The stable ranges concerning the composition and temperature have been experimentally de- termined for the intermetallic compounds in system Fe-Cr-Mo at high-temperatures. The isothermal section of the Fe-Cr-Mo ternar...The stable ranges concerning the composition and temperature have been experimentally de- termined for the intermetallic compounds in system Fe-Cr-Mo at high-temperatures. The isothermal section of the Fe-Cr-Mo ternary phase diagram at 1250℃ and the formation re- actions for the intermetallic compounds, which are different in part from those shown in the literature, have been proposed.展开更多
Correlation between pitting corrosion behavior and chi（ χ ）phase formed after a short-term aging（5,10 and 15 min）at 850 ℃ of 2205 duplex stainless steel（DSS）was investigated using potentiodynamic polarization ...Correlation between pitting corrosion behavior and chi（ χ ）phase formed after a short-term aging（5,10 and 15 min）at 850 ℃ of 2205 duplex stainless steel（DSS）was investigated using potentiodynamic polarization tests,optical microscopy,and scanning electron microscopy equipped with energy-dispersive spectrum system.Results showed that after aging for 5min,the χ phase initially precipitated at ferrite grain boundaries,developed and then became linked with prolonging aging time.The χ phase was rich in Cr and Mo,resulting in formation of depleted zones nearby.The χ phase could reduce corrosion resistance of DSS and slightly influence its stability,but the specimens still displayed the capacity for repassivation.Some lines of evidence showed that stable pitting corrosion initiated at the boundaries of precipitates.The χ phase was selectively corroded during the first stage of corrosion and then the depleted zones nearby were attacked.In addition,the grain size and volume of precipitates also affected pit nucleation and progress,and suitable size and distribution of χ phase could aggravate pit initiation at precipitate boundaries.The χ phase with considerably low volume fraction and small size was not sensitive position for pit initiation.展开更多
文摘The stable ranges concerning the composition and temperature have been experimentally de- termined for the intermetallic compounds in system Fe-Cr-Mo at high-temperatures. The isothermal section of the Fe-Cr-Mo ternary phase diagram at 1250℃ and the formation re- actions for the intermetallic compounds, which are different in part from those shown in the literature, have been proposed.
基金Item Sponsored by National Natural Science Foundation of China(51371123)Special Scientific Research Fund for the Doctoral Program of Higher Education of China(2013140211003)Natural Science Foundation of Shanxi Province of China(2014011002)
文摘Correlation between pitting corrosion behavior and chi（ χ ）phase formed after a short-term aging（5,10 and 15 min）at 850 ℃ of 2205 duplex stainless steel（DSS）was investigated using potentiodynamic polarization tests,optical microscopy,and scanning electron microscopy equipped with energy-dispersive spectrum system.Results showed that after aging for 5min,the χ phase initially precipitated at ferrite grain boundaries,developed and then became linked with prolonging aging time.The χ phase was rich in Cr and Mo,resulting in formation of depleted zones nearby.The χ phase could reduce corrosion resistance of DSS and slightly influence its stability,but the specimens still displayed the capacity for repassivation.Some lines of evidence showed that stable pitting corrosion initiated at the boundaries of precipitates.The χ phase was selectively corroded during the first stage of corrosion and then the depleted zones nearby were attacked.In addition,the grain size and volume of precipitates also affected pit nucleation and progress,and suitable size and distribution of χ phase could aggravate pit initiation at precipitate boundaries.The χ phase with considerably low volume fraction and small size was not sensitive position for pit initiation.