The bi-functional carbazole-based photorefractive polyphosphazenes with different content of C_（60）-doped were fabricated. The glass transition temperature（T_g） of these polymer composite materials was determined ...The bi-functional carbazole-based photorefractive polyphosphazenes with different content of C_（60）-doped were fabricated. The glass transition temperature（T_g） of these polymer composite materials was determined using a differential scanning calorimetric（DSC） method. According to the DSC measurement results with different heating rates, the variation of T_g and the active energy of glass transition（E_g） were analyzed in detail. The analysis results indicate that the transition region shifts to higher temperatures with increasing heating rate, and C_（60） content（below 1.0 wt%） can influence the T_g of photorefractive polyphosphazenes. The T_g first increases and then decreases with the C_（60） content（below 1.0 wt%）. The probable causes of the influence of C_（60） on T_g was proposed.展开更多
基金the National Science Foundation of China(No.11174258)the Development Foundation of China Academy of Engineering Physics(No.2013A0302016)
文摘The bi-functional carbazole-based photorefractive polyphosphazenes with different content of C_（60）-doped were fabricated. The glass transition temperature（T_g） of these polymer composite materials was determined using a differential scanning calorimetric（DSC） method. According to the DSC measurement results with different heating rates, the variation of T_g and the active energy of glass transition（E_g） were analyzed in detail. The analysis results indicate that the transition region shifts to higher temperatures with increasing heating rate, and C_（60） content（below 1.0 wt%） can influence the T_g of photorefractive polyphosphazenes. The T_g first increases and then decreases with the C_（60） content（below 1.0 wt%）. The probable causes of the influence of C_（60） on T_g was proposed.