Effect of Rare Earths on the Wear Resistance and High Temperature Oxidation Resistance of H13 Steel Surface-Treated with S-N-C Co-diffusion

Steel H13 was put in non toxic salt bath with addition of CeO 2 for co diffusion of sulfur, nitrogen and carbon and followed by oxidation treatment. The effect of rare earths on the improvement of wear resistance and high temperature oxidation resistance of steel H13 was studied using scanning electron microscope, energy dispersive spectrometry and X ray diffraction. The results show that compared to the surface treatment without rare earth addition, the treatment with addition of rare earths improves the wear resistance and high temperature resistance to oxidation of steel H13. Under the conditions of 30 N and 2 h, the wear weight loss was decreased by 40%, and the friction coefficient was reduced from 0 25 to 0 22; whereas for 150 N and 0 2 h, the wear weight loss was decreased by 24%, and the friction coefficient was reduced from 0 35 to 0 32. For the oxidation at 700 ℃ and 4 h, the rate of weight gain decreased to only about 1/30 of that without rare earths.

RESEARCH AND APPLICATION OF AS-CAST WEAR RESISTANCE HIGH CHROMIUM CAST IRON

The influence of alloy elements, such as boron and silicon, on the microstructure and properties of as cast high chromium cast iron is studied. The results show that boron and silicon have a great effect on the mechanical properties and the wear resistance. Through proper addition of boron and silicon, the properties of as cast high chromium cast iron can be improved effectively. Through analyzing the distribution of elements by scanning electron microscope, it has been shown that the addition of boron and silicon lowers the mass fraction of chromium saturated in as cast austenite, and makes it unstable and liable to be transformed into martensite. The as cast high chromium cast iron with proper content of boron and silicon is suitable for the manufacture of lining for asphalt concrete mixer and its wear resistance is 14 times that of lining made of low alloy white cast iron.

Microstructure and Wear/corrosion Resistance of Stainless Steel Laser-alloyed with Mn+W_(2)C, Mn+NiWC and Mn+SiC

In-situ formed high Mn steel coating reinforced by carbides was formed by laser surface alloying(LSA).Laser alloyed layers on 1Cr18Ni9Ti steel with Mn+W_(2)C(specimen A),Mn+NiWC(specimen B)and Mn+SiC(specimen C)powders were fabricated to improve the wear and corrosion behavior of 1Cr18Ni9Ti steel blades in high speed mixers.Microstructure evolution,phases,element distribution,microhardness,wear and corrosion behavior of the laser alloyed layers were investigated.Results indicated that high Mn steel matrix composites with undissolved W_(2)C,WC and other in-situ formed carbides were formed by LSA with Mn+W_(2)C and Mn+NiWC while SiC totally dissolved into the high Mn matrix when adding Mn+SiC.Ni as the binding phase in Ni-WC powder decreased the crack sensitivity of the alloyed layer as compared with the addition of W_(2)C powder.An improvement in average microhardness was achieved in the matrix in specimen A,B and C,with the value of 615,602 and 277 HV_(0.5),while that of the substrate was 212 HV_(0.5).The increase of microhardness,wear and corrosion resistance is highly corelated to microstructure,formed phases,type and content of carbides,micro-hardness and toughness of the alloyed layers.

Greatly enhanced corrosion/wear resistances of epoxy coating for Mg alloy through a synergistic effect between functionalized graphene and insulated blocking layer

The poor corrosion and wear resistances of Mg alloys seriously limit their potential applications in various industries.The conventional epoxy coating easily forms many intrinsic defects during the solidification process,which cannot provide sufficient protection.In the current study,we design a double-layer epoxy composite coating on Mg alloy with enhanced anti-corrosion/wear properties,via the spin-assisted assembly technique.The outer layer is functionalized graphene(FG)in waterborne epoxy resin(WEP)and the inner layer is Ce-based conversion(Ce)film.The FG sheets can be homogeneously dispersed within the epoxy matrix to fill the intrinsic defects and improve the barrier capability.The Ce film connects the outer layer with the substrate,showing the transition effect.The corrosion rate of Ce/WEP/FG composite coating is 2131 times lower than that of bare Mg alloy,and the wear rate is decreased by~90%.The improved corrosion resistance is attributed to the labyrinth effect(hindering the penetration of corrosive medium)and the obstruction of galvanic coupling behavior.The synergistic effect derived from the FG sheet and blocking layer exhibits great potential in realizing the improvement of multi-functional integration,which will open up a new avenue for the development of novel composite protection coatings of Mg alloys.

Enhanced wear resistance,antibacterial performance,and biocompatibility using nanotubes containing nano-Ag and bioceramics in vitro

A good Ti-based joint implant should prevent stress shielding and achieve good bioactivity and anti-infection performance.To meet these requirements,the low-elastic-modulus alloy—Ti–35Nb–2Ta–3Zr—was used as the substrate,and functional coatings that contained bioceramics and Ag ions were prepared for coating on TiO_(2)nanotubes(diameter:(80±20)nm and(150±40)nm)using anodization,deposition,and spin-coating methods.The effects of the bioceramics(nano-β-tricalcium phosphate,microhydroxyapatite(micro-HA),and meso-CaSiO_(3))and Ag nanoparticles(size:(50±20)nm)on the antibacterial activity and the tribocorrosion,corrosion,and early in vitro osteogenic behaviors of the nanotubes were investigated.The tribocorrosion and corrosion results showed that the wear rate and corrosive rate were highly dependent on the features of the nanotube surface.Micro-HA showed great wear resistance with a wear rate of(1.26±0.06)×10^(−3)mm^(3)/(N·m)due to adhesive and abrasivewear.Meso-CaSiO_(3)showed enhanced cell adhesion,proliferation,and alkaline phosphatase activity.The coatings that contained nano-Ag exhibited good antibacterial activity with an antibacterial rate of≥89.5%against Escherichia coli.These findings indicate that hybrid coatings may have the potential to accelerate osteogenesis.

Reactive HVOF sprayed TiN-matrix composite coating and its corrosion and wear resistance properties

TiN-matrix composite coating was prepared on 45# steel by reactive high-velocity oxy-fuel （HVOF） spraying. Its microstructure, phase composition, micro-hardness, corrosion resistance in 3.5% NaC1 solution and wear resistance were analyzed. The results suggest that the TiN-matrix composite coating is well bonded with the substrate. The micro-hardness measured decreases with the increase of applied test loads. And the micro-hardness of the coating under heavy loads is relatively high. The TiN-matrix composite coating exhibits an excellent corrosion resistance in 3.5% NaC1 solution. The corrosion potential of coating is positive and the passivation zone is broad, which indicates that the TiN-matrix composite coating is stable in the electrolyte and provides excellent protection to the substrate. The wear coefficient of the coating under all loads maintains at 0.49-0.50. The wear mechanism of the coating is revealed to be three-body abrasive wear. Yet the failure forms of TiN-matrix composite coating under different loads have an obvious difference. The failure form of coating under light loads is particle spallation due to the stress concentration while that of coating under heavy loads is crackin~ between inter-lamellae.

Microstructure,mechanical properties and dry wear resistance of β-type Ti-15Mo-xNb alloys for biomedical applications

In order to study the effect of element Nb on the microstructure and properties of the biomedical β-type Ti-Mo based alloys,Ti-15Mo-xNb（x=5,10,15 and 20 in %） alloys were investigated.The dry wear resistance of β-type Ti-15Mo-xNb alloys against Gr15 ball was investigated on CJS111A ball-disk wear instrument.Experimental results indicate that crystal structure and morphology of the Ti-15Mo-xNb alloys are sensitive to their Nb contents.Ti-15Mo-xNb alloys match those for β phase peaks and no any phases are found.The Vickers hardness values of all the Ti-15Mo-xNb alloys are higher than HV200.The compression yield strength of the Ti-15Mo-5Nb alloy is the lowest and that of the Ti-15Mo-10Nb alloy is the highest.For all the Ti-15Mo-xNb alloys,the friction coefficient is not constant but takes a higher value.In dry condition,SEM study reveals deep parallel scars on the wear surfaces of all the Ti-15Mo-xNb alloys under different loads.The friction coefficient of the Ti-15Mo-5Nb alloy under 1 N is the lowest.The wear principal mechanism for Ti-15Mo-xNb alloys is adhesive wear.

Effects of slurry pack cementation temperature on microstructure and wear resistance of Ti-Al co-deposited coating on copper plated nickel layer

In order to improve the wear resistance properties of copper substrate, a layer of electroplated nickel was firstly deposited on copper substrate, subsequently these electroplated specimens were treated by slurry pack cementation process with a slurry pack cementation mixture composed of TiO2 as titanizing source, pure Al powder as aluminzing source and also a reducer for titanizing, an activator of NH4Cl and albumen （egg white） as cohesive agent. The Ti-Al coating was fabricated on the surface of electro-deposited nickel layer on copper matrix followed by the slurry pack cementation process. The effects of slurry pack cementation temperature on the microstructures and wear resistance of Ti-Al coating were studied. The results show that the microstructure of the coating changed from NiAl＋Ni3（Ti,Al） to NiAl ＋Ni3（Ti,Al）＋Ni4Ti3 to Ni4Ti3＋NiAl, and to NiAl＋Ni3（Ti,Al）＋NiTi with slurry pack cementation temperature ranging from 800 ℃ to 950 ℃ in 12 h. The friction coefficient of Ti-Al coating decreased and the hardness increased with increasing the slurry pack cementation temperature. The minimum friction coefficient was 1/3 and the minimum hardness was 5 times larger than that of pure copper.

HARDNESS PROPERTY AND WEAR RESISTANCE OF Al_2O_(3P)/ Zn-Al COMPOSITE

The hardness values and the wear resistance of Al2O3P/ Zn-Al composite, prepared by means of rheological casting technology,are investigated separately in this work. The results show that the addition of Al2O3P increases the hardness values of the matrix at both room and high temperature and improves the wear resistance of the material.The hardness values and the wear resistance of the composite rise with the increase of the particle volume fraction or the decrease of the particle size.The raising of test temperature results in a rapid descending of its hardness values.However, the addition of Al2O3P improves the property of high temperature resistance of Zn-Al alloys significantly.Moreover,the effect of quenching, tempering or cycling heat treatment on the hardness values of the composite is also studied.

Mechanical properties and wear resistance of aluminum composite welded by electron beam

The welding property of TiB2/ZL101 composite was investigated using electron beam（EB） welding experimental system with a function generator.The fine defect-free welding seam was obtained under proper processing parameters and scanning rate.The reinforcement particles TiB2 distributed homogeneously in welding seam without any segregation.The tensile results show that fracture occurs at the base metal and elastic modulus increases compared with base metal.Wear resistance of welding seam is improved greatly compared with base metal.The results show that the TiB2/ZL101 composite can be successfully welded by EB technology.

CATHODIC PROCESS AND WEAR RESISTANCE OF ELECTRO-DEPOSITED RE-Ni-W-P-SiC COMPOSITE COATING

Cathodic deposition current density of the composite coatings increases when SiC par-ticles and rare earth (RE) were added in the bath, which is profitable for Ni- W-P alloy to deposit in the cathod, forming Ni-W-P-SiC and RE-Ni-W-P-SiC composite coatings. On the contrary, the addition of PTFE in the bath decreases cathodic deposition current density of the coatings. The current density increases a little when the amount of RE is 7-9g/l; however, the current density increases greatly when the amount of RE is increased to 11-13g/l. Bui ij the amount of RE is raised further, the current density decreases. Hardness and wear resistance of RE-Ni-W-P-SiC composite coating have been studied, and the results show that the hardness and wear resistance of RE-Ni-W-P-SiC composite coating increase with increasing heat treatment tempera-ture, which reach peak values at 400℃; while the hardness and wear resistance of the coating decrease with the rise of heat treated temperature continuously.

Effects of process parameters on microstructure and wear resistance of TiN coatings deposited on TC11 titanium alloy by electrospark deposition

In the present study,the effects of process parameters(output voltage x,nitrogen flux l and specific strengthening time s)on the microstructure and wear resistance properties of TiN coatings prepared by electrospark deposition(ESD)were investigatedsystematically.The microstructure of the coatings was characterized for thickness(TOC),content of TiN(CON)and porosity(POC).A statistical model was developed to identify the significant factors affecting the microstructure and wear resistance of the coatings.The results show that the output voltage x and nitrogen flux l present significant effects on majority of the evaluation indexes such asTOC,friction coefficient(COF)and wear mass loss(Id),while the specific strengthening time s has a significant effect on POC and asmall effect on the other indexes.The optimal process parameters were obtained as follows:output voltage(x,60V),nitrogen flux(l,15L/min)and specific strengthening time(s,3min/cm2).The variation of wear mass loss(Id)by the variation of the outputvoltage(x)and nitrogen flux(l)is attributed to the change of wear mechanisms of TiN coatings.The main wear mechanism of TiNcoating prepared under optimal process parameters is micro-cutting wear accompanied by micro-fracture wear.

Effects of additives on corrosion and wear resistance of micro-arc oxidation coatings on TiAl alloy

Ceramic coating was deposited on TiAl alloy substrate by micro-arc oxidation(MAO)in a silicate-aluminate electrolyte solution with additives including sodium citrate,graphite and sodium tungstate.The microstructures and compositions were analyzed by SEM,EDX and XRD.The corrosion and wear properties of the coatings were investigated by potentiodynamic polarization and ball-on-disc wear test,respectively.The results show that the MAO coatings consist of WO3,Ti2O3,graphite and Al2O3 besides Al2TiO5 and Al2SiO5.With additives in the electrolyte,the working voltage at the micro-arc discharge stage decreases,and the ceramic coating gets smoother and more compact.The corrosion current density of MAO coating is much lower than that of TiAl substrate.It can be reduced from 9.81×10-8A/cm 2to 3.02×10-10A/cm 2 .The MAO coatings composed of hard Al2O3,WO3 and Ti2O3 obviously improve the wear resistance of TiAl alloy.The wear rate is-3.27×10-7g/(N·m).

Effects of reinforcement on wear resistance of aluminum matrix composites

The effect of reinforcement on the wear mechanism of metal matrix composites （MMCs） was investigated by considering different parameters, such as sliding distance （6 km）, pressure （0.14-1.1 MPa） and sliding speed （230-1480 r/min）. The wear mechanisms of an MMC and the corresponding matrix material under similar experimental conditions were compared on a pin-on-disc wear machine. The pins were made of 6061 aluminum matrix alloy and 6061 aluminum matrix composite reinforced with 10% Al2O3 （volume fraciton） particles （6-18μm）. The disc was made of steel. The major findings are as follows： the MMC shows much higher wear resistance than the corresponding matrix material; unlike that of matrix material, the wear of MMC is very much linear and possible to predict easily; the wear mechanism is similar for both materials other than the three-body abrasion in the case of MMC; the reinforced particles resist the abrasion and restrict the deformation of MMCs which causes high resistance to wear. These results reveal the roles of the reinforcement particles on the wear resistance of MMCs and provide a useful guide for a better control of their wear.

Structure and wear resistance of TiN and TiAlN coatings on AZ91 alloy deposited by multi-arc ion plating

In order to investigate the microstructure of TiN and TiAlN coatings and their effect on the wear resistance of Mg alloy, TiN and TiAlN coatings were deposited on AZ91 magnesium alloy by multi-arc ion plating technology.TiN and Ti70Al30N coatings were prepared on the substrate,respectively,which exhibited dark golden color and compact microstructure.The microstructures of TiN and Ti70Al30N coatings were investigated by X-ray diffractometry(XRD)and scanning electron microscopy(SEM).The micro-hardness and wear resistance of TiN and Ti70Al30N coatings were investigated in comparison with the uncoated AZ91 alloy. The XRD peaks assigned to TiN and TiAlN phases are found.The hardness of TiN coatings is two times as high as that of AZ91 alloy, and Ti70Al30N coating exhibits the highest hardness.The wear resistance of the hard coatings increases obviously as result of their high hardness.

Heat Treatment Effect on Microstructure, Hardness and Wear Resistance of Cr26 White Cast Iron

High chromium cast iron（HCCI） is taken as material of coal water slurry pump impeller, but it is susceptible to produce serious abrasive wear and erosion wear because of souring of hard coal particles. The research on optimization of heat treatments to improve abrasive wear properties of HCCI is insufficient, so effect of heat treatments on the microstructure, hardness, toughness, and wear resistance of Cr26 HCCI is investigated to determine the optimal heat treatment process for HCCI. A series of heat treatments are employed. The microstructures of HCCI specimens are examined by using optical microscopy and scanning electron microscopy. The hardness and impact fracture toughness of as-cast and heat treated specimens are measured. The wear tests are assessed by a Type M200 ring-on block wear tester. The results show the following： With increase of the quenching temperature from 950 ℃ to 1050 ℃, the hardness of Cr26 HCCI increased to a certain value, kept for a time and then decreased. The optimal heat treatment process is 2 h quenching treatment at 1000 ℃, followed by a subsequent 2 h tempering at 400 ℃. The hardness of HCCI is related to the precipitation and redissolution of secondary carbides in the process of heat treatment. The subsequent tempering treatment would result in a slight decrease of hardness but increase of toughness. The wear resistance is much related to the ＂supporting＂ effect of the matrix and the ＂protective＂ effect of the hard carbide embedded in the matrix, and the wear resistance is further dependent on the hardness and the toughness of the matrix. This research can provide an important insight on developing an optimized heat treatment method to improve the wear resistance of HCCI.

Effects of nano-Al_2O_3 and nano-ZrO_2 on the microstructure, behavior and abrasive wear resistance of WC-8Co cemented carbide

WC-8wt.% Co cemented carbides with varied nano-Al 2 O 3 and nano-ZrO 2 contents were prepared respectively following conventional powder metallurgical procedures. Effects of nano-Al 2 O 3 and nano-ZrO 2 on the microstructure, behavior, and abrasive wear resistance were investigated. The result shows that a finer and more homogenous microstructure can be achieved by increasing nano-Al 2 O 3 , and increasing nano-ZrO 2 makes the microstructure more refined. Nano-Al 2 O 3 and nano-ZrO 2 could both help to give increased hardness. Transverse rupture strength is higher if the above nano-oxides are doped appropriately, whereas excess addition is deleterious. Abrasive wear resistance presents different variations with respect to increasing nano-Al 2 O 3 and nano-ZrO 2 . By contrast, increasing nano-ZrO 2 enhances the abrasive wear resistance more effectively than increasing nano-Al 2 O 3 . The influence of the two nano-oxides contents on the abrasive wear resistance does not almost vary with wear time, and the optimum addition level of nano-Al 2 O 3 in WC-8% Co cemented carbide is 0.3 wt.% from the stand of abrasive wear resistance. In addition, both of the nano-oxides can retard the increase of wear rate in long-term abrasive wear.

Improvement of wear and corrosion resistance of AZ91 magnesium alloy by applying Ni-SiC nanocomposite coating via pulse electrodeposition

To improve the surface properties of AZ91 magnesium alloy, Ni-SiC nanocomposite coatings with various SiC contents were pulse electrodeposited in modified Watts baths containing SiC nano-particles with the concentration of 0-15 g/L. The morphology of the coatings was studied by scanning electron microscope （SEM）. The SiC content of the coatings was measured by energy dispersive spectroscopy （EDS） analyzer. Microhardness measurement of the coatings showed up to 600% enhancement for the sample produced from the bath with 15 g/L SiC. The corrosion behavior of the coated AZ91 alloy was investigated by potentiodynamic polarization method. The results reveal a significant improvement in the corrosion resistance, that is, the corrosion current density decreases from 0.13 mA/cm2 for uncoated specimen to 1.74x10-6 mA/cm2 for the sample coated from the bath containing 15 g/L SiC and the corrosion potential increases from -1.6 V for uncoated specimen to -0.31 V for the sample coated from the bath. The wear resistance of both coated and uncoated samples was evaluated by pin-on-disc tribotester. The results show that the wear volume loss of coated sample is 8 times less than the bare alloy.

Wear and corrosion resistance of laser-cladded Fe-based composite coatings on AISI 4130 steel

The wear and corrosion resistance of Fe_（72.2）Cr_（16.8）Ni_（7.3）Mo_（1.6）Mn_（0.7）C_（0.2）Si_（1.2） and Fe_（77.3）Cr_（15.8）Ni_（3.9）Mo_（1.1）Mn_（0.5）C_（0.2）Si_（1.2） coatings laser-cladded on AISI 4130 steel were studied.The coatings possess excellent wear and corrosion resistance despite the absence of expensive yttrium,tungsten,and cobalt and very little molybdenum.The microstructure mainly consists of dendrites and eutectic phases,such as duplex（γ＋α）-Fe and the Fe–Cr（Ni）solid solution,confirmed via energy dispersive spectrometry and X-ray diffraction.The cladded Fe-based coatings have lower coefficients of friction,and narrower and shallower wear tracks than the substrate without the cladding,and the main wear mechanism is mild abrasive wear.Electrochemical test results suggest that the soft Fe_（72.2）Cr_（16.8）Ni_（7.3）Mo_（1.6）Mn_（0.7）C_（0.2）Si_（1.2） coating with high Cr and Ni concentrations has high passivation resistance,low corrosion current,and positive corrosion potential,providing a better protective barrier layer to the AISI 4130 steel against corrosion.

Effect of scanning speed during PTA remelting treatment on the microstructure and wear resistance of nodular cast iron

The surface of nodular cast iron （NCI） with a ferrite substrate was rapidly remelted and solidified by plasma transferred arc （PTA） to induce a chilled structure with high hardness and favorable wear resistance. The effect of scanning speed on the microstructure, micro-hardness distribution, and wear properties of PTA-remelted specimens was systematically investigated. Microstructural characterization in-dicated that the PTA remelting treatment could dissolve most graphite nodules and that the crystallized primary austenite dendrites were transformed into cementite, martensite, an interdendritic network of ledeburite eutectic, and certain residual austenite during rapid solidifica-tion. The dimensions of the remelted zone and its dendrites increase with decreased scanning speed. The microhardness of the remelted zone varied in the range of 650 HV0.2 to 820 HV0.2, which is approximately 2.3-3.1 times higher than the hardness of the substrate. The wear re-sistance of NCI was also significantly improved after the PTA remelting treatment.