The molten slag in smelting reduction with iron bath has peculiar behaviour for its high FeO concentration. Slag foaming is effected by the concentration and reduction rate of FeO, basicity of slag and temperature. Ad...The molten slag in smelting reduction with iron bath has peculiar behaviour for its high FeO concentration. Slag foaming is effected by the concentration and reduction rate of FeO, basicity of slag and temperature. Addition of granulated coke can greatly decrease slag foaming extent in the process of smelting reduction with iron bath. The anti-foaming capacity of granulated coke is the best when the ratio of coke used for coke layer to total coke used in smelting reduction is controlled at about 20%.展开更多
Effects of FeO content （0, 5%, 10%, and 15% in mass, respectively ） in lab-synthesized smelting redttc- tion slag with iron bath and test temperature （1 450, 1 500, 1550, anti 1 600 ℃ ） on corrosion am,amount and...Effects of FeO content （0, 5%, 10%, and 15% in mass, respectively ） in lab-synthesized smelting redttc- tion slag with iron bath and test temperature （1 450, 1 500, 1550, anti 1 600 ℃ ） on corrosion am,amount and microstructure of fused rebonded magnesia - chrome brick with 26.02 massqc of Cr2O3 were researched by rotary cylinder method. The results show that ： （ 1 ） the corro- sion amolult of magnesia -chrome brick by slag without FeO is higher than that by the slag with 5% FeO, and the vorrosion amount increases when FeO content increa- ses from 5% to 15% ; （2） the test temperature is one of the important factors affecting the slag corrosion resist- ance of magnesia - chrome brick, and the corrosion of smelting reduction slag to brick increases with the temperature rising.展开更多
When cast iron is added with Al, the compound layer formed by reaction between cast iron and liquid Zn at 500～600℃ consists of nubby δ +Fe-Al phases instead of column δ+г phases, and the width of the compound lay...When cast iron is added with Al, the compound layer formed by reaction between cast iron and liquid Zn at 500～600℃ consists of nubby δ +Fe-Al phases instead of column δ+г phases, and the width of the compound layer increases obviously. The consumption of Fe in cast iron is dominated by the diffusive rate of Fe through the compound layer, therefore, the corrosive rate of cast iron is decreased remarkably. With increasing the content of Al in cast iron, the corrosive rate of the cast iron further decrease. For the cast iron containing 8.1 wt.% Al, its corrosive rate is ten times as low as that of general gray cast iron.展开更多
文摘The molten slag in smelting reduction with iron bath has peculiar behaviour for its high FeO concentration. Slag foaming is effected by the concentration and reduction rate of FeO, basicity of slag and temperature. Addition of granulated coke can greatly decrease slag foaming extent in the process of smelting reduction with iron bath. The anti-foaming capacity of granulated coke is the best when the ratio of coke used for coke layer to total coke used in smelting reduction is controlled at about 20%.
文摘Effects of FeO content （0, 5%, 10%, and 15% in mass, respectively ） in lab-synthesized smelting redttc- tion slag with iron bath and test temperature （1 450, 1 500, 1550, anti 1 600 ℃ ） on corrosion am,amount and microstructure of fused rebonded magnesia - chrome brick with 26.02 massqc of Cr2O3 were researched by rotary cylinder method. The results show that ： （ 1 ） the corro- sion amolult of magnesia -chrome brick by slag without FeO is higher than that by the slag with 5% FeO, and the vorrosion amount increases when FeO content increa- ses from 5% to 15% ; （2） the test temperature is one of the important factors affecting the slag corrosion resist- ance of magnesia - chrome brick, and the corrosion of smelting reduction slag to brick increases with the temperature rising.
文摘When cast iron is added with Al, the compound layer formed by reaction between cast iron and liquid Zn at 500～600℃ consists of nubby δ +Fe-Al phases instead of column δ+г phases, and the width of the compound layer increases obviously. The consumption of Fe in cast iron is dominated by the diffusive rate of Fe through the compound layer, therefore, the corrosive rate of cast iron is decreased remarkably. With increasing the content of Al in cast iron, the corrosive rate of the cast iron further decrease. For the cast iron containing 8.1 wt.% Al, its corrosive rate is ten times as low as that of general gray cast iron.
基金supported by the National Key R&D Program of China (No. 2019YFC1905703)Provincial Science and Technology Plan Projects in Guangdong Province, China (No. GDKJ2020002)。