Monodisperse poly (chloromethylstyrene divinylbenzene) particles were prepared by a two-step swelling method. It was demonstrated that the packings have comparative advantages for biopolymer separation with high colum...Monodisperse poly (chloromethylstyrene divinylbenzene) particles were prepared by a two-step swelling method. It was demonstrated that the packings have comparative advantages for biopolymer separation with high column efficiency, low interstitial volume and low back pressure to the packings prepared with suspension polymerization method. Using size exclusionchromatography and weak ion exchange chromatography as examples, it was shown that these packings could be modified chemically more easily than poly (styrene divinylbenzene) packings.展开更多
Monodisperse crosslinked poly(chloromethylstyrene-co-divinylbenzene)(poly(CMSt-co-DVB))microsphereswere prepared by distillation-precipitation copolymerization of chloromethylstyrene(CMSt)and divinylbenzene(DVB)inneat...Monodisperse crosslinked poly(chloromethylstyrene-co-divinylbenzene)(poly(CMSt-co-DVB))microsphereswere prepared by distillation-precipitation copolymerization of chloromethylstyrene(CMSt)and divinylbenzene(DVB)inneat acetonitrile.The polymer particles had clean surfaces due to the absence of any added stabilizer.The size of the particlesranges from 2.59 μm to 3.19 μm and with mono-dispersity around 1.002-1.014.The effects of monomer feed incopolymerization on the microsphere formation were described.The polymer microspheres were characterized by SEM andchlorinity elemental analysis.展开更多
文摘Monodisperse poly (chloromethylstyrene divinylbenzene) particles were prepared by a two-step swelling method. It was demonstrated that the packings have comparative advantages for biopolymer separation with high column efficiency, low interstitial volume and low back pressure to the packings prepared with suspension polymerization method. Using size exclusionchromatography and weak ion exchange chromatography as examples, it was shown that these packings could be modified chemically more easily than poly (styrene divinylbenzene) packings.
基金This work was funded by the financial support of the National Natural Science Foundation of China(Project No.20274018)Nankai University.
文摘Monodisperse crosslinked poly(chloromethylstyrene-co-divinylbenzene)(poly(CMSt-co-DVB))microsphereswere prepared by distillation-precipitation copolymerization of chloromethylstyrene(CMSt)and divinylbenzene(DVB)inneat acetonitrile.The polymer particles had clean surfaces due to the absence of any added stabilizer.The size of the particlesranges from 2.59 μm to 3.19 μm and with mono-dispersity around 1.002-1.014.The effects of monomer feed incopolymerization on the microsphere formation were described.The polymer microspheres were characterized by SEM andchlorinity elemental analysis.