Effect of Sputtered TiAlCr Coatings on Oxidation and Hot Corrosion Resistance of Ti-24Al-14Nb-3V 被引量:2
1
作者 Fuhui WANG, Chunhong GUAN, Zhaolin TANG and Weitao WU State Key Laboratory for Corrosion and Protection, Institute of Metal Research, The Chinese Academy of Sciences, Shenyang 110016, China 《Journal of Materials Science & Technology》 SCIE EI CAS CSCD 2001年第5期501-506,共6页
The effect of sputtered Ti-50Al-10Cr and Ti-50A1-20Cr coatings on both isothermal and cyclic oxidation resistance at 800-900℃ and hot corrosion resistance at 850℃ of Ti-24Al-14Nb-3V was investigated. Results indicat... The effect of sputtered Ti-50Al-10Cr and Ti-50A1-20Cr coatings on both isothermal and cyclic oxidation resistance at 800-900℃ and hot corrosion resistance at 850℃ of Ti-24Al-14Nb-3V was investigated. Results indicated that Ti-24Al-14Nb-3V alloys exhibited poor oxidation resistance due to the formation of Al2O3+TiO2+AlNbO4 mixed scales in air at 800-900℃ and poor hot corrosion resistance due to the spoliation of scales formed in Na2SO4+K2SO4 melts at 850℃. Both Ti-50Al-10Cr and Ti-50Al-20Cr coatings remarkably improved the oxidation and hot corrosion resistance of Ti-24Al-14Nb-3V alloy. 展开更多
关键词 Ti Cr Effect of Sputtered tialcr coatings on Oxidation and Hot Corrosion Resistance of Ti-24Al-14Nb-3V Al
下载PDF
上一页 1 下一页 到第
使用帮助 返回顶部