A precursor of BaCe0.5Zr0.4Y0. 1O3-α electrolytes was synthesized by the sol-gel method and sintered at temperature which were 150 - 250 ℃ lower than by solid state reaction. The AC impedance spectrums of electrolyt...A precursor of BaCe0.5Zr0.4Y0. 1O3-α electrolytes was synthesized by the sol-gel method and sintered at temperature which were 150 - 250 ℃ lower than by solid state reaction. The AC impedance spectrums of electrolytes were measured by AUTOLAB PGSTA30 electrochemical measuring device at different temperatures. The conductivities of the electrolytes are 1.62×10^-4 - 6.43×10^-3, 2.52×10^-5 - 3.73×10^-3S·cm^-1 in the temperature range of 350-800℃. The activity energies are 0.54 and 0.84 eV. At the same time BaCe0.9Y0.1O3-α was prepared by direct solid state reaction. The conductivity of BaCe0.9Y0.1O3-α is 1 × 10^-4- 4×10^-3 S·cm^-1 and the activation energy is 0.50 eV at the same condition. The results show that conduction of electrolyte prepared by sol-gel method is higher than the one by solid state reaction. As far as BaCe0.9Y0.1O3-α concerned, its conductivity of the Zr-substituted specimens is decreased.展开更多
Pr0.6-x NdxCa0.4 FeO3-δ （ x = 0.0, 0.2, 0.3, 0.4, 0.5, 0.6） were synthesized using Pechini method. A number of studies were conducted concerning composition, specific area, crystalline structure and microstructure ...Pr0.6-x NdxCa0.4 FeO3-δ （ x = 0.0, 0.2, 0.3, 0.4, 0.5, 0.6） were synthesized using Pechini method. A number of studies were conducted concerning composition, specific area, crystalline structure and microstructure of the samples by means of FT-IR, BET, XRD TG-DTA and SEM. The results show that all the samples with different doping amounts of Pr^3＋ and Nd^3＋ on A-site are fine dispersed, and mean particle size less than 100 nm. The powders have good sinterability, and the relative density is 95% after sintered at 1200 ℃ for 2 h. It is found that all specimens are entirely single phase solid solutions with orthorhombic perovskite structure, the stable perovskitetype phase is formed completely after calcination at 900 ℃.展开更多
文摘A precursor of BaCe0.5Zr0.4Y0. 1O3-α electrolytes was synthesized by the sol-gel method and sintered at temperature which were 150 - 250 ℃ lower than by solid state reaction. The AC impedance spectrums of electrolytes were measured by AUTOLAB PGSTA30 electrochemical measuring device at different temperatures. The conductivities of the electrolytes are 1.62×10^-4 - 6.43×10^-3, 2.52×10^-5 - 3.73×10^-3S·cm^-1 in the temperature range of 350-800℃. The activity energies are 0.54 and 0.84 eV. At the same time BaCe0.9Y0.1O3-α was prepared by direct solid state reaction. The conductivity of BaCe0.9Y0.1O3-α is 1 × 10^-4- 4×10^-3 S·cm^-1 and the activation energy is 0.50 eV at the same condition. The results show that conduction of electrolyte prepared by sol-gel method is higher than the one by solid state reaction. As far as BaCe0.9Y0.1O3-α concerned, its conductivity of the Zr-substituted specimens is decreased.
文摘Pr0.6-x NdxCa0.4 FeO3-δ （ x = 0.0, 0.2, 0.3, 0.4, 0.5, 0.6） were synthesized using Pechini method. A number of studies were conducted concerning composition, specific area, crystalline structure and microstructure of the samples by means of FT-IR, BET, XRD TG-DTA and SEM. The results show that all the samples with different doping amounts of Pr^3＋ and Nd^3＋ on A-site are fine dispersed, and mean particle size less than 100 nm. The powders have good sinterability, and the relative density is 95% after sintered at 1200 ℃ for 2 h. It is found that all specimens are entirely single phase solid solutions with orthorhombic perovskite structure, the stable perovskitetype phase is formed completely after calcination at 900 ℃.
