The emeraldine base form of polyaniline (PANI) can be doped by a photo-induced doping method. In this method a. copolymer of vinylidene chloride and methyl acrylate (VCMAC) was used as photo acid generator which can r...The emeraldine base form of polyaniline (PANI) can be doped by a photo-induced doping method. In this method a. copolymer of vinylidene chloride and methyl acrylate (VCMAC) was used as photo acid generator which can release proton when it is exposed to ultraviolet light (lambda = 254 nm). The structure of PANI-VCMAC system before and after irradiation was characterized by elemental analysis, IR, XTP, anti SEM images. Results obtained indicate that the photo-induced doping characteristics, such as doping position and type of charge carriers, are similar to that of PANI doped with HCl. The poor room-temperature conductivity (similar to 10-S-5/cm) of PANI-VCMAC system after irradiation may be due to low doping degree (similar to pH=3) and the difference in morphology as compared with PANI-HCl film.展开更多
基金The work was supported by the National Natural Science Foundation of China
文摘The emeraldine base form of polyaniline (PANI) can be doped by a photo-induced doping method. In this method a. copolymer of vinylidene chloride and methyl acrylate (VCMAC) was used as photo acid generator which can release proton when it is exposed to ultraviolet light (lambda = 254 nm). The structure of PANI-VCMAC system before and after irradiation was characterized by elemental analysis, IR, XTP, anti SEM images. Results obtained indicate that the photo-induced doping characteristics, such as doping position and type of charge carriers, are similar to that of PANI doped with HCl. The poor room-temperature conductivity (similar to 10-S-5/cm) of PANI-VCMAC system after irradiation may be due to low doping degree (similar to pH=3) and the difference in morphology as compared with PANI-HCl film.