The aim of this study was to fabricate multi-layered recycled α-Fe<sub>2</sub>O<sub>3</sub>/OPEFB fiber/PCL composites for microwave absorbing applications in the 1 - 4 GHz frequency range. Th...The aim of this study was to fabricate multi-layered recycled α-Fe<sub>2</sub>O<sub>3</sub>/OPEFB fiber/PCL composites for microwave absorbing applications in the 1 - 4 GHz frequency range. The multi-layered composites were 6 mm thick and each consisted of a 2 mm thick layer of recycled α-Fe<sub>2</sub>O<sub>3</sub>/PCL composites at various loadings (5 wt% - 25 wt%) of 16.2 nm recycled α-Fe<sub>2</sub>O<sub>3</sub> nanofiller, placed between two layers of 2 mm thick OPEFB fiber/PCL composites blended at a fixed ratio of 7:3. The real (ε') and imaginary (ε") components of the relative complex permittivity were measured using the open-ended coaxial probe technique and the values obtained were applied as inputs for the Finite Element Method to calculate the reflection coefficient magnitudes from which the reflection loss (RL) properties were determined. Both ε' and ε" increased linearly with recycled α-Fe<sub>2</sub>O<sub>3</sub> nanofiller content and the values of ε' varied between 3.0 and 3.9 while the ε" values ranged between 0.26 and 0.64 within 1 - 4 GHz. The RL (dB) showed the most prominent values within the 1.38 - 1.46 GHz band with a minimum of -38 dB attained by the 25 wt% composite. Another batch of minimum values occurred in the 2.39 - 3.49 GHz range with the lowest of -25 dB at 2.8 GHz. The recycled α-Fe<sub>2</sub>O<sub>3</sub>/OPEFB fiber/PCL multi-layered composites are promising materials that can be engineered for solving noise problems in the 1 - 4 GHz range.展开更多
采用均匀沉淀法,以硫酸钛为前躯体,制备TiO_2-Bi_2O_3复合粉体材料。以罗丹明B为目标降解物,研究了热处理温度、催化剂用量对该复合材料光催化性能的影响。光催化活性随焙烧温度升高而增大,550℃焙烧的样品光催化活性高。当催化剂用量为...采用均匀沉淀法,以硫酸钛为前躯体,制备TiO_2-Bi_2O_3复合粉体材料。以罗丹明B为目标降解物,研究了热处理温度、催化剂用量对该复合材料光催化性能的影响。光催化活性随焙烧温度升高而增大,550℃焙烧的样品光催化活性高。当催化剂用量为0.026g/10 m L时,20 mg/L的罗丹明B溶液在紫外光照射100 min后,降解率可达到90%。该复合物对罗丹明B溶液的光催化降解符合一级动力学方程。展开更多
TiB2-Al2O3 composite powders were produced by self-propagating high-temperature synthesis（SHS） method with reductive process from B2O3-TiO2-AI system. X-ray diffraction（XRD） and scanning electron microscopy（SEM...TiB2-Al2O3 composite powders were produced by self-propagating high-temperature synthesis（SHS） method with reductive process from B2O3-TiO2-AI system. X-ray diffraction（XRD） and scanning electron microscopy（SEM） analyses show the presence of TiB2 and Al2O3 only in the composite powders produced by SHS. The powders are uniform and free-agglomerate. Transmission electron microscopy （TEM） and high resolution electron microscopy （HREM） observation of microstructure of the composite powders indicate that the interfaces of the TiB2-Al2O3 bond well, without any interfacial reaction products. It is proposed that the good interfacial bonding of the composite powders can be resulted from the TiB2 particles crystallizing and growing on the Al2O3 particles surface with surface defects acting as nucleation centers.展开更多
Processing of alumina fiber-reinforced alumina matrix composites by hot-pressing was described. The mechanical properties of the composites fabricated by different sintering conditions including temperature and pressu...Processing of alumina fiber-reinforced alumina matrix composites by hot-pressing was described. The mechanical properties of the composites fabricated by different sintering conditions including temperature and pressure have been investigated. The results indicated that the higher sintering temperature and pressure corresponded to the higher bulk density and higher maximum strength of the composite, whereas the pseudo-ductility of the composite was lower. The preliminary results of the composite with monazite-coated fibers showed that maximum strength could be improved up to 35% compared with the noncoated fiber composite in the same sintering condition. Moreover, the fracture behavior of the composite changed from completely brittle fracture to non-brittle fracture under the suitable sintering conditions. SEM observation of the fracture surface indicated that the coating worked as a protective barrier and avoided sintering of the fibers together even at high temperature and pressure during densificatio展开更多
A nanoheterojunction composite photocatalyst Bi2O3/TiO2 working under visible-light （λ≥ 420 nm） was prepared by combining two semiconductors Bi2O3 and TiO2 varying the Bi2O3/TiO2 molar ratio. Maleic acid was emplo...A nanoheterojunction composite photocatalyst Bi2O3/TiO2 working under visible-light （λ≥ 420 nm） was prepared by combining two semiconductors Bi2O3 and TiO2 varying the Bi2O3/TiO2 molar ratio. Maleic acid was employed as an organic binder to unite Bi2O3 and TiO2 nanoparticles. The SEM, TEM, XRD and diffuse reflectance spectra were utilized to characterize the prepared Bi2O3/TiO2 nanoheterojunction. The nanocomposite exhibited unusual high photocatalytic activity in decomposing 2-propanol in gas phase and phenol in aqueous phase and, evolution of CO2 under visible light irradiation while the end members exhibited low photocatalytic activity. The composite was optimized to 5 mol% Bi2O3/TiO2. The remarkable high photocatalytic efficiency originates from the unique relative energy band position of Bi2O3 and TiO2 as well as the absorption of visible light by Bi2O3.展开更多
Pd supported on TiO2-Al2O3 binary oxides prepared by coprecipitation method has been investigated for the total oxidation of methane. All Pd/TiO2-Al2O3 catalysts show higher activity than Pd/Al2O3 and Pd/TiO2. Among t...Pd supported on TiO2-Al2O3 binary oxides prepared by coprecipitation method has been investigated for the total oxidation of methane. All Pd/TiO2-Al2O3 catalysts show higher activity than Pd/Al2O3 and Pd/TiO2. Among them, Pd/2Ti-3Al with a Ti/Al ratio of 2 to 3 has a T90% of 395 ℃ at a gas hourly mass velocity of 33000 mL/（h＊g）, which is at least 50 ℃ lower than that of Pd supported on single metal oxide Al2O3 or TiO2. The results of TPR and ^180-isotope exchange experiments demonstrated that the excellent activity of Pd/2Ti-3Al was due to its high oxygen mobility and moderate reducibility, which is in accordance with our previous work, XPS results indicated that the dispersion of Pd was not the key factor to influence the catalytic activity.展开更多
文摘The aim of this study was to fabricate multi-layered recycled α-Fe<sub>2</sub>O<sub>3</sub>/OPEFB fiber/PCL composites for microwave absorbing applications in the 1 - 4 GHz frequency range. The multi-layered composites were 6 mm thick and each consisted of a 2 mm thick layer of recycled α-Fe<sub>2</sub>O<sub>3</sub>/PCL composites at various loadings (5 wt% - 25 wt%) of 16.2 nm recycled α-Fe<sub>2</sub>O<sub>3</sub> nanofiller, placed between two layers of 2 mm thick OPEFB fiber/PCL composites blended at a fixed ratio of 7:3. The real (ε') and imaginary (ε") components of the relative complex permittivity were measured using the open-ended coaxial probe technique and the values obtained were applied as inputs for the Finite Element Method to calculate the reflection coefficient magnitudes from which the reflection loss (RL) properties were determined. Both ε' and ε" increased linearly with recycled α-Fe<sub>2</sub>O<sub>3</sub> nanofiller content and the values of ε' varied between 3.0 and 3.9 while the ε" values ranged between 0.26 and 0.64 within 1 - 4 GHz. The RL (dB) showed the most prominent values within the 1.38 - 1.46 GHz band with a minimum of -38 dB attained by the 25 wt% composite. Another batch of minimum values occurred in the 2.39 - 3.49 GHz range with the lowest of -25 dB at 2.8 GHz. The recycled α-Fe<sub>2</sub>O<sub>3</sub>/OPEFB fiber/PCL multi-layered composites are promising materials that can be engineered for solving noise problems in the 1 - 4 GHz range.
文摘采用均匀沉淀法,以硫酸钛为前躯体,制备TiO_2-Bi_2O_3复合粉体材料。以罗丹明B为目标降解物,研究了热处理温度、催化剂用量对该复合材料光催化性能的影响。光催化活性随焙烧温度升高而增大,550℃焙烧的样品光催化活性高。当催化剂用量为0.026g/10 m L时,20 mg/L的罗丹明B溶液在紫外光照射100 min后,降解率可达到90%。该复合物对罗丹明B溶液的光催化降解符合一级动力学方程。
文摘TiB2-Al2O3 composite powders were produced by self-propagating high-temperature synthesis（SHS） method with reductive process from B2O3-TiO2-AI system. X-ray diffraction（XRD） and scanning electron microscopy（SEM） analyses show the presence of TiB2 and Al2O3 only in the composite powders produced by SHS. The powders are uniform and free-agglomerate. Transmission electron microscopy （TEM） and high resolution electron microscopy （HREM） observation of microstructure of the composite powders indicate that the interfaces of the TiB2-Al2O3 bond well, without any interfacial reaction products. It is proposed that the good interfacial bonding of the composite powders can be resulted from the TiB2 particles crystallizing and growing on the Al2O3 particles surface with surface defects acting as nucleation centers.
文摘Processing of alumina fiber-reinforced alumina matrix composites by hot-pressing was described. The mechanical properties of the composites fabricated by different sintering conditions including temperature and pressure have been investigated. The results indicated that the higher sintering temperature and pressure corresponded to the higher bulk density and higher maximum strength of the composite, whereas the pseudo-ductility of the composite was lower. The preliminary results of the composite with monazite-coated fibers showed that maximum strength could be improved up to 35% compared with the noncoated fiber composite in the same sintering condition. Moreover, the fracture behavior of the composite changed from completely brittle fracture to non-brittle fracture under the suitable sintering conditions. SEM observation of the fracture surface indicated that the coating worked as a protective barrier and avoided sintering of the fibers together even at high temperature and pressure during densificatio
文摘A nanoheterojunction composite photocatalyst Bi2O3/TiO2 working under visible-light （λ≥ 420 nm） was prepared by combining two semiconductors Bi2O3 and TiO2 varying the Bi2O3/TiO2 molar ratio. Maleic acid was employed as an organic binder to unite Bi2O3 and TiO2 nanoparticles. The SEM, TEM, XRD and diffuse reflectance spectra were utilized to characterize the prepared Bi2O3/TiO2 nanoheterojunction. The nanocomposite exhibited unusual high photocatalytic activity in decomposing 2-propanol in gas phase and phenol in aqueous phase and, evolution of CO2 under visible light irradiation while the end members exhibited low photocatalytic activity. The composite was optimized to 5 mol% Bi2O3/TiO2. The remarkable high photocatalytic efficiency originates from the unique relative energy band position of Bi2O3 and TiO2 as well as the absorption of visible light by Bi2O3.
基金Project supported by the Major State Basic Research Development Program （No. G2000077503）, the National Natural Science Foundation of China （No. 20173002）, and Cooperation Project between NSFC and DFG （No. 20411130104）.
文摘Pd supported on TiO2-Al2O3 binary oxides prepared by coprecipitation method has been investigated for the total oxidation of methane. All Pd/TiO2-Al2O3 catalysts show higher activity than Pd/Al2O3 and Pd/TiO2. Among them, Pd/2Ti-3Al with a Ti/Al ratio of 2 to 3 has a T90% of 395 ℃ at a gas hourly mass velocity of 33000 mL/（h＊g）, which is at least 50 ℃ lower than that of Pd supported on single metal oxide Al2O3 or TiO2. The results of TPR and ^180-isotope exchange experiments demonstrated that the excellent activity of Pd/2Ti-3Al was due to its high oxygen mobility and moderate reducibility, which is in accordance with our previous work, XPS results indicated that the dispersion of Pd was not the key factor to influence the catalytic activity.