Orthorhombic Nb_(2)O_(5)(T-Nb_(2)O_(5))is attractive for fast-charging Li-ion batteries,but it is still hard to realize rapid charge transfer kinetics for Li-ion storage.Herein,F-doped T-Nb_(2)O_(5) microflowers(F-Nb_(...Orthorhombic Nb_(2)O_(5)(T-Nb_(2)O_(5))is attractive for fast-charging Li-ion batteries,but it is still hard to realize rapid charge transfer kinetics for Li-ion storage.Herein,F-doped T-Nb_(2)O_(5) microflowers(F-Nb_(2)O_(5))are rationally synthesized through topotactic conversion.Specifically,F-Nb_(2)O_(5) are assembled by single-crystal nanoflakes with nearly 97%exposed(100)facet,which maximizes the exposure of the feasible Li^(+)transport pathways along loosely packed 4g atomic layers to the electrolytes,thus effectively enhancing the Li^(+)-intercalation performance.Besides,the band gap of F-Nb_(2)O_(5) is reduced to 2.87 eV due to the doping of F atoms,leading to enhanced electrical conductivity.The synergetic effects between tailored exposed crystal facets,F-doping,and ultrathin building blocks,speed up the Li^(+)/electron transfer kinetics and improve the pseudocapacitive properties of F-Nb_(2)O_(5).Therefore,F-Nb_(2)O_(5) exhibit superior rate capability(210.8 and 164.9 mAh g^(-1) at 1 and 10 C,respectively)and good long-term 10 C cycling performance(132.7 mAh g^(-1) after 1500 cycles).展开更多
基金supported by the National Natural Science Foundation of China(No.51802163)the Natural Science Foundation of Henan Province of China(No.222300420252)the Natural Science Foundation of Henan Department of Education(No.20A480004).
文摘Orthorhombic Nb_(2)O_(5)(T-Nb_(2)O_(5))is attractive for fast-charging Li-ion batteries,but it is still hard to realize rapid charge transfer kinetics for Li-ion storage.Herein,F-doped T-Nb_(2)O_(5) microflowers(F-Nb_(2)O_(5))are rationally synthesized through topotactic conversion.Specifically,F-Nb_(2)O_(5) are assembled by single-crystal nanoflakes with nearly 97%exposed(100)facet,which maximizes the exposure of the feasible Li^(+)transport pathways along loosely packed 4g atomic layers to the electrolytes,thus effectively enhancing the Li^(+)-intercalation performance.Besides,the band gap of F-Nb_(2)O_(5) is reduced to 2.87 eV due to the doping of F atoms,leading to enhanced electrical conductivity.The synergetic effects between tailored exposed crystal facets,F-doping,and ultrathin building blocks,speed up the Li^(+)/electron transfer kinetics and improve the pseudocapacitive properties of F-Nb_(2)O_(5).Therefore,F-Nb_(2)O_(5) exhibit superior rate capability(210.8 and 164.9 mAh g^(-1) at 1 and 10 C,respectively)and good long-term 10 C cycling performance(132.7 mAh g^(-1) after 1500 cycles).