The structure and dielectric properties of(Pb,Sr)Nb2O6-NaNbO3-SiO2 glass-ceramics with different Pb and Sr contents were investigated.The XRD pattern of glass-ceramics without Sr substitution is different from that wi...The structure and dielectric properties of(Pb,Sr)Nb2O6-NaNbO3-SiO2 glass-ceramics with different Pb and Sr contents were investigated.The XRD pattern of glass-ceramics without Sr substitution is different from that with Sr substitution,which indicates the existence of orthorhombic phase in the latter ones.TEM bright field observation shows nanosized microstructures,while for samples with Sr,typical eutectic microstructure with separated crystallized bands is found in the glass matrix.Dielectric properties measurement of the samples indicates an obvious improvement of dielectric constant,dielectric loss,DC field and temperature dependence of dielectric constant when the molar ratio of Sr to Pb is 4:6.展开更多
The influences of the PbO-B2O3-CuV2O6 （PBC） additives on the microwave dielectric properties of （Pb0.5Ca0.5） （Fe0.5Nb0.5）O3 （PCFN） ceramics were investigated as a function of sintering temperature from 950 ℃ ...The influences of the PbO-B2O3-CuV2O6 （PBC） additives on the microwave dielectric properties of （Pb0.5Ca0.5） （Fe0.5Nb0.5）O3 （PCFN） ceramics were investigated as a function of sintering temperature from 950 ℃ to 1 100 ℃. The sintering temperature of the specimens with the glass could be lowered from 1125 ℃ to 1 025℃ without the degradation of microwave dielectric properties. The microwave results showed that the dielectric constant cr was not significantly different while Qf values decreased with the increase of CuV206 content of PBC glass. For the specimens doped with PB-CV0.1 glass （81% PbO-9% B203-10% CuV2O6） and sintered at 1 025 ℃ for 3 h, the microwave dielectric properties of Qf=4 823 GHz, Cr=107.1 with TCF=＋15.03 ×10^-6/℃ were obtained.展开更多
A series of aluminates were successfully synthesized via hydrothermal precipitated method, followed by solid state reaction at high temperature. The optimum condition to synthesize Sr3Al2O6 was determined by adjusting...A series of aluminates were successfully synthesized via hydrothermal precipitated method, followed by solid state reaction at high temperature. The optimum condition to synthesize Sr3Al2O6 was determined by adjusting the pH value of the solutions. The as prepared Sr3Al2O6 with lattice constant a=1.58556nm were characterized by X ray diffraction (XRD) and photoluminescence spectroscopy (PLS). In PL spectrum, a strongest peak at 655nm is observed, which is corresponding to red light, with an excitation wavelength of 459nm.展开更多
Thermoelectric properties of Li-doped Sr0.70Ba0.30Nb2O6-δ ceramics were investigated in the temperature range from 323 K to 1073 K. The electrical conductivity increases significantly after lithium interstitial dopin...Thermoelectric properties of Li-doped Sr0.70Ba0.30Nb2O6-δ ceramics were investigated in the temperature range from 323 K to 1073 K. The electrical conductivity increases significantly after lithium interstitial doping. However, both of the magnitudes of Seebeck coefficient and electrical conductivity vary non-monotonically but synchronously with the doping contents, indicating that doped lithium ions may not be fully ionized and oxygen vacancy may also contribute to carriers. The lattice thermal conductivity increases firstly and then decreases as the doping content increases, which is affected by competing factors.Thermoelectric performance is enhanced by lithium interstitial doping due to the increase of the power factor and the thermoelectric figure of merit reaches maximum value （0.21 at 1073 K） in the sample Sr0.70Ba0.30Li0.10Nb2O6.展开更多
The thermoelectric properties of Sr0.61Ba0.39Nb2O6-δ ceramics, reduced in different conditions, are investigated in the temperature range from 323 K to 1073 K. The electrical transport behaviors of the samples are do...The thermoelectric properties of Sr0.61Ba0.39Nb2O6-δ ceramics, reduced in different conditions, are investigated in the temperature range from 323 K to 1073 K. The electrical transport behaviors of the samples are dominated by the thermal-activated polaron hopping in the low temperature range, the Fermi glass behavior in the middle temperature range, and the Anderson localized behavior in the high temperature range. The thermal conductivity presents a plateau at high- temperatures, indicating a glass-like thermal conduction behavior. Both the thermoelectric power factor and the thermal conductivity increase with the increase of the degree of oxygen-reduction. Taking these two factors into account, the oxygen-reduction can still contribute to promoting the thermoelectric figure of merit. The highest ZT value is obtained to be -0.19 at 1073 K in the heaviest oxygen reduced sample.展开更多
文摘The structure and dielectric properties of(Pb,Sr)Nb2O6-NaNbO3-SiO2 glass-ceramics with different Pb and Sr contents were investigated.The XRD pattern of glass-ceramics without Sr substitution is different from that with Sr substitution,which indicates the existence of orthorhombic phase in the latter ones.TEM bright field observation shows nanosized microstructures,while for samples with Sr,typical eutectic microstructure with separated crystallized bands is found in the glass matrix.Dielectric properties measurement of the samples indicates an obvious improvement of dielectric constant,dielectric loss,DC field and temperature dependence of dielectric constant when the molar ratio of Sr to Pb is 4:6.
基金Project supported by the National Natural Science Foundation of China (Grant No.60578041)the National High Tech-nology Research and Development Program of China (Grant No.715-006-0060)
文摘The influences of the PbO-B2O3-CuV2O6 （PBC） additives on the microwave dielectric properties of （Pb0.5Ca0.5） （Fe0.5Nb0.5）O3 （PCFN） ceramics were investigated as a function of sintering temperature from 950 ℃ to 1 100 ℃. The sintering temperature of the specimens with the glass could be lowered from 1125 ℃ to 1 025℃ without the degradation of microwave dielectric properties. The microwave results showed that the dielectric constant cr was not significantly different while Qf values decreased with the increase of CuV206 content of PBC glass. For the specimens doped with PB-CV0.1 glass （81% PbO-9% B203-10% CuV2O6） and sintered at 1 025 ℃ for 3 h, the microwave dielectric properties of Qf=4 823 GHz, Cr=107.1 with TCF=＋15.03 ×10^-6/℃ were obtained.
文摘A series of aluminates were successfully synthesized via hydrothermal precipitated method, followed by solid state reaction at high temperature. The optimum condition to synthesize Sr3Al2O6 was determined by adjusting the pH value of the solutions. The as prepared Sr3Al2O6 with lattice constant a=1.58556nm were characterized by X ray diffraction (XRD) and photoluminescence spectroscopy (PLS). In PL spectrum, a strongest peak at 655nm is observed, which is corresponding to red light, with an excitation wavelength of 459nm.
基金supported by the National Basic Research Program of China(Grant No.2013CB632506)the National Natural Science Foundation of China(Grant Nos.51202132,51231007,and 11374186)
文摘Thermoelectric properties of Li-doped Sr0.70Ba0.30Nb2O6-δ ceramics were investigated in the temperature range from 323 K to 1073 K. The electrical conductivity increases significantly after lithium interstitial doping. However, both of the magnitudes of Seebeck coefficient and electrical conductivity vary non-monotonically but synchronously with the doping contents, indicating that doped lithium ions may not be fully ionized and oxygen vacancy may also contribute to carriers. The lattice thermal conductivity increases firstly and then decreases as the doping content increases, which is affected by competing factors.Thermoelectric performance is enhanced by lithium interstitial doping due to the increase of the power factor and the thermoelectric figure of merit reaches maximum value （0.21 at 1073 K） in the sample Sr0.70Ba0.30Li0.10Nb2O6.
基金Project supported by the National Basic Research Program of China(Grant No.2013CB632506)the National Natural Science Foundation of China(Grant Nos.51202132 and 51002087)
文摘The thermoelectric properties of Sr0.61Ba0.39Nb2O6-δ ceramics, reduced in different conditions, are investigated in the temperature range from 323 K to 1073 K. The electrical transport behaviors of the samples are dominated by the thermal-activated polaron hopping in the low temperature range, the Fermi glass behavior in the middle temperature range, and the Anderson localized behavior in the high temperature range. The thermal conductivity presents a plateau at high- temperatures, indicating a glass-like thermal conduction behavior. Both the thermoelectric power factor and the thermal conductivity increase with the increase of the degree of oxygen-reduction. Taking these two factors into account, the oxygen-reduction can still contribute to promoting the thermoelectric figure of merit. The highest ZT value is obtained to be -0.19 at 1073 K in the heaviest oxygen reduced sample.