The hot deformation behavior of Ti-22Al-25Nb alloy fabricated by hot compressed sintering was investigated under various conditions of compression tests in the deformation temperature range of 975-1075 °C with 20...The hot deformation behavior of Ti-22Al-25Nb alloy fabricated by hot compressed sintering was investigated under various conditions of compression tests in the deformation temperature range of 975-1075 °C with 20 °C intervals and the strain rate range of 0.001-1.0 s^-1. Based on the experimental data, a novel constitutive relation combining a series of models was developed, including Zener-Hollomon parameter (Z), DRX critical model and kinetics model. The results show that the hot-deformed activation energy Q is calculated to be 410.172 kJ/mol, the ratio of critical strain (εc) to peak strain (εp) is a constant value of about 0.67. The predicted stress obtained by the established constitutive equations matches well with the true stress from experimental data. Despite large errors occur at the stage where strain rate is 0.1 s^-1 and the values of true strain are less than 0.1, the stage of large strain should be more concerned during plastic forming. Furthermore, the predicting accuracy with the DRX kinetics model was testified by an electron back-scattered diffraction (EBSD) technique.展开更多
TX-80 low-transformation-temperature(LTT)welding wire was used to replace the traditional ER 307Si welding wire to realize the connection of 22SiMn2TiB armor steel in manual overlay welding.The previously existing iss...TX-80 low-transformation-temperature(LTT)welding wire was used to replace the traditional ER 307Si welding wire to realize the connection of 22SiMn2TiB armor steel in manual overlay welding.The previously existing issues,such as welding cracks,large welding deformation,and severe welding residual stress,were solved to ensure good strength and ductility requirements.In particular,with the same welding conditions,TX-80 LTT wire eliminates welding cracks.It reduces the welding deformation no matter the base pretreatment of pre-setting angle or no pre-setting angle.By comparison,it was found that the microstructure at the TX-80 weld is mainly composed of martensite and a small amount of retained austenite.In contrast,the microstructure of the ER 307Si weld consists of a large amount of austenite and a small amount of skeleton-like ferrite.The variation trend of residual stress and microhardness from the weld to the base were investigated and compared with the mechanical properties of base materials.The TX-80 and the ER 307Si tensile samples elongation is 6.76%and 6.01%,while the ultimate tensile strengths are 877 and 667 MPa,respectively.The average impact toughness at room temperature of the ER 307Si weld is 143.9 J/cm^(2),much higher than that of the TX-80 weld,which is only 36.7 J/cm^(2).The relationship between impact and tensile properties with microstructure species and distribution was established.In addition,the fracture surface of the tensile and the impact samples was observed and analyzed.Deeper dimples,fewer pores,larger radiation zone,and shear lips of TX-80 samples indicate better tensile ductility and worse impact toughness than those of ER 307Si weld.展开更多
基金Project(51405110) supported by the National Natural Science Foundation of ChinaProject(2014M551234) supported by the China Postdoctoral Science Foundation+2 种基金Project(20132302120002) supported by the Specialized Research Fund for the Doctoral Program of Higher Education,ChinaProject(HIT.NSRIF.2014006) supported by the Fundamental Research Funds for the Central Universities,ChinaProject(LBH-Z14096) supported by the Heilongjiang Province Postdoctoral Fund,China
文摘The hot deformation behavior of Ti-22Al-25Nb alloy fabricated by hot compressed sintering was investigated under various conditions of compression tests in the deformation temperature range of 975-1075 °C with 20 °C intervals and the strain rate range of 0.001-1.0 s^-1. Based on the experimental data, a novel constitutive relation combining a series of models was developed, including Zener-Hollomon parameter (Z), DRX critical model and kinetics model. The results show that the hot-deformed activation energy Q is calculated to be 410.172 kJ/mol, the ratio of critical strain (εc) to peak strain (εp) is a constant value of about 0.67. The predicted stress obtained by the established constitutive equations matches well with the true stress from experimental data. Despite large errors occur at the stage where strain rate is 0.1 s^-1 and the values of true strain are less than 0.1, the stage of large strain should be more concerned during plastic forming. Furthermore, the predicting accuracy with the DRX kinetics model was testified by an electron back-scattered diffraction (EBSD) technique.
基金sponsored by the National Key Laboratory Foundation of Science and Technology on Materials under Shock and Impact(2021ZX52002222019)National Natural Science Foundation of China(NSFC No.U2141216)+1 种基金the Beijing Institute of Technology Young Scholar Startup Program.The authors gratefully acknowledge financial support from the China Scholarship Council(CSC No:202106030118)technical support from the Experimental Center of Advanced Materials(ECAM)of the Beijing Institute of Technology.
文摘TX-80 low-transformation-temperature(LTT)welding wire was used to replace the traditional ER 307Si welding wire to realize the connection of 22SiMn2TiB armor steel in manual overlay welding.The previously existing issues,such as welding cracks,large welding deformation,and severe welding residual stress,were solved to ensure good strength and ductility requirements.In particular,with the same welding conditions,TX-80 LTT wire eliminates welding cracks.It reduces the welding deformation no matter the base pretreatment of pre-setting angle or no pre-setting angle.By comparison,it was found that the microstructure at the TX-80 weld is mainly composed of martensite and a small amount of retained austenite.In contrast,the microstructure of the ER 307Si weld consists of a large amount of austenite and a small amount of skeleton-like ferrite.The variation trend of residual stress and microhardness from the weld to the base were investigated and compared with the mechanical properties of base materials.The TX-80 and the ER 307Si tensile samples elongation is 6.76%and 6.01%,while the ultimate tensile strengths are 877 and 667 MPa,respectively.The average impact toughness at room temperature of the ER 307Si weld is 143.9 J/cm^(2),much higher than that of the TX-80 weld,which is only 36.7 J/cm^(2).The relationship between impact and tensile properties with microstructure species and distribution was established.In addition,the fracture surface of the tensile and the impact samples was observed and analyzed.Deeper dimples,fewer pores,larger radiation zone,and shear lips of TX-80 samples indicate better tensile ductility and worse impact toughness than those of ER 307Si weld.