Roman scattering measurement of （ 1 - x ） GeS2-x Ga2S3 system glasses was conducted in order to understand the microstructural change caused by the addition of Ga2S3 . According to the change of Raman spectra with t...Roman scattering measurement of （ 1 - x ） GeS2-x Ga2S3 system glasses was conducted in order to understand the microstructural change caused by the addition of Ga2S3 . According to the change of Raman spectra with the addition of Ga2S3, two main structural transformations were deduced ： the gradual enhancement of ethane- like structural units S3 Ge- GeS3 （ 250 cm ^- 1） and S3 Ga- GaS3 （270 cm ^- 1 ） and the appearance of charge imbalanced units [ Ga2 S2 （ S1/2 ）4 ]^2- and [Ga（ S1/2 ）4 ]^- . And this change of structural aspect seems to give as a clue to understanding the cause of the increased rare-earth solubility.展开更多
文摘Roman scattering measurement of （ 1 - x ） GeS2-x Ga2S3 system glasses was conducted in order to understand the microstructural change caused by the addition of Ga2S3 . According to the change of Raman spectra with the addition of Ga2S3, two main structural transformations were deduced ： the gradual enhancement of ethane- like structural units S3 Ge- GeS3 （ 250 cm ^- 1） and S3 Ga- GaS3 （270 cm ^- 1 ） and the appearance of charge imbalanced units [ Ga2 S2 （ S1/2 ）4 ]^2- and [Ga（ S1/2 ）4 ]^- . And this change of structural aspect seems to give as a clue to understanding the cause of the increased rare-earth solubility.