Varistor ceramics of ZnO Bi 2O 3 TiO 2 Sb 2O 3 system have been fabricated by introducing pre fabricated ZnO seed grains with different size distributions respectively. The results show that the varistor properties we...Varistor ceramics of ZnO Bi 2O 3 TiO 2 Sb 2O 3 system have been fabricated by introducing pre fabricated ZnO seed grains with different size distributions respectively. The results show that the varistor properties were significantly influenced by the size of introduced seed grains, and introducing larger seed grains is more advantageous to the modification of microstructure and the improvement of varistor properties. The varistor properties were considerably improved with a moderately increased sintering temperature or time, whereas degraded apparently when the sintering temperature or time was excessively increased. Compared with the sintering time, the sintering temperature plays a more critical role in determining the varistor properties. By introducing pre fabricated ZnO seed grains into the original powders, low voltage ZnO varistor ceramics possessing the desired electrical properties have been produced with a sintering temperature of about 1 210 ℃ and a sintering temperature of 2～2.5 h. [展开更多
The microstructures and electrical properties of Bi0.5（Na1-x-yKxLiy）0.5TiO3 lead-free piezoelectric ceramics were studied.These ceramics were prepared by conventional ceramic technique.XRD analysis reveals that the ...The microstructures and electrical properties of Bi0.5（Na1-x-yKxLiy）0.5TiO3 lead-free piezoelectric ceramics were studied.These ceramics were prepared by conventional ceramic technique.XRD analysis reveals that the ceramics possess almost pure perovskite phase when y≤0.2.The SEM results show that,with more amounts of Li＋,the crystalline grain growing speed is accelerated,and the sintering temperature can effectively be decreased.The measurements of piezoelectric properties indicate that the ceramics with relatively low amount of Li＋ and high amount of K＋ have comparatively large piezoelectricity.The dielectric measurements show that the ceramics have properties like relaxor ferroelectrics and diffuse phase transition（DPT） at Td and Tc,respectively.The results of ferroelectric measurements reveal the system has relatively higher remanent polarization Pr（27.6 μC/cm2） and lower coercive field Ec（37.5 kV/cm）.展开更多
The ac impedance of Nb-doped semicon-ducting (Bao.72Pbo.28)TiO3 ceramics implanted with copper ions(200keV,6X1015 and 1X1017 ions/cm2) in the temperature range 25-320C and the frequency range 10 Hz -13MHz was measured...The ac impedance of Nb-doped semicon-ducting (Bao.72Pbo.28)TiO3 ceramics implanted with copper ions(200keV,6X1015 and 1X1017 ions/cm2) in the temperature range 25-320C and the frequency range 10 Hz -13MHz was measured. According to the change of impedance spectroscopy and the equivalent circuit model of semiconducting(Ba, Pb)TiO3 ceramics, the dependence of resistance of bulk and grain-boundary on temperature was analyzed. The results show that relatively low dose must be used to increase the magnitude of the positive temperature coeffieient of resistance(PTCR)effects in the cermmics. In addition,the effects of Cu ion implantation on the PTCR behavior of the ceramics was studied by raststance-tempera-ture measurement.展开更多
Lead-free piezoelectric ceramics of (Bi1/2Na1/2)TiO3-BaTiO3(BNT-BT) were prepared by the conventional piezoelectric ceramic preparation technique (free air atmosphere sintering). The influence of BaTiO3 additive amoun...Lead-free piezoelectric ceramics of (Bi1/2Na1/2)TiO3-BaTiO3(BNT-BT) were prepared by the conventional piezoelectric ceramic preparation technique (free air atmosphere sintering). The influence of BaTiO3 additive amount and La2O3 additive amount on the properties of BNT-BT lead-free piezoceramics were investigated. The results show that the dielectric constant(ε) and piezoelectric strain constant(d33) of materials start increasing and then decreasing while BaTiO3 additive amount increasing, the e and d33 of materials have maximum value (ε= 1650, d33 = 120 PC·N -1 ) while x (BaTiO3) =0.06 mol. Theεand d33 of materials start increasing and then decreasing while La2O3 additive amount increasing, the e and d33 of materials have maximum value (ε= 1684, d33 = 153 PC·N-1) while w(La2O3) =0.3% . The influence of La2O3 additive amount on the microstructure of BNT-BT piezoelectric ceramics was analysed by SEM( scanning electron microscope). The influence mechanism of La2O3 additive amount on the properties of BNT-BT piezoelectric ceramics was discussed. The BNT-BT ceramics with optimum comprehensive properties were obtained.展开更多
The nanotitanium dioxide （TiO2） photocatalytic and porous ceramic filtering technique is one of the advanced methods to effectively treat organic wastewater. The TiO2 sol doped with Fe^3＋ ions was prepared by sol-g...The nanotitanium dioxide （TiO2） photocatalytic and porous ceramic filtering technique is one of the advanced methods to effectively treat organic wastewater. The TiO2 sol doped with Fe^3＋ ions was prepared by sol-gel processing. The influences of the process conditions of coating nanophotocatalytic material- Fe^3＋-TiO2 film on the surface of porous ceramic filter by dipping-lift method on the performance of porous ceramic filter were studied. The porous ceramic filters have two functions at the same time, filtration and photocatalytic degradation. The results of this study showed that the pH and viscosity of the sol, amount of Fe^3＋ ions doped as well as the coating times greatly affect the quality of coating film, the performance parameters and the photocatalytic activity of the porous ceramic filter. When the pH of the sol is 3-4, the viscosity is about 6 mPa.S, the amount of doped Fe^3＋ ions is about 2.0 g/L, the porous ceramic filter has been shown to have the best filtering performance and photocatalytic activity. In this condition, the porosity of porous ceramic is about 42.5%, the pore diameter is 8-10μm. The degradation of methyl-orange is 74.76% under lighting for 120 rain.展开更多
Al 2O 3-SiO 2-TiO 2-ZrO 2 supported membranes were prepar ed by Sol-Gel method. These composite ceramic membranes are level, even and no macro crack. There exist several crystalline phases such as Al 2O 3, TiO...Al 2O 3-SiO 2-TiO 2-ZrO 2 supported membranes were prepar ed by Sol-Gel method. These composite ceramic membranes are level, even and no macro crack. There exist several crystalline phases such as Al 2O 3, TiO 2(a natase), Al 2SiO 5, and ZrO 2 in these membranes. Changing the molar ratio of Al∶Si∶Ti∶Zr,the kinds and content of crystal phases of composite membranes could be different, which may lead to a variety of microstructure of membranes. The surface nanoscale topography and microstructure of membranes were investiga ted by XRD,SEM,AFM,EPMA. The effects of additives and heat treatments on the sur face nanoscale topography and microstructure of composite ceramic membranes were also analyzed.展开更多
The conventional Al2O3-13 wt. % TiO2 composite ceramic coatings are fabricated by plasma spraying on the surface of extrusion wheel. The microstrueture, morphology and phase compositions of the substrate and coat- ing...The conventional Al2O3-13 wt. % TiO2 composite ceramic coatings are fabricated by plasma spraying on the surface of extrusion wheel. The microstrueture, morphology and phase compositions of the substrate and coat- ing are investigated by using X-ray diffractometry （XRD） , scanning electron microsopy （SEM） and energy dis- persive spectroscopy （EDS）. Moreover, the microhardness of the substrate and the coating are investigated using Vickers mierohardness tester, the friction and wear behaviors of the substrate and the coating are investigated by using a block-on-ring tribometer under dry sliding conditions with the load of 245 N. The results show that both γ-Al2O3 and α-Al2O3 phases are observed in the as-sprayed coatings, the mian phase is γ-Al2O3. There are white particulates Al2O3 on its surface. The Al2O3-13 wt. % TiO2 coating possesses higher mierohardness which is about 1018HV and 1.6 times that of the substrate. The wear performance of coating is better than that of the substrate. In a practical application, the life of the extrusion wheel which is plasma sprayed Al2O3-13 wt. % TiO2 coating on the surface is 1.2 times that of the conventional extrusion wheel, and the life is about 330 h.展开更多
文摘Varistor ceramics of ZnO Bi 2O 3 TiO 2 Sb 2O 3 system have been fabricated by introducing pre fabricated ZnO seed grains with different size distributions respectively. The results show that the varistor properties were significantly influenced by the size of introduced seed grains, and introducing larger seed grains is more advantageous to the modification of microstructure and the improvement of varistor properties. The varistor properties were considerably improved with a moderately increased sintering temperature or time, whereas degraded apparently when the sintering temperature or time was excessively increased. Compared with the sintering time, the sintering temperature plays a more critical role in determining the varistor properties. By introducing pre fabricated ZnO seed grains into the original powders, low voltage ZnO varistor ceramics possessing the desired electrical properties have been produced with a sintering temperature of about 1 210 ℃ and a sintering temperature of 2～2.5 h. [
基金Supported by Program for New Century Excellent Talents in University(No.NCET-07-0329)
文摘The microstructures and electrical properties of Bi0.5（Na1-x-yKxLiy）0.5TiO3 lead-free piezoelectric ceramics were studied.These ceramics were prepared by conventional ceramic technique.XRD analysis reveals that the ceramics possess almost pure perovskite phase when y≤0.2.The SEM results show that,with more amounts of Li＋,the crystalline grain growing speed is accelerated,and the sintering temperature can effectively be decreased.The measurements of piezoelectric properties indicate that the ceramics with relatively low amount of Li＋ and high amount of K＋ have comparatively large piezoelectricity.The dielectric measurements show that the ceramics have properties like relaxor ferroelectrics and diffuse phase transition（DPT） at Td and Tc,respectively.The results of ferroelectric measurements reveal the system has relatively higher remanent polarization Pr（27.6 μC/cm2） and lower coercive field Ec（37.5 kV/cm）.
文摘The ac impedance of Nb-doped semicon-ducting (Bao.72Pbo.28)TiO3 ceramics implanted with copper ions(200keV,6X1015 and 1X1017 ions/cm2) in the temperature range 25-320C and the frequency range 10 Hz -13MHz was measured. According to the change of impedance spectroscopy and the equivalent circuit model of semiconducting(Ba, Pb)TiO3 ceramics, the dependence of resistance of bulk and grain-boundary on temperature was analyzed. The results show that relatively low dose must be used to increase the magnitude of the positive temperature coeffieient of resistance(PTCR)effects in the cermmics. In addition,the effects of Cu ion implantation on the PTCR behavior of the ceramics was studied by raststance-tempera-ture measurement.
文摘Lead-free piezoelectric ceramics of (Bi1/2Na1/2)TiO3-BaTiO3(BNT-BT) were prepared by the conventional piezoelectric ceramic preparation technique (free air atmosphere sintering). The influence of BaTiO3 additive amount and La2O3 additive amount on the properties of BNT-BT lead-free piezoceramics were investigated. The results show that the dielectric constant(ε) and piezoelectric strain constant(d33) of materials start increasing and then decreasing while BaTiO3 additive amount increasing, the e and d33 of materials have maximum value (ε= 1650, d33 = 120 PC·N -1 ) while x (BaTiO3) =0.06 mol. Theεand d33 of materials start increasing and then decreasing while La2O3 additive amount increasing, the e and d33 of materials have maximum value (ε= 1684, d33 = 153 PC·N-1) while w(La2O3) =0.3% . The influence of La2O3 additive amount on the microstructure of BNT-BT piezoelectric ceramics was analysed by SEM( scanning electron microscope). The influence mechanism of La2O3 additive amount on the properties of BNT-BT piezoelectric ceramics was discussed. The BNT-BT ceramics with optimum comprehensive properties were obtained.
文摘The nanotitanium dioxide （TiO2） photocatalytic and porous ceramic filtering technique is one of the advanced methods to effectively treat organic wastewater. The TiO2 sol doped with Fe^3＋ ions was prepared by sol-gel processing. The influences of the process conditions of coating nanophotocatalytic material- Fe^3＋-TiO2 film on the surface of porous ceramic filter by dipping-lift method on the performance of porous ceramic filter were studied. The porous ceramic filters have two functions at the same time, filtration and photocatalytic degradation. The results of this study showed that the pH and viscosity of the sol, amount of Fe^3＋ ions doped as well as the coating times greatly affect the quality of coating film, the performance parameters and the photocatalytic activity of the porous ceramic filter. When the pH of the sol is 3-4, the viscosity is about 6 mPa.S, the amount of doped Fe^3＋ ions is about 2.0 g/L, the porous ceramic filter has been shown to have the best filtering performance and photocatalytic activity. In this condition, the porosity of porous ceramic is about 42.5%, the pore diameter is 8-10μm. The degradation of methyl-orange is 74.76% under lighting for 120 rain.
文摘Al 2O 3-SiO 2-TiO 2-ZrO 2 supported membranes were prepar ed by Sol-Gel method. These composite ceramic membranes are level, even and no macro crack. There exist several crystalline phases such as Al 2O 3, TiO 2(a natase), Al 2SiO 5, and ZrO 2 in these membranes. Changing the molar ratio of Al∶Si∶Ti∶Zr,the kinds and content of crystal phases of composite membranes could be different, which may lead to a variety of microstructure of membranes. The surface nanoscale topography and microstructure of membranes were investiga ted by XRD,SEM,AFM,EPMA. The effects of additives and heat treatments on the sur face nanoscale topography and microstructure of composite ceramic membranes were also analyzed.
文摘The conventional Al2O3-13 wt. % TiO2 composite ceramic coatings are fabricated by plasma spraying on the surface of extrusion wheel. The microstrueture, morphology and phase compositions of the substrate and coat- ing are investigated by using X-ray diffractometry （XRD） , scanning electron microsopy （SEM） and energy dis- persive spectroscopy （EDS）. Moreover, the microhardness of the substrate and the coating are investigated using Vickers mierohardness tester, the friction and wear behaviors of the substrate and the coating are investigated by using a block-on-ring tribometer under dry sliding conditions with the load of 245 N. The results show that both γ-Al2O3 and α-Al2O3 phases are observed in the as-sprayed coatings, the mian phase is γ-Al2O3. There are white particulates Al2O3 on its surface. The Al2O3-13 wt. % TiO2 coating possesses higher mierohardness which is about 1018HV and 1.6 times that of the substrate. The wear performance of coating is better than that of the substrate. In a practical application, the life of the extrusion wheel which is plasma sprayed Al2O3-13 wt. % TiO2 coating on the surface is 1.2 times that of the conventional extrusion wheel, and the life is about 330 h.