Effect of slow shot speed on externally solidified crystal,porosity and tensile property in a newly developed high-pressure die-cast Al-Si alloy

The effect of slow shot speed on externally solidified crystal(ESC),porosity and tensile property in a newly developed high-pressure die-cast Al-Si alloy was investigated by optical microscopy(OM),scanning electron microscopy(SEM)and laboratory computed tomography(CT).Results showed that the newly developed AlSi9MnMoV alloy exhibited improved mechanical properties when compared to the AlSi10MnMg alloy.The AlSi9MnMoV alloy,which was designed with trace multicomponent additions,displays a notable grain refining effect in comparison to the AlSi10MnMg alloy.Refining elements Ti,Zr,V,Nb,B promote heterogeneous nucleation and reduce the grain size of primaryα-Al.At a lower slow shot speed,the large ESCs are easier to form and gather,developing into the dendrite net and net-shrinkage.With an increase in slow shot speed,the size and number of ESCs and porosities significantly reduce.In addition,the distribution of ESCs is more dispersed and the net-shrinkage disappears.The tensile property is greatly improved by adopting a higher slow shot speed.The ultimate tensile strength is enhanced from 260.31 MPa to 290.31 MPa(increased by 11.52%),and the elongation is enhanced from 3.72%to 6.34%(increased by 70.52%).

Effect of mixing temperature on microstructure of an Al-Si alloy prepared by controlled diffusion solidification

The effects of mixing temperature,i.e.,the temperatures of two precursor melts(pure Al and Al-12Si),on the temperature and solute fields of resultant mixture,the nucleation and growth,and the size and morphology of primary grains during controlled diffusion solidification(CDS) of Al-8Si alloy were investigated by using simulation and calculation.The results indicate that a lower mixing temperature is helpful for achieving more supercooled microscale Al-rich pockets in the mixture,and increasing the width and supercooling degree of supercooling zone in the Al-rich pockets,and thus,the nucleation rate.The nuclei grow up in nondendritic mode,resulting in spheroidal,at least,nondendritic grains.In a successful CDS,the superheat degrees of the two precursor melts should be limited within several degrees,and it is not necessary to extra stipulate the superheat degree of target alloy melt(Al-8Si) when the requirement about Gibbs energies of the three melts is matched.Subsequent observation on casting microstructures shows that the employed simulation and calculation processes are reasonable and the achieved results are reliable.

Microstructure and mechanical properties of hypereutectic Al-Si alloy modified with Cu-P

The microstructure and mechanical properties of Al-14.6Si castings modified by Cu-P master alloy under different conditions were studied with optical microscope（OM） and mechanical testing and simulation（MTS）.The results indicate that the Cu-P master alloy possesses not only obvious modification effect,but also longevity effect with more than 8 h on the hypereutectic Al-Si alloy.It is shown from thermal calculation,scanning electron microscope（SEM）,and energy dispersive analysis of X-rays（EDAX） that the modification mechanism of Cu-P on primary silicon in the castings is heterogeneous nucleation around AlP particles.The Cu-P master alloy has no or little modifying effect on eutectic silicon,even though it has obvious modification on primary silicon in the castings.This may be because of the fast transformation of eutectic silicon at a very narrow temperature,which will notably weaken the role of AlP particles as heterogeneous nuclei for eutectic silicon.

Research on semi-solid slurry of a hypoeutectic Al-Si alloy prepared by low superheat pouring and weak electromagnetic stirring

The semi-solid slurry of a hypoeutectic Al-Si alloy was manufactured by low superheat pouring and weak electromagnetic stirring. The effects of pouting temperature and stirring power on the semi-solid slurry were investigated. The results indicated that the semi-solid slurry to satisfy rheocasting can be manufactured by low superheat pouring and weak electromagnetic stirring. The pouring temperature （or superheat） and the stirring power remarkably affected the morphology of primary α-Al and the size of primary α-Al, and there is no obvious effect of stirring time on primary α-Al. Compared with the samples made by low superheat pouring with no stirring, the nucleation rate, particle morphology and grain size of primary α-Al in A356 were markedly improved by low superheat pouring and weak electromagnetic stirring. On the condition of weak electromagnetic stirring, the pouring temperature with low superheat can be suitably raised to reach the effectiveness obtained from the lower pouring temperature without stirring.

Al-Si-P master alloy and its modification and refinement performance on Al-Si alloys

An Al-Si-P master alloy has been developed by an in-situ reaction and the electron probe microanalyzer （EPMA） results show that there are many pre-formed AlP particles contained in the master alloy. Silicon introduced into the system plays an important role in remarkably improving the distribution and content of AlP particles due to their similar crystal structure and lattice parameters. ZL109 alloys have shown fast modification response to the addition of 0.5% Al-15Si-3.5P master alloy at 720℃, with a mass of primary Si precipitating in size of about 15 μm. Also, coarse primary Si grains in AI-30Si alloy can be refined dramatically from 150 μm to 37 μm after the addition of 2.0% Al-15Si-3.5P master alloy at 850℃. The P recovery of the Al-15Si-3.5P master alloy is much higher than that of a Cu-8.5P master alloy due to the pre-formed AlP particles.

Functions and mechanism of modification elements in eutectic solidification of Al-Si alloys:A brief review

Being used more and more widely in engineering,AlSi alloys comprise about 80%of all kinds of aluminum alloys,which are the most widely utilized nonferrous alloys.Although most Al-Si alloys consist of multiple components,the eutectics in the structure accounts for 50%-90%of the sum volume of such alloys.Therefore,understanding the modification mechanism and function rules of the AlSi eutectic solidification is the technical key in controlling the structures and properties of such casting alloys.The present paper chiefly reviews recent investigation developments and important conclusions along the lines of the functions of modification elements and their modification mechanism in the eutectic solidification of Al-Si alloys.

Solidification structure of eutectic Al-Si alloy under a high magnetic field-aid-electromagnetic vibration

An electromagnetic vibration was generated by simultaneously imposing a strong static magnetic field （up to 10 T） and an alternative electricity current to the metal. Its effects on the solidification structure of eutectic Al-Si alloy have been investigated experimentally. It is found that the eutectic structure has been refined by solely imposing high magnetic field while it is coarsened under the electromagnetic vibration. Furthermore, polyhedral Si grains and non-dendritic α-Al appeared when the electromagnetic vibration strength was strong enough. The refining of eutectic structure is attributed to the decrease of diffusion coefficient caused by the strong magnetic field. The coarseness of eutectic structure may be attributed to the convection caused by electromagnetic vibration. Strong convection may break co-operative growth of eutectic phases to form polyhedral Si grains and non-dendritic α-Al.

Effects of electric pulse on microstructure of Al-Si alloy in liquid and solid states

In order to investigate the change in liquid microstructure of Al-Si alloytreated by electric pulse (EP), X-ray diffraction tests with liquid Al-Si alloy and ZL109 alloytreated or not by EP were carried out. The results show that the number of Al-Si atomic clustersdecreases and that of Al-Al and Si-Si atomic clusters increases for the treated samples. The testswith ZL109 alloy indicate that a large amount of primary crystal Si appears in the solidifiedmicrostructure after treated by EP. It is found that EP can change the microstructure of liquidmetal by affecting the probability of electrons appearing in different atoms (Al and Si) in theliquid metal. The combining force of different atoms decreases relatively, and that of the sameatoms increases, which is the main reason of reducing the atomic cluster with different atoms(Al-Si) and increasing the atomic cluster with the same atoms (Al-Al, Si-Si). The increasing of theatomic cluster with the same atom cluster resulted in the increasing of Si activity and the higherpoint of eutectics in the phase diagram. It makes a lot of primary silicon appeared in ZL109 alloy.

Distributions of Sr and Fe and their influence on modification of hypoeutectic Al-Si alloy

The influence of cooling rate and Fe-containing phases on Sr-modification of Si phases in hypoeutectic Al-Si alloys, a problem with great industrial importance, was investigated. The microstructures of samples were examined using scanning electron microscopy(SEM) with energy-dispersive X-ray spectroscopy(EDX). A new method of electron probe microanalysis(EPMA) map scanning was used to analyze the Sr distribution, which gave quantitative results covering more Si particles. EPMA map scanning, together with SEM with EDX, was also used in analyzing the distribution of Fe phases. Results show that Fe-containing phase was related to the unmodified Si particles in samples with partial modification failure and the plate-like Si phases in samples without modification failure. Such a relationship was further confirmed by the microstructure observation.In conclusion, a partial failure of Sr-modification can be caused by both slow cooling rate and Fe-containing phases.

AN IN SITU SURFACE COMPOSITE AND GRADIENT MATERIAL OF Al-Si ALLOY PRODUCED BY ELECTROMAGNETIC FORCE

Because of the different conductivities between the primary phase (low electric conduc tivity) and the metal melt, electromagnetic force scarcely acts on the primary phase. Thus, an electromagnetic repulsive force applied by the metal melt exerts on the pri mary phase when the movement of the melt in the direction of electromagnetic force is limited. As a result, the repulsive force exerts on the primary phase to push them to move in the direction opposite to that of the electromagnetic force when the metal melt with primary phase solidifies under an electromagnetic force field. Based on this, a new method for production of in situ surface composite and gradient material by electromagnetic force is proposed. An in situ primary Si reinforced surface composite of Al-15wt%Si alloy and gradient material of Al-l9wt%Si alloy were produced by this method. The microhardness of the primary Si is HV1320. The reinforced phase size is in the range from 40μm to 100μm. The wear resistance of Al-Si alloy gradient material can be more greatly increased than that of their matrix material.

Electromagnetic Filtration of Primary Fe-Rich Phases from Al-Si Alloy Melt

Electromagnetic filtration of primary Fe-rich phases (complex compound of AlFeSiMn) from Al-Si alloy melt containing 1.2 wt pct Fe have been studied by theoretical analysis and on a self-designed electromagnetic filtration equipment. The principle of the electromagnetic filtration is that the EMF (electromagnetic force) scarcely acts on the primary Fe-rich phases having low electric conductivity, which are then moved in the direction opposite to that of the EMF. Experimental results show that the primary Fe-rich phases are separated from Al-Si alloy melt and are collected in the filter while the melt is in horizontal flow. The removal efficiency of the primary iron-phases (77) calculated is less as the greatest flow velocity of the melt (UM) and the height of the filter (2h) are larger, while it becomes larger as EMF, operating distance of electromagnetic force (cr) and particle size (dv) become larger. It has been confirmed that the primary iron-phases larger than 20 jim can be removed efficiently by theoretical analysis and experiments. This new technique is high efficient and available for continuously flowing melts as compared with natural settling and filtration methods, which offer a possibility for recycling high quality aluminum alloys.

Characteristics and Microstructure of a Hypereutectic Al-Si Alloy Powder by Ultrasonic Gas Atomization Process

A hypereutectic Al-Si alloy powder was prepared by ultrasonic gas atomization process. The morphologies, microstructure and phase constituent of the alloy powder were studied. The results showed that powder of the alloy was very fine and its microstructure was mainly consisted of Si crystals plus intermetallic compound A19FeSi3, which were.very fine and uniformly distributed.

Fabrication of ceramic layer on an Al-Si alloy by MAO process

The MAO (Micro-Arc Oxidation) process is applied to a eutectic Al-Si alloy(Al-12.0 percent Si-l.0 percent Cu-0.9 percent Mg (mass fraction)). The oxide ceramic layer wasfabricated with about 220 mum thickness and 3000 Hv micro-hardness. By XRD (X-ray diffractometry)and DSC (differential scanning calorimetry) analyses, the oxide layer consists of amorphous Al_2O_3,which is distinct from the results reported by the other researchers. The SEM photographs of suchlayer show that the layer is fixed tightly on the substrate alloy. So this alloy can he used in thehigh temperature and friction environment alter it is treated with such process.

Separation of primary solid phases from Al-Si alloy melts

The iron-rich solids formed during solidification of Al-Si alloys which are known to be detrimental to the mechanical,physical and chemical properties of the alloys should be removed.On the other hand,Al-Si hypereutectic alloys are used to extract the pure primary silicon which is suitable for photovoltaic cells in the solvent refining process.One of the important issues in iron removal and in solvent refining is the effective separation of the crystallized solids from the Al-Si alloy melts.This paper describes the separation methods of the primary solids from Al-Si alloy melts such as sedimentation,draining,filtration,electromagnetic separation and centrifugal separation,focused on the iron removal and on the separation of silicon in the solvent refining process.

Effects of P+Cr complex modification and solidification conditions on microstmcture of hypereutectic Al-Si alloys by wedge-shaped copper mould casting

Large and segregated primary Si particles may drastically decrease the mechanical properties of Al-Si alloys. To solve this problem, a P-Cr complex modif ier was added into the alloy, and the effects of P-Cr complex modification and solidification conditions on the microstructure of hypereutectic Al-Si alloys casting produced in wedge-shaped copper mould were studied. The thermal analysis technique was applied to calculate the cooling rate during solidification. The microstructures were observed by means of optical and scanning electron microscopies. Results showed that the primary Si segregates in the as-cast hypereutectic Al-Si alloys. The segregation of primary Si can be inhibited by adding a P+Cr complex modif ier and increasing the cooling rate during solidif ication. The ref inement of primary Si particles by P+Cr complex modif ication is due to the formation of CrS i2 and AlP particles which act as the heterogeneous nuclei for the primary Si phase. The segregation of Si was also inhibited through the adherence of heavier CrS i2 particles to the primary Si particles.

TEMPERATURE DEPENDENCE OF VISCOSITY OF Al-Si ALLOY MELTS

The relationship between the viscosity and temperature of Al-Si alloy melts was investigated. The viscosity of three different types of Al-Si alloy melts was measured. It was showed that the relationship between the viscosity and temperature of hypoeutectic Al-5%Si and eutectic Al- 12.5%Si alloy melts is approximately exponential except for some special zones, but that of the hypereutectic melt is different. The paper discussed the correlation of the viscosity and atomic density, which is thought that the viscosity corresponds to the atomic density to some extent.

INFLUENCES OF TRACE ADDITIONS OF STRONTIUM AND PHOSPHORUS ON ELECTRICAL RESISTIVITY AND VISCOSITY OF LIQUID Al-Si ALLOYS

The electrical resistivity and viscosity of liquid hypoeutectic Al 7%Si and hypereutectic Al 18%Si alloys, and the influences of trace strontium and phosphorus on them were investigated. The trace additions of the two elements increase the electrical resistivity. At the precipitation temperatures of primary phase, the electrical resistivity exhibits a discontinuity for all experimental Al Si alloys. In the discontinuity the electrical resistivity, respectively, decreases and increases abruptly for Al 7%Si alloys and Al 18%Si alloys. Phosphorus and strontium both have some effects on the discontinuity temperature and the jump value of electrical resistivity of Al 18%Si alloys, but strontium hardly has effect on them in Al 7%Si alloys. The trace additions of strontium and phosphorus increase the viscosity of the experimental alloy.

Refining Effect of Boron on Hypoeutectic Al-Si Alloys

Several concepts of the grain refinement mechanism of B on hypoeutectic Al-Si alloys have been adopted: the refining effect of B on the a-AI and eutectic Si with the different additions of Al-B master alloys made at 850℃ was investigated; and the Al-B master alloys formed under different temperature conditions have been studied to explore the morphologies of AIB2 particles; slowly cooled sample with addition of Al-B was made to explore the refinement mechanism. AI-B master alloy can refine not only a-AI, but eutectic Si. Theoretical analysis indicates that, although AIB2 does not take part directly in the nucleation process in pure Al in the presence of Si, it provides a substrate for precipitation of a small content of Si from which a-At will grow without any undercooling. When the temperature decreases to eutectic line, AIB2 subsequently nucleates eutectic Si; AIB2 particles appear in two different morphologies, namely, hexagonal platelet and tetradehedron morphology which depend on the processing temperature conditions.

Effect of AlP master alloy on grain refinement of primary silicon in eutectic Al-Si alloys

To obtain the finer primary silicon crystals, the proprietary Al-P masteralloy was adopted to modify the eutectic Al-Si alloys and the most suitable modification process wasmade in the experiments. The SEM (Scanning Electron Microscope) and DSC (Differential ScanningCalorimeter) analysis indicate that the Al-P modifier has more advantages over Cu-P and Fe-Pmodifier in easily addition, no elemental alteration and less undercooling of primary silicon'ssolidification, which suggests the Al-P master alloy is an effective modifier of eutectic Al-Sialloys.

EFFECT OF Ti ON MICROSTRUCTURE OF RAPIDLY SOLIDIFIED Al-Si ALLOYS

An addition of Ti as alloying element to Al-Si binary alloy will reduce the undercooling-abili- ty on rapid solidification of the melt-spun ribbon.The microstructure will be encoarsened even at initiation of its solidification,so as to aggravate the eellular segregation of Si in the alloy ribbon.