为解决普通喷射混凝土凝结时间长、早期强度低和抗渗性能差等问题,通过外掺纳米水化硅酸钙(calcium-silicate-hydrate,C-S-H)凝胶的方式对其进行性能提升。研究纳米C-S-H凝胶对喷射混凝土凝结时间、抗压强度及抗渗等性能的影响,并采用...为解决普通喷射混凝土凝结时间长、早期强度低和抗渗性能差等问题,通过外掺纳米水化硅酸钙(calcium-silicate-hydrate,C-S-H)凝胶的方式对其进行性能提升。研究纳米C-S-H凝胶对喷射混凝土凝结时间、抗压强度及抗渗等性能的影响,并采用水化热测试、X射线衍射(X-ray diffraction,XRD)和扫描电子显微镜(scanning electron microscope,SEM)等技术探究纳米C-S-H凝胶提升喷射混凝土性能的机理。结果表明:纳米C-S-H凝胶可明显缩短掺速凝剂水泥净浆的凝结时间,与基准组相比,掺2%纳米C-S-H凝胶的喷射混凝土1 d抗压强度可提高19.0%,渗水深度降低31.4%。机理分析表明,纳米C-S-H凝胶的晶核和填充效应能够促进水泥水化且可以致密混凝土内部结构,从而提升喷射混凝土的各项性能。展开更多
The characteristics of C-S-H gel in hardened Portland cement pastes and complex binder pastes with ground granulated blast furnace slag were investigated with nanoindentation. The composition of C-S-H gel was analysed...The characteristics of C-S-H gel in hardened Portland cement pastes and complex binder pastes with ground granulated blast furnace slag were investigated with nanoindentation. The composition of C-S-H gel was analysed with SEM-EDS. The obtained results showed that the volume fraction of LD C-S-H gradually reduced and the volume fraction of HD C-S-H increased with the prolongation of hydration age. Most of the C-S-H gel produced at later age was HD C-S-H. The volume fraction of HD C-S-H increased as the fraction of slag in complex binder pastes increased, suggesting that HD C-S-H was mainly in the hydration products of slag. The chemichal compositions of the two types of C-S-H gel were simlar, meaning that formation and transformation of the two types of C-S-H gel were not affected by their Ca/Si ratio.展开更多
文摘为解决普通喷射混凝土凝结时间长、早期强度低和抗渗性能差等问题,通过外掺纳米水化硅酸钙(calcium-silicate-hydrate,C-S-H)凝胶的方式对其进行性能提升。研究纳米C-S-H凝胶对喷射混凝土凝结时间、抗压强度及抗渗等性能的影响,并采用水化热测试、X射线衍射(X-ray diffraction,XRD)和扫描电子显微镜(scanning electron microscope,SEM)等技术探究纳米C-S-H凝胶提升喷射混凝土性能的机理。结果表明:纳米C-S-H凝胶可明显缩短掺速凝剂水泥净浆的凝结时间,与基准组相比,掺2%纳米C-S-H凝胶的喷射混凝土1 d抗压强度可提高19.0%,渗水深度降低31.4%。机理分析表明,纳米C-S-H凝胶的晶核和填充效应能够促进水泥水化且可以致密混凝土内部结构,从而提升喷射混凝土的各项性能。
基金supported by the National Basic Research Program of China ("973" Project) (Grant No. 2009CB623106)the National Natural Science Foundation of China (Grant No. U1134008)
文摘The characteristics of C-S-H gel in hardened Portland cement pastes and complex binder pastes with ground granulated blast furnace slag were investigated with nanoindentation. The composition of C-S-H gel was analysed with SEM-EDS. The obtained results showed that the volume fraction of LD C-S-H gradually reduced and the volume fraction of HD C-S-H increased with the prolongation of hydration age. Most of the C-S-H gel produced at later age was HD C-S-H. The volume fraction of HD C-S-H increased as the fraction of slag in complex binder pastes increased, suggesting that HD C-S-H was mainly in the hydration products of slag. The chemichal compositions of the two types of C-S-H gel were simlar, meaning that formation and transformation of the two types of C-S-H gel were not affected by their Ca/Si ratio.