Durability design of recycled high performance concrete（RHPC） is fundamental for improving the use rate and level of concrete waste as coarse recycled aggregate（CRA）. We discussed a frostdurability-based mix propo...Durability design of recycled high performance concrete（RHPC） is fundamental for improving the use rate and level of concrete waste as coarse recycled aggregate（CRA）. We discussed a frostdurability-based mix proportion design method for RHPC using 100 % CRA and natural sand. Five groups of RHPC mixes with five strength grades（40, 50, 60, 70 and 80 MPa） were produced using CRA with four quality classes, and their workability, 28 d compressive strengths and frost resistances（measured by the compressive strength loss ratio and the relative dynamic modulus of elasticity） were tested. Relationships between the 28 d compressive strength, the frost resistance and the CRA quality characteristic parameter, water absorption, were then developed. The criterion of a CRA maximum water absorption limit value for RHPC was suggested, independent of its source and quality class. The results show that all RHPC mixes achieve the expected target workability, strength, and frost durability. The research results demonstrate that the application of the proposed method does not require trial testing prior to use.展开更多
Durability of traditional reactive powder concrete （RPC） with rich cement and high volume of fly-ash reactive powder concrete （FRPC） were studied. The X-diffraction and scanning electron microscope （SEM） measure...Durability of traditional reactive powder concrete （RPC） with rich cement and high volume of fly-ash reactive powder concrete （FRPC） were studied. The X-diffraction and scanning electron microscope （SEM） measurement was imployed to analyze the microstructure. The results show that both types of RPC have higher compressive strength, less volume shrinkage ratio and better carbonation-, chloride-, freezing-resistances than the conventional concrete. The results of X-diffraction indicate that they basically have C-S-H as the main composition without Ca（OH）2 crystal and ettringite. SEM results show that hydration products of FRPC is mainly Ⅲ-C-S-H which is piled up closely like densely arranged stone body and it has very compacted structure, in addition, Ca/Si ratio of C-S-H gel is lower than 1.5.展开更多
基金Funded by the National Natural Science Foundation of China(No.51278073)Prospective Joint Research Project of Jiangsu Province(No.BY2015027-23)State Key Laboratory for Geo Mechanics and Deep Underground Engineering,China University of Mining&Technology(No.SKLGDUEK1704)
文摘Durability design of recycled high performance concrete（RHPC） is fundamental for improving the use rate and level of concrete waste as coarse recycled aggregate（CRA）. We discussed a frostdurability-based mix proportion design method for RHPC using 100 % CRA and natural sand. Five groups of RHPC mixes with five strength grades（40, 50, 60, 70 and 80 MPa） were produced using CRA with four quality classes, and their workability, 28 d compressive strengths and frost resistances（measured by the compressive strength loss ratio and the relative dynamic modulus of elasticity） were tested. Relationships between the 28 d compressive strength, the frost resistance and the CRA quality characteristic parameter, water absorption, were then developed. The criterion of a CRA maximum water absorption limit value for RHPC was suggested, independent of its source and quality class. The results show that all RHPC mixes achieve the expected target workability, strength, and frost durability. The research results demonstrate that the application of the proposed method does not require trial testing prior to use.
文摘Durability of traditional reactive powder concrete （RPC） with rich cement and high volume of fly-ash reactive powder concrete （FRPC） were studied. The X-diffraction and scanning electron microscope （SEM） measurement was imployed to analyze the microstructure. The results show that both types of RPC have higher compressive strength, less volume shrinkage ratio and better carbonation-, chloride-, freezing-resistances than the conventional concrete. The results of X-diffraction indicate that they basically have C-S-H as the main composition without Ca（OH）2 crystal and ettringite. SEM results show that hydration products of FRPC is mainly Ⅲ-C-S-H which is piled up closely like densely arranged stone body and it has very compacted structure, in addition, Ca/Si ratio of C-S-H gel is lower than 1.5.