Cr1-xAlxN coatings have been deposited on a Ti3Al based alloy by reactive sputtering method. The results of the isothermal oxidation test at 800-900℃ showed that Cr1-xAlxN coatings could remarkably reduce the oxidati...Cr1-xAlxN coatings have been deposited on a Ti3Al based alloy by reactive sputtering method. The results of the isothermal oxidation test at 800-900℃ showed that Cr1-xAlxN coatings could remarkably reduce the oxidation rate of the alloy owing to the formation of Al2O3＋Cr2O3 mixture oxide scale on the surface of the coatings. No spallation of the coatings or oxide scales took place during the cyclic oxidation at 800℃. Ti was observed to diffuse into the coatings, the diffusion distance of which was very short, and the diffusion ability of it was proportional to the AI content in the coatings. Compared to Ti, Nb can diffuse much more easily through the whole coatings and oxide scales.展开更多
To investigate the evolution of microstructure and wear behavior of TiSiN coatings with the variation of Si in targets and lays the foundation for its controllable mass production, Ti1-xSixN composite coatings were de...To investigate the evolution of microstructure and wear behavior of TiSiN coatings with the variation of Si in targets and lays the foundation for its controllable mass production, Ti1-xSixN composite coatings were deposited onto Si(100) and cemented carbide substrates using TiSi targets with different Si content by cathodic arc ion plating. The influences of Si on the microstructure and mechanical properties were studied. Nano-amorphous composite structure appeared in the Ti1-xSixN coatings when Si content in TiSi target was higher than 5 at%. However, further increase of Si content in TiSi target exhibited a negligible effect on the microstructure of Ti1-xSixN coatings. Hardness and deformation resistance were correlated to the content of Si in TiSi targets. Maximum hardness was obtained as the Si content in target increased up to 20 at%. Friction coefficient and wear rate significantly decreased with addition of Si in TiN coating, and then dually increased with the increase of Si content in targets.展开更多
基金the National Natural Science Foundation of China under grant Nos. 50371095 , 50571106.
文摘Cr1-xAlxN coatings have been deposited on a Ti3Al based alloy by reactive sputtering method. The results of the isothermal oxidation test at 800-900℃ showed that Cr1-xAlxN coatings could remarkably reduce the oxidation rate of the alloy owing to the formation of Al2O3＋Cr2O3 mixture oxide scale on the surface of the coatings. No spallation of the coatings or oxide scales took place during the cyclic oxidation at 800℃. Ti was observed to diffuse into the coatings, the diffusion distance of which was very short, and the diffusion ability of it was proportional to the AI content in the coatings. Compared to Ti, Nb can diffuse much more easily through the whole coatings and oxide scales.
基金Funded by the National Natural Science Foundation of China(U1832127)
文摘To investigate the evolution of microstructure and wear behavior of TiSiN coatings with the variation of Si in targets and lays the foundation for its controllable mass production, Ti1-xSixN composite coatings were deposited onto Si(100) and cemented carbide substrates using TiSi targets with different Si content by cathodic arc ion plating. The influences of Si on the microstructure and mechanical properties were studied. Nano-amorphous composite structure appeared in the Ti1-xSixN coatings when Si content in TiSi target was higher than 5 at%. However, further increase of Si content in TiSi target exhibited a negligible effect on the microstructure of Ti1-xSixN coatings. Hardness and deformation resistance were correlated to the content of Si in TiSi targets. Maximum hardness was obtained as the Si content in target increased up to 20 at%. Friction coefficient and wear rate significantly decreased with addition of Si in TiN coating, and then dually increased with the increase of Si content in targets.