The(Cu−10Sn)−Ni−MoS2 composites,prepared by powder metallurgy,were studied for the effects of Ni-coated MoS2 on the microstructure,mechanical properties and lubricating properties.The mechanism of effects of Ni and Mo...The(Cu−10Sn)−Ni−MoS2 composites,prepared by powder metallurgy,were studied for the effects of Ni-coated MoS2 on the microstructure,mechanical properties and lubricating properties.The mechanism of effects of Ni and MoS2 on the properties of composites was analyzed through a comparative experiment by adding Ni and MoS2 separately.The results show that the nickel wrapping around the MoS2 particles decreases the reaction rate of MoS2 with the copper matrix,and greatly improves the bonding of the matrix.The composites with 12 wt.%Ni-coated MoS2(C12)show the optimum performance including the mechanical properties and tribological behaviors.Under oil lubrication conditions,the friction coefficient is 0.0075 with a pressure of 8 MPa and a linear velocity of 0.25 m/s.The average dry friction coefficient,sliding against 40Cr steel disc,is measured to be 0.1769 when the linear velocity and pressure are 0.25 m/s and 4 MPa,respectively.展开更多
采用铜模吸铸法在TiNiCuSn合金系中添加难熔金属Nb,制备出了d3 mm Ti60Cu14Ni12Sn4Nb10棒状多相复合材料。对该合金的显微组织特征和相组成进行了分析,并对其室温压缩性能进行了测试。研究结果表明,Ti60Cu14Ni12Sn4Nb10的显微组织主要由...采用铜模吸铸法在TiNiCuSn合金系中添加难熔金属Nb,制备出了d3 mm Ti60Cu14Ni12Sn4Nb10棒状多相复合材料。对该合金的显微组织特征和相组成进行了分析,并对其室温压缩性能进行了测试。研究结果表明,Ti60Cu14Ni12Sn4Nb10的显微组织主要由β-Ti枝晶相、纳米晶化相和少量非晶相组成。该合金在室温下表现出较好的综合力学性能,其抗压断裂强度可达1.71 GPa,断裂应变约为17.7%,弹性模量为116 GPa。合金的断口分析结果表明,由于产生了塑性枝晶相,因此该合金具有较高塑性。展开更多
基金Projects(51371099,51501091)supported by the National Natural Science Foundation of China。
文摘The(Cu−10Sn)−Ni−MoS2 composites,prepared by powder metallurgy,were studied for the effects of Ni-coated MoS2 on the microstructure,mechanical properties and lubricating properties.The mechanism of effects of Ni and MoS2 on the properties of composites was analyzed through a comparative experiment by adding Ni and MoS2 separately.The results show that the nickel wrapping around the MoS2 particles decreases the reaction rate of MoS2 with the copper matrix,and greatly improves the bonding of the matrix.The composites with 12 wt.%Ni-coated MoS2(C12)show the optimum performance including the mechanical properties and tribological behaviors.Under oil lubrication conditions,the friction coefficient is 0.0075 with a pressure of 8 MPa and a linear velocity of 0.25 m/s.The average dry friction coefficient,sliding against 40Cr steel disc,is measured to be 0.1769 when the linear velocity and pressure are 0.25 m/s and 4 MPa,respectively.
文摘采用铜模吸铸法在TiNiCuSn合金系中添加难熔金属Nb,制备出了d3 mm Ti60Cu14Ni12Sn4Nb10棒状多相复合材料。对该合金的显微组织特征和相组成进行了分析,并对其室温压缩性能进行了测试。研究结果表明,Ti60Cu14Ni12Sn4Nb10的显微组织主要由β-Ti枝晶相、纳米晶化相和少量非晶相组成。该合金在室温下表现出较好的综合力学性能,其抗压断裂强度可达1.71 GPa,断裂应变约为17.7%,弹性模量为116 GPa。合金的断口分析结果表明,由于产生了塑性枝晶相,因此该合金具有较高塑性。