In this study,Ag/γ-Al_(2)O_(3)catalysts were synthesized by an Ar dielectric barrier discharge plasma using silver nitrate as the Ag source andγ-alumina(γ-Al_(2)O_(3))as the support.It is revealed that plasma can r...In this study,Ag/γ-Al_(2)O_(3)catalysts were synthesized by an Ar dielectric barrier discharge plasma using silver nitrate as the Ag source andγ-alumina(γ-Al_(2)O_(3))as the support.It is revealed that plasma can reduce silver ions to generate crystalline silver nanoparticles(Ag NPs)of good dispersion and uniformity on the alumina surface,leading to the formation of Ag/γ-Al_(2)O_(3)catalysts in a green manner without traditional chemical reductants.Ag/γ-Al_(2)O_(3)exhibited good catalytic activity and stability in CO oxidation reactions,and the activity increased with increase in the Ag content.For catalysts with more than 2 wt%Ag,100%CO conversion can be achieved at 300°C.The catalytic activity of the Ag/γ-Al_(2)O_(3)catalysts is also closely related to the size of theγ-alumina,where Ag/nano-γ-Al_(2)O_(3)catalysts demonstrate better performance than Ag/micro-γ-Al_(2)O_(3)catalysts with the same Ag content.In addition,the catalytic properties of plasma-generated Ag/nano-γ-Al_(2)O_(3)(Ag/γ-Al_(2)O_(3)-P)catalysts were compared with those of Ag/nano-γ-Al_(2)O_(3)catalysts prepared by the traditional calcination approach(Ag/γ-Al_(2)O_(3)-C),with the plasma-generated samples demonstrating better overall performance.This simple,rapid and green plasma process is considered to be applicable for the synthesis of diverse noble metal-based catalysts.展开更多
针对常规气相色谱填充柱分析稳定氢同位素的柱效低、峰宽大、保留时间长等问题,采用MnCl_2改性γ-Al_2O_3填充的石英毛细管柱开展了系统性柱效分析及氢同位素分析技术研究。研究结果表明,使用MnCl_2对γ-Al_2O_3进行改性后,可大大改善...针对常规气相色谱填充柱分析稳定氢同位素的柱效低、峰宽大、保留时间长等问题,采用MnCl_2改性γ-Al_2O_3填充的石英毛细管柱开展了系统性柱效分析及氢同位素分析技术研究。研究结果表明,使用MnCl_2对γ-Al_2O_3进行改性后,可大大改善单纯的γ-Al_2O_3表面有序度、孔结构和吸附性质,并将正氢(o-H_2)和仲氢(p-H_2)峰洗脱在单一谱峰区域内。制备的长1.0 m、内径0.53 mm的石英毛细填充柱与热导检测器(TCD)级联测试,在体积浓度1至10 m L/L范围内有较好的线性关系,对于低浓度样品检测的相对误差不大于5%。H_2、HD和D_2的保留时间可分别缩短至39、46和60 s,检出限可分别降低至0.046、0.067和0.072 m L/L。毛细管填充柱较常规填充柱具有峰形尖锐、相邻组分分离度高、保留时间短、检出限低等优点,可用于低浓度氢同位素快速测量及氢同位素在线分析。展开更多
基金financial support from National Natural Science Foundation of China(Nos.52004102 and 22078125)Postdoctoral Science Foundation of China(No.2021M690068)+2 种基金Fundamental Research Funds for the Central Universities(Nos.JUSRP221018 and JUSRP622038)Key Laboratory of Green Cleaning Technology and Detergent of Zhejiang Province(No.Q202204)Open Project of Key Laboratory of Green Chemical Engineering Process of Ministry of Education(No.GCP202112)。
文摘In this study,Ag/γ-Al_(2)O_(3)catalysts were synthesized by an Ar dielectric barrier discharge plasma using silver nitrate as the Ag source andγ-alumina(γ-Al_(2)O_(3))as the support.It is revealed that plasma can reduce silver ions to generate crystalline silver nanoparticles(Ag NPs)of good dispersion and uniformity on the alumina surface,leading to the formation of Ag/γ-Al_(2)O_(3)catalysts in a green manner without traditional chemical reductants.Ag/γ-Al_(2)O_(3)exhibited good catalytic activity and stability in CO oxidation reactions,and the activity increased with increase in the Ag content.For catalysts with more than 2 wt%Ag,100%CO conversion can be achieved at 300°C.The catalytic activity of the Ag/γ-Al_(2)O_(3)catalysts is also closely related to the size of theγ-alumina,where Ag/nano-γ-Al_(2)O_(3)catalysts demonstrate better performance than Ag/micro-γ-Al_(2)O_(3)catalysts with the same Ag content.In addition,the catalytic properties of plasma-generated Ag/nano-γ-Al_(2)O_(3)(Ag/γ-Al_(2)O_(3)-P)catalysts were compared with those of Ag/nano-γ-Al_(2)O_(3)catalysts prepared by the traditional calcination approach(Ag/γ-Al_(2)O_(3)-C),with the plasma-generated samples demonstrating better overall performance.This simple,rapid and green plasma process is considered to be applicable for the synthesis of diverse noble metal-based catalysts.
文摘针对常规气相色谱填充柱分析稳定氢同位素的柱效低、峰宽大、保留时间长等问题,采用MnCl_2改性γ-Al_2O_3填充的石英毛细管柱开展了系统性柱效分析及氢同位素分析技术研究。研究结果表明,使用MnCl_2对γ-Al_2O_3进行改性后,可大大改善单纯的γ-Al_2O_3表面有序度、孔结构和吸附性质,并将正氢(o-H_2)和仲氢(p-H_2)峰洗脱在单一谱峰区域内。制备的长1.0 m、内径0.53 mm的石英毛细填充柱与热导检测器(TCD)级联测试,在体积浓度1至10 m L/L范围内有较好的线性关系,对于低浓度样品检测的相对误差不大于5%。H_2、HD和D_2的保留时间可分别缩短至39、46和60 s,检出限可分别降低至0.046、0.067和0.072 m L/L。毛细管填充柱较常规填充柱具有峰形尖锐、相邻组分分离度高、保留时间短、检出限低等优点,可用于低浓度氢同位素快速测量及氢同位素在线分析。