The resistance brazing of 2024Al reinforced with15 volume percent of Sic particulate was simulated by using a Gleeble - 1500 Tharmal/Mechanical sindator. The results show that too high or too low brazing temperature a...The resistance brazing of 2024Al reinforced with15 volume percent of Sic particulate was simulated by using a Gleeble - 1500 Tharmal/Mechanical sindator. The results show that too high or too low brazing temperature and pressure result in decrease in shear strength of joint,but brazing time influenc- es it slightly. The action between filler metals and the composite was analyzed by SEM and EPAM. The use of simulation method helped in the design and predication of welding technology,which re- duced the rejection rate as well as the cost of production.展开更多
SiC particulate reinforced 6066 aluminium alloy metal matrix composites (MMCs) were prepared by multi layer spray forming. The preparation technology and process parameters were discussed. It is shown that SiC particu...SiC particulate reinforced 6066 aluminium alloy metal matrix composites (MMCs) were prepared by multi layer spray forming. The preparation technology and process parameters were discussed. It is shown that SiC particulate can be continuously and evenly fed and co deposited in the spray forming process. The reciprocally scanning movement of spraying system can make the SiC particulates distribute homogeneously in the composite. The ratio of SiC particulates captured by the metal matrix is influenced by process parameters, especially the metal flow rate. 6066/SiC p composite preforms of d 300 mm×540 mm and tubes with a size of up to d 650/ d 300 mm×1 000 mm were made by the same process. After extrusion and T6 heat treatment, the multi layer spray deposited 6066/SiC p composites can achieve improved properties. [展开更多
文摘The resistance brazing of 2024Al reinforced with15 volume percent of Sic particulate was simulated by using a Gleeble - 1500 Tharmal/Mechanical sindator. The results show that too high or too low brazing temperature and pressure result in decrease in shear strength of joint,but brazing time influenc- es it slightly. The action between filler metals and the composite was analyzed by SEM and EPAM. The use of simulation method helped in the design and predication of welding technology,which re- duced the rejection rate as well as the cost of production.
文摘SiC particulate reinforced 6066 aluminium alloy metal matrix composites (MMCs) were prepared by multi layer spray forming. The preparation technology and process parameters were discussed. It is shown that SiC particulate can be continuously and evenly fed and co deposited in the spray forming process. The reciprocally scanning movement of spraying system can make the SiC particulates distribute homogeneously in the composite. The ratio of SiC particulates captured by the metal matrix is influenced by process parameters, especially the metal flow rate. 6066/SiC p composite preforms of d 300 mm×540 mm and tubes with a size of up to d 650/ d 300 mm×1 000 mm were made by the same process. After extrusion and T6 heat treatment, the multi layer spray deposited 6066/SiC p composites can achieve improved properties. [