The synthesis of zeolite HXDM-Theta-1(HXDM = hexanediamine) from the reaction mixture HXDM-Al2O3-SiO2-HF-H2O is described. The formation of HXDM-Theta-1 is favoured at 150℃, and a mixture of Theta-1 and ZSM-5 is obta...The synthesis of zeolite HXDM-Theta-1(HXDM = hexanediamine) from the reaction mixture HXDM-Al2O3-SiO2-HF-H2O is described. The formation of HXDM-Theta-1 is favoured at 150℃, and a mixture of Theta-1 and ZSM-5 is obtained at a higher temperature. The asynthesized Theta-1 was characterized by means of scanning electron micrography, thermal analysis and 13C MAS NMR techniques. Keywords Theta-1, Hydrothermal crystallization, Hexanediamine template, Thermal analysis, 13C MAS NMR展开更多
A series of Y zeolites exchanged with different amount of cerium and lanthanum cations were investigated. Comprehensive routine analysis tools including X-ray photoelectron spectroscopy（XPS）, X-ray fluorescence（XRF...A series of Y zeolites exchanged with different amount of cerium and lanthanum cations were investigated. Comprehensive routine analysis tools including X-ray photoelectron spectroscopy（XPS）, X-ray fluorescence（XRF）, X-ray diffraction（XRD） and Py-Fourier transform infrared spectroscopy（Py-FTIR） were used to identify the cation location, and the result was verified via XRD Rietveld study. The results revealed that almost all the RE cations in RE-4, most cations in RE-8 to RE-14 and part of cations in RE-16 were located in the sodalite cage. The Al^（IV）/（Al^V＋Al^（VI）） values revealed by ^（27）Al MAS NMR spectra, the silicon aluminum ratio of the framework（SARF） values deduced from ^（29）Si MAS NMR spectra and XRD, and hydroxyl amount were reasonably in accordance with the location and content of rare earth cations. The hydrothermal stability derived from in situ XRD investigation and catalyst activity provided by micro-activity test manifested that samples RE-8 to RE-14 exhibited better performances than RE-4 and RE-16, among which RE-12 had the best properties. The phenomena were interpreted by the cation location and structural properties.展开更多
文摘The synthesis of zeolite HXDM-Theta-1(HXDM = hexanediamine) from the reaction mixture HXDM-Al2O3-SiO2-HF-H2O is described. The formation of HXDM-Theta-1 is favoured at 150℃, and a mixture of Theta-1 and ZSM-5 is obtained at a higher temperature. The asynthesized Theta-1 was characterized by means of scanning electron micrography, thermal analysis and 13C MAS NMR techniques. Keywords Theta-1, Hydrothermal crystallization, Hexanediamine template, Thermal analysis, 13C MAS NMR
基金Project supported by the Foundation of SINOPEC(111015)
文摘A series of Y zeolites exchanged with different amount of cerium and lanthanum cations were investigated. Comprehensive routine analysis tools including X-ray photoelectron spectroscopy（XPS）, X-ray fluorescence（XRF）, X-ray diffraction（XRD） and Py-Fourier transform infrared spectroscopy（Py-FTIR） were used to identify the cation location, and the result was verified via XRD Rietveld study. The results revealed that almost all the RE cations in RE-4, most cations in RE-8 to RE-14 and part of cations in RE-16 were located in the sodalite cage. The Al^（IV）/（Al^V＋Al^（VI）） values revealed by ^（27）Al MAS NMR spectra, the silicon aluminum ratio of the framework（SARF） values deduced from ^（29）Si MAS NMR spectra and XRD, and hydroxyl amount were reasonably in accordance with the location and content of rare earth cations. The hydrothermal stability derived from in situ XRD investigation and catalyst activity provided by micro-activity test manifested that samples RE-8 to RE-14 exhibited better performances than RE-4 and RE-16, among which RE-12 had the best properties. The phenomena were interpreted by the cation location and structural properties.