Forced convection rheoforming process for preparation of 7075 aluminum alloy semisolid slurry and its numerical simulation

A self-developed forced convection rheoforming （FCR） machine for the preparation of light alloy semisolid slurry was introduced. The microstructure characteristics of 7075 aluminium alloy semisolid slurry at different stirring speeds prepared by the FCR process were analyzed. The experimental results suggest that with the increase of the stirring speed, the mean grain size of the semisolid decreases and the shape factor as well as the number of primary grains increase. Meanwhile, the preparation process of semisolid slurry was numerically simulated. The flow characteristics of the melt in the device and the effect of the stirring speed on temperature field and solid fraction of the melt were investigated. The simulated results show that during the preparation process of semisolid slurry, there is a complex convection within the FCR device that obviously changes the temperature field distribution and solid fraction of the melt. When the convection intensity increases, the scope of the undercooling gradient of the melt is reduced and temperature distribution is improved.

Semi-solid processing of hypereutectic A390 alloys using novel rheoforming process

The feasibility of semi solid processing of hypereutectic A390 alloys using a novel rheoforming process was investigated. A combination of the swirl enthalpy equilibration device （SEED） process, isothermal holding using insulation and addition of solid alloy during swirling was introduced as a novel method to improve the processability of semi solid slurry. The effects of isothermal holding and the addition of solid alloy on the temperature gradient between the centre and the wall and on the formation of a（Al） particles were examined. In additional tests, phosphorus and strontium were added to the molten metal to refine the primary and eutectic silicon structure to facilitate semi solid processing. The results show that the combination of the SEED process with two additional processing steps can produce semi-solid A390 alloys that can be rheoprocessed. The microstructure reveals an adequate amount of non-dendritic a（Al） globules surrounded by liquid, which greatly improves the processability of semi-solid slurry.

Effects of rheoforming on microstructures and mechanical properties of 7075 wrought aluminum alloy

It is economically advantageous to cast wrought aluminum alloys directly into near-net-shape components.The objective of the present work is to take advantage of the rheoforming with 7075 alloy to improve the competitiveness of this emerging technology in the manufacture of wrought aluminum alloy.High quality semi-solid slurry was produced,in which primary α(Al) presents in diameter of 62 μm and shape factor of 0.78 and features no eutectics entrapped.Higher forming pressure results in small grain size,improved shape factor and higher density.Especially,rheoforming can effectively reduce the occurrence of hot tearing.The average yield strength and elongation of the rheoformed samples in the T6 condition are 483 MPa and 8%,respectively.

Simulation of temperature field and metal flow during continuous semisolid extending extrusion process of 6201 alloy tube

A continuous semisolid extending extrusion （CSEP） method was proposed. Temperature field and metal flow during continuous semisolid extending extrusion process of 6201 alloy tube were studied. During the process, the temperature in the roll-shoe cavity decreases gradually, and the isothermal lines of the alloy deviate from the shoe side to the work roll side in the roll–shoe gap. Metal flow velocity decreases gradually from the surface of the work roll to the surface of the shoe. In the extrusion mould, alloy temperature decreases gradually from the entrance to the exit and from the center to the sidewall of the mould. The extending cavity is radially filled with the alloy. The flow lines in the tube corresponding to the centers of the splitflow orifices and the welding gaps are dense, and the corresponding harness values are high; there are 8 transitional bands between them. In order to prepare 6201 alloy tubes with good surface quality, the pouring temperature from 750 ℃ to 780 ℃ was suggested.

Performance of Semi-solid Slurry Produced by Twin-screw Stirring Mixer and Rheo-diecasting Process of AZ91D Alloy

The microstructure of semi-solid slurry of AZ91D alloy, which was produced by twin-screw stirring mixer under the different parameters, was investigated.Rheoforming by cold chamber die casting process was performed thereafter. The results indicate that with decreasing of the barrel temperature of the mixer and the pouring temperature of molten Mg alloy, the solid fraction of semi-solid slurry increases and the size of non-dendritic grains becomes smaller. While the shear rate increases, the solid fraction of semi-solid slurry decreases. The tensile strength and elongation of metal rheoformed by die casting are higher by about 37% and 44% respectively than those produced by conventional liquid die casting.