Extractability of zinc from two types of electric arc furnace (EAF) dusts containing 24.8% and 16.8% of zinc respectively (denoted as Sample A and Sample B) were tested using direct alkaline leaching followed by fusio...Extractability of zinc from two types of electric arc furnace (EAF) dusts containing 24.8% and 16.8% of zinc respectively (denoted as Sample A and Sample B) were tested using direct alkaline leaching followed by fusion of the resulting leaching residues with caustic soda. The experimental results show that the extraction of zinc is heavily dependent on the contents of iron in the dusts. The higher iron content, the lower extraction of zinc is obtained. 53% and 38% of zinc can be extracted when both dusts were directly contacted with 5mol·L^-1 NaOH solution for 42h. The remaining zinc left in the leaching residues, which supposed to be present as zinc ferrites, can be further leached when the residues were fused with caustic soda. Quantitative extraction of zinc can be obtained from the leaching residue of Sample A while only 85% from Sample B. The extractability of zinc from dusts wit hvarious contents of iron is compared. The production flowsheet for zinc from the dusts using the process proposed is discussed.展开更多
Scheelite and scheelite-wolframite mixed concentrates with different grades were decomposed by caustic soda digestion, and the effects of caustic soda（NaOH） dosage, the ratio of water to ore and the stirring rate on...Scheelite and scheelite-wolframite mixed concentrates with different grades were decomposed by caustic soda digestion, and the effects of caustic soda（NaOH） dosage, the ratio of water to ore and the stirring rate on tungsten recovery were studied. The results show that under the conditions that the ratio of water to ore is （0.8,） stirring rate is 500 r·min-1 and the heating time is 2.0 h at （160 ℃,） the recovery of tungsten reaches 98% for scheelite （w（WO3） is （65.04%）） and wolframite containing high proportion of calcium （w（WO3） is 65.58%, w（Ca） is （7.53%）,） when caustic soda dosage is 2.2 and 2.0 times of theoretical value, respectively; the recovery of tungsten can be more than 98%,98% and 96% respectively for low-grade scheelite-wolframite mixed concentrate with （55.78%,） 45.32% and 25.21% WO3, when caustic soda dosage is 2.6,3.2 and 5.5 times of theoretical value, respectively.展开更多
文摘Extractability of zinc from two types of electric arc furnace (EAF) dusts containing 24.8% and 16.8% of zinc respectively (denoted as Sample A and Sample B) were tested using direct alkaline leaching followed by fusion of the resulting leaching residues with caustic soda. The experimental results show that the extraction of zinc is heavily dependent on the contents of iron in the dusts. The higher iron content, the lower extraction of zinc is obtained. 53% and 38% of zinc can be extracted when both dusts were directly contacted with 5mol·L^-1 NaOH solution for 42h. The remaining zinc left in the leaching residues, which supposed to be present as zinc ferrites, can be further leached when the residues were fused with caustic soda. Quantitative extraction of zinc can be obtained from the leaching residue of Sample A while only 85% from Sample B. The extractability of zinc from dusts wit hvarious contents of iron is compared. The production flowsheet for zinc from the dusts using the process proposed is discussed.
文摘Scheelite and scheelite-wolframite mixed concentrates with different grades were decomposed by caustic soda digestion, and the effects of caustic soda（NaOH） dosage, the ratio of water to ore and the stirring rate on tungsten recovery were studied. The results show that under the conditions that the ratio of water to ore is （0.8,） stirring rate is 500 r·min-1 and the heating time is 2.0 h at （160 ℃,） the recovery of tungsten reaches 98% for scheelite （w（WO3） is （65.04%）） and wolframite containing high proportion of calcium （w（WO3） is 65.58%, w（Ca） is （7.53%）,） when caustic soda dosage is 2.2 and 2.0 times of theoretical value, respectively; the recovery of tungsten can be more than 98%,98% and 96% respectively for low-grade scheelite-wolframite mixed concentrate with （55.78%,） 45.32% and 25.21% WO3, when caustic soda dosage is 2.6,3.2 and 5.5 times of theoretical value, respectively.