One-dimensional and quasi-one-dimensional nanostructure materials are promising building blocks for electromagnetic devices and nanosystems.In this work,the composite Ni0.5Zn0.5Fe2O4（NZFO）/ Pb（Zr0.52Ti0.48）O3（PZT...One-dimensional and quasi-one-dimensional nanostructure materials are promising building blocks for electromagnetic devices and nanosystems.In this work,the composite Ni0.5Zn0.5Fe2O4（NZFO）/ Pb（Zr0.52Ti0.48）O3（PZT） nanofibers with average diameters about 65 nm are prepared by electrospinning from poly（vinyl pyrrolidone） （PVP） and metal salts.The precursor composite NZFO/PZT/PVP nanofibers and the subsequent calcined NZFO/PZT nanofibers are investigated by Fourier transform infrared spectroscopy （FT- IR） ,X-ray diffraction （XRD）,scanning electron microscopy （SEM）.The magnetic properties for nanofibers are measured by vibrating sample magnetometer（VSM）.The NZFO/PZT nanofibers obtained at calcination temperature of 900 °C for 2 h consist of the ferromagnetic spinel NZFO and ferroelectric perovskite PZT phases,which are constructed from about 37 nm NZFO and 17 nm PZT grains.The saturation magnetization of these NZFO/PZT nanofibers increases with increasing calcination temperature and contents of NZFO in the composite.展开更多
基金Funded by the National Natural Science Foundation of China (No. 50674048)Research Fund for the Doctoral Program of Higher Education of China(No.20103227110006)
文摘One-dimensional and quasi-one-dimensional nanostructure materials are promising building blocks for electromagnetic devices and nanosystems.In this work,the composite Ni0.5Zn0.5Fe2O4（NZFO）/ Pb（Zr0.52Ti0.48）O3（PZT） nanofibers with average diameters about 65 nm are prepared by electrospinning from poly（vinyl pyrrolidone） （PVP） and metal salts.The precursor composite NZFO/PZT/PVP nanofibers and the subsequent calcined NZFO/PZT nanofibers are investigated by Fourier transform infrared spectroscopy （FT- IR） ,X-ray diffraction （XRD）,scanning electron microscopy （SEM）.The magnetic properties for nanofibers are measured by vibrating sample magnetometer（VSM）.The NZFO/PZT nanofibers obtained at calcination temperature of 900 °C for 2 h consist of the ferromagnetic spinel NZFO and ferroelectric perovskite PZT phases,which are constructed from about 37 nm NZFO and 17 nm PZT grains.The saturation magnetization of these NZFO/PZT nanofibers increases with increasing calcination temperature and contents of NZFO in the composite.
基金This work was supported by the National Natural Science Foundation of China (Grant No. 69771024) the Natural Science Foundation of Hebei Province (Grant No. 98J026) .