. This ultimately calls for a decisive solution. This study therefore applied compliance to cost ratio (C-CR) analysis in evaluating the optimum properties of fired ceramic bricks. The optimum mix proportions of waste glass (WG) and wood saw dust (WSD) in fired bricks, that will be suitable for housing constructions were hence determined. Fired clay brick samples which contained varied proportions of WG and WSD were examined for physical, mechanical and thermal properties in line with standard procedures. The results were compared with existing standards and property evaluation index, compliance level and C-CR were applied in analyzing the results obtained. It was observed that with increasing WG content, compliance level increased. Also, cost ratio and experimental cost of each brick sample trended upward. Sample with mix proportion;20 wt% WG, 5 wt% WSD and 75 wt% clay had compliance level of 94% and C-CR index of 7.81, hence chosen as optimum mix proportion for masonry bricks.
文摘Based on the current situation of studying the thermodynamic property of Fe-C-Cr melt using the carbon saturated solubility, an experimental data treatment method of the carbon saturated solubility was put forward. With this method a linear relationship ex- pression of the carbon saturated solubility in Fe-C-Cr melt was obtained, which intercept is dependent on temperature and independent of third component [Cr], but which slope is dependent on third component [Cr] and independent of temperature. Through this expression activity interaction coefficients at different temperatures were calculated and the relationship between activity interaction coefficients and temperature is also obtained.