A set of correct expressions for calculating activities and activity coefficients from binary phase diagrams involving intermediate compounds are presented in this paper by the introduction of a correct parameter θ. ...A set of correct expressions for calculating activities and activity coefficients from binary phase diagrams involving intermediate compounds are presented in this paper by the introduction of a correct parameter θ. The application of these expressions to system Mg-Sn shows that they are quite feasible.展开更多
New formulae for calculating activities and activity coefficients from binary phase diagrams containing solidsolution are presented. In the new formulae, a parameterθ is introduced. It seems be more efficient The app...New formulae for calculating activities and activity coefficients from binary phase diagrams containing solidsolution are presented. In the new formulae, a parameterθ is introduced. It seems be more efficient The application ofthese formulae to system Ag-Pb proves its efficiency.展开更多
The 5Cu40Zn55Al and 15Cu20Zn65Al alloys were prepared in the Al-Zn-Cu system. There exist the metastable phases ε and θ in the two alloys after homogenization treatment and furnace cooling,respectively. It is shown ...The 5Cu40Zn55Al and 15Cu20Zn65Al alloys were prepared in the Al-Zn-Cu system. There exist the metastable phases ε and θ in the two alloys after homogenization treatment and furnace cooling,respectively. It is shown that the particles are refined from 3 mm to less than 10 μm after hammering the two alloys but there are still metastable phases. This means that the phase constituents of the two alloys have no changes by the deformation,which is different from that by balling. The phase constituents are not changed at room temperature by hammering,which is dependent on the deformation mechanism of hammering.展开更多
文摘A set of correct expressions for calculating activities and activity coefficients from binary phase diagrams involving intermediate compounds are presented in this paper by the introduction of a correct parameter θ. The application of these expressions to system Mg-Sn shows that they are quite feasible.
文摘New formulae for calculating activities and activity coefficients from binary phase diagrams containing solidsolution are presented. In the new formulae, a parameterθ is introduced. It seems be more efficient The application ofthese formulae to system Ag-Pb proves its efficiency.
基金Project(50171019) supported by the National Natural Science Foundation of ChinaProject(1063293) supported by Shenyang Science and Technology Foundation, China
文摘The 5Cu40Zn55Al and 15Cu20Zn65Al alloys were prepared in the Al-Zn-Cu system. There exist the metastable phases ε and θ in the two alloys after homogenization treatment and furnace cooling,respectively. It is shown that the particles are refined from 3 mm to less than 10 μm after hammering the two alloys but there are still metastable phases. This means that the phase constituents of the two alloys have no changes by the deformation,which is different from that by balling. The phase constituents are not changed at room temperature by hammering,which is dependent on the deformation mechanism of hammering.