The electrochemical behaviour of copper electrode in molten NaCl-KCl-LaCl_3 has been investigated.The La-Cu alloy is formed at first and then the metallic lanthanum is deposited when the La^(3+)is reduced on the coppe...The electrochemical behaviour of copper electrode in molten NaCl-KCl-LaCl_3 has been investigated.The La-Cu alloy is formed at first and then the metallic lanthanum is deposited when the La^(3+)is reduced on the copper electrode.The technological conditions of preparing La-Cu alloy by consumable cathode have been dis- cussed.The La-Cu alloy contained lanthanum over 90wt% was obtained.The composition of alloy was LaCu_2 and La.The current efficiency was 85% and the recovery of lanthanum was near 90%.展开更多
A novel type of thermal stabilizer-lanthanum tris (mono- i -octyl phthalate) (LTMP) was synthesized by double-decomposition reaction o f sodium mono- i -octyl phthalate with lanthanum chloride at 60 ℃. Sodium m ono- ...A novel type of thermal stabilizer-lanthanum tris (mono- i -octyl phthalate) (LTMP) was synthesized by double-decomposition reaction o f sodium mono- i -octyl phthalate with lanthanum chloride at 60 ℃. Sodium m ono- i -octyl phthalate was prepared by sodium hydrate and mono- i -octy l phthalate prepared by reaction of isooctyl alcohol and phthalic anhydride in th e presence of sulfuric acid catalyst at 110 ℃. The yield of lanthanum tris (mon o- i -octyl phthalate) is about 84.5%. Its thermal stabilities were measured by heat-ageing oven test when incorporated into PVC. The experimental results show that the heat stability time is about 40min at 190 ℃ when adding 3phr (pe r hundred resin) to PVC. The thermal stability of this product is better than th at of Ca-Zn complex and basic lead salt stabilizers, and equal to that of dibut yltin dilaurate.展开更多
热镀锌件铬酸盐转化膜耐蚀性优良,但环境污染严重;铈盐转化膜效果差,复合铈盐转化膜耐蚀好,成本高;镧盐转化膜无毒,耐蚀效果比铈盐好。采用以La(NO3)3为主盐的成膜溶液浸泡热镀锌层,获得了La盐转化膜。通过SEM,EDS和电化学测试方法对La...热镀锌件铬酸盐转化膜耐蚀性优良,但环境污染严重;铈盐转化膜效果差,复合铈盐转化膜耐蚀好,成本高;镧盐转化膜无毒,耐蚀效果比铈盐好。采用以La(NO3)3为主盐的成膜溶液浸泡热镀锌层,获得了La盐转化膜。通过SEM,EDS和电化学测试方法对La盐转化膜层的结构和耐蚀性能进行了研究。结果表明:转化膜随浸泡时间增加而增厚,膜的极化电阻和电化学阻抗也随之增大;膜层中存在均匀分布的微裂纹,且随膜增厚而扩宽;处理时间过长,膜的表层开裂脱落,极化电阻和电化学阻抗下降。浸泡30 m in所获La盐转化膜,极化电阻和EIS低频阻抗达20 kΩ.cm2以上,耐蚀性能远高于单一铈盐转化膜,极大地提高了热镀锌件的耐蚀性能。展开更多
文摘The electrochemical behaviour of copper electrode in molten NaCl-KCl-LaCl_3 has been investigated.The La-Cu alloy is formed at first and then the metallic lanthanum is deposited when the La^(3+)is reduced on the copper electrode.The technological conditions of preparing La-Cu alloy by consumable cathode have been dis- cussed.The La-Cu alloy contained lanthanum over 90wt% was obtained.The composition of alloy was LaCu_2 and La.The current efficiency was 85% and the recovery of lanthanum was near 90%.
文摘A novel type of thermal stabilizer-lanthanum tris (mono- i -octyl phthalate) (LTMP) was synthesized by double-decomposition reaction o f sodium mono- i -octyl phthalate with lanthanum chloride at 60 ℃. Sodium m ono- i -octyl phthalate was prepared by sodium hydrate and mono- i -octy l phthalate prepared by reaction of isooctyl alcohol and phthalic anhydride in th e presence of sulfuric acid catalyst at 110 ℃. The yield of lanthanum tris (mon o- i -octyl phthalate) is about 84.5%. Its thermal stabilities were measured by heat-ageing oven test when incorporated into PVC. The experimental results show that the heat stability time is about 40min at 190 ℃ when adding 3phr (pe r hundred resin) to PVC. The thermal stability of this product is better than th at of Ca-Zn complex and basic lead salt stabilizers, and equal to that of dibut yltin dilaurate.
基金supported by the National Key Research and Development Program of China(No.2019YFC1908405)Natural Science Foundation of Jiangxi Province,China(No.20202BAB214015)+3 种基金Training Plan for Academic and Technical Leaders of Major Disciplines in Jiangxi Province,China(No.20212BCJ23006)Program of Qingjiang Excellent Young Talents,Jiangxi University of Science and Technology,China,Guangdong Basic and Applied Basic Research Foundation,China(No.2021A1515012268)China Postdoctoral Science Foundation(No.2021M702504)Distinguished Professor Program of Jinggang Scholars in Institutions of Higher Learning,Jiangxi Province,China.
文摘热镀锌件铬酸盐转化膜耐蚀性优良,但环境污染严重;铈盐转化膜效果差,复合铈盐转化膜耐蚀好,成本高;镧盐转化膜无毒,耐蚀效果比铈盐好。采用以La(NO3)3为主盐的成膜溶液浸泡热镀锌层,获得了La盐转化膜。通过SEM,EDS和电化学测试方法对La盐转化膜层的结构和耐蚀性能进行了研究。结果表明:转化膜随浸泡时间增加而增厚,膜的极化电阻和电化学阻抗也随之增大;膜层中存在均匀分布的微裂纹,且随膜增厚而扩宽;处理时间过长,膜的表层开裂脱落,极化电阻和电化学阻抗下降。浸泡30 m in所获La盐转化膜,极化电阻和EIS低频阻抗达20 kΩ.cm2以上,耐蚀性能远高于单一铈盐转化膜,极大地提高了热镀锌件的耐蚀性能。