In this study,Ag/γ-Al_(2)O_(3)catalysts were synthesized by an Ar dielectric barrier discharge plasma using silver nitrate as the Ag source andγ-alumina(γ-Al_(2)O_(3))as the support.It is revealed that plasma can r...In this study,Ag/γ-Al_(2)O_(3)catalysts were synthesized by an Ar dielectric barrier discharge plasma using silver nitrate as the Ag source andγ-alumina(γ-Al_(2)O_(3))as the support.It is revealed that plasma can reduce silver ions to generate crystalline silver nanoparticles(Ag NPs)of good dispersion and uniformity on the alumina surface,leading to the formation of Ag/γ-Al_(2)O_(3)catalysts in a green manner without traditional chemical reductants.Ag/γ-Al_(2)O_(3)exhibited good catalytic activity and stability in CO oxidation reactions,and the activity increased with increase in the Ag content.For catalysts with more than 2 wt%Ag,100%CO conversion can be achieved at 300°C.The catalytic activity of the Ag/γ-Al_(2)O_(3)catalysts is also closely related to the size of theγ-alumina,where Ag/nano-γ-Al_(2)O_(3)catalysts demonstrate better performance than Ag/micro-γ-Al_(2)O_(3)catalysts with the same Ag content.In addition,the catalytic properties of plasma-generated Ag/nano-γ-Al_(2)O_(3)(Ag/γ-Al_(2)O_(3)-P)catalysts were compared with those of Ag/nano-γ-Al_(2)O_(3)catalysts prepared by the traditional calcination approach(Ag/γ-Al_(2)O_(3)-C),with the plasma-generated samples demonstrating better overall performance.This simple,rapid and green plasma process is considered to be applicable for the synthesis of diverse noble metal-based catalysts.展开更多
Spray pyrolysis method was used to deposit Lutetium Oxide (Lu<sub>2</sub>O<sub>3</sub>) thin films using lutetium (III) chloride as source material and water as oxidizer. Annealing was carried ...Spray pyrolysis method was used to deposit Lutetium Oxide (Lu<sub>2</sub>O<sub>3</sub>) thin films using lutetium (III) chloride as source material and water as oxidizer. Annealing was carried out in argon atmosphere at 450°C for 60 minutes of the films. To investigate the composition and stoichiometry of sprayed as-deposited and annealed Lu<sub>2</sub>O<sub>3</sub> thin films, depth profile studies using X-ray photoelectron spectroscopy (XPS) was done. Nearly stoichiometric was observed for both annealed and as-deposited films in inner and surface layers.展开更多
Ga<sub>2</sub>O<sub>3</sub> thin films were fabricated by spray pyrolysis method using gallium acetylacetonate as source material and water as oxidizer. The films were annealed at 450°C fo...Ga<sub>2</sub>O<sub>3</sub> thin films were fabricated by spray pyrolysis method using gallium acetylacetonate as source material and water as oxidizer. The films were annealed at 450°C for 60 minutes in argon atmosphere. X-ray photoelectron spectroscopy (XPS) depth profile studies were carried out to analyze the stoichiometry and composition of sprayed as-deposited and annealed Ga<sub>2</sub>O<sub>3</sub> thin films. Surface layers and the inner layers of as-deposited and annealed films were found nearly stoichiometric.展开更多
The forming-regions of phosphate glasses doped with high Sm2O3 contents were studied by two step melting method. The relationship between absorption spectrum and rare earth contents was also discussed. The spectra of ...The forming-regions of phosphate glasses doped with high Sm2O3 contents were studied by two step melting method. The relationship between absorption spectrum and rare earth contents was also discussed. The spectra of BASP glasses were measured by spectrophotometer. The results show that the forming regions will shrink with the increase of Al2O3 and it is difficult to form glass when [PO4]/[AlO4] < 2. The forming regions tend to be a closed elliptical, and the intensity of characteristic absorption peak increases gradually with the increase of Sm2O3, the absorption lines broadens non-uniformly and there is approximate linear relation between optical density at the 1064 nm wavelength and Sm2O3 content.展开更多
基金financial support from National Natural Science Foundation of China(Nos.52004102 and 22078125)Postdoctoral Science Foundation of China(No.2021M690068)+2 种基金Fundamental Research Funds for the Central Universities(Nos.JUSRP221018 and JUSRP622038)Key Laboratory of Green Cleaning Technology and Detergent of Zhejiang Province(No.Q202204)Open Project of Key Laboratory of Green Chemical Engineering Process of Ministry of Education(No.GCP202112)。
文摘In this study,Ag/γ-Al_(2)O_(3)catalysts were synthesized by an Ar dielectric barrier discharge plasma using silver nitrate as the Ag source andγ-alumina(γ-Al_(2)O_(3))as the support.It is revealed that plasma can reduce silver ions to generate crystalline silver nanoparticles(Ag NPs)of good dispersion and uniformity on the alumina surface,leading to the formation of Ag/γ-Al_(2)O_(3)catalysts in a green manner without traditional chemical reductants.Ag/γ-Al_(2)O_(3)exhibited good catalytic activity and stability in CO oxidation reactions,and the activity increased with increase in the Ag content.For catalysts with more than 2 wt%Ag,100%CO conversion can be achieved at 300°C.The catalytic activity of the Ag/γ-Al_(2)O_(3)catalysts is also closely related to the size of theγ-alumina,where Ag/nano-γ-Al_(2)O_(3)catalysts demonstrate better performance than Ag/micro-γ-Al_(2)O_(3)catalysts with the same Ag content.In addition,the catalytic properties of plasma-generated Ag/nano-γ-Al_(2)O_(3)(Ag/γ-Al_(2)O_(3)-P)catalysts were compared with those of Ag/nano-γ-Al_(2)O_(3)catalysts prepared by the traditional calcination approach(Ag/γ-Al_(2)O_(3)-C),with the plasma-generated samples demonstrating better overall performance.This simple,rapid and green plasma process is considered to be applicable for the synthesis of diverse noble metal-based catalysts.
文摘Spray pyrolysis method was used to deposit Lutetium Oxide (Lu<sub>2</sub>O<sub>3</sub>) thin films using lutetium (III) chloride as source material and water as oxidizer. Annealing was carried out in argon atmosphere at 450°C for 60 minutes of the films. To investigate the composition and stoichiometry of sprayed as-deposited and annealed Lu<sub>2</sub>O<sub>3</sub> thin films, depth profile studies using X-ray photoelectron spectroscopy (XPS) was done. Nearly stoichiometric was observed for both annealed and as-deposited films in inner and surface layers.
文摘Ga<sub>2</sub>O<sub>3</sub> thin films were fabricated by spray pyrolysis method using gallium acetylacetonate as source material and water as oxidizer. The films were annealed at 450°C for 60 minutes in argon atmosphere. X-ray photoelectron spectroscopy (XPS) depth profile studies were carried out to analyze the stoichiometry and composition of sprayed as-deposited and annealed Ga<sub>2</sub>O<sub>3</sub> thin films. Surface layers and the inner layers of as-deposited and annealed films were found nearly stoichiometric.
基金Project supported by Research Project (A3820060136)
文摘The forming-regions of phosphate glasses doped with high Sm2O3 contents were studied by two step melting method. The relationship between absorption spectrum and rare earth contents was also discussed. The spectra of BASP glasses were measured by spectrophotometer. The results show that the forming regions will shrink with the increase of Al2O3 and it is difficult to form glass when [PO4]/[AlO4] < 2. The forming regions tend to be a closed elliptical, and the intensity of characteristic absorption peak increases gradually with the increase of Sm2O3, the absorption lines broadens non-uniformly and there is approximate linear relation between optical density at the 1064 nm wavelength and Sm2O3 content.