At different annealing temperatures, the saturation magnetostrictions and the correlation between the permeability μi and the temperature T （μi-T curves） of the Co66Fe4Mo2Si16B12 alloy were investigated using a sm...At different annealing temperatures, the saturation magnetostrictions and the correlation between the permeability μi and the temperature T （μi-T curves） of the Co66Fe4Mo2Si16B12 alloy were investigated using a small-angle magnetization tester and core tester. The experimental results showed that the μi-T curves had different shapes at different ranges of annealing temperature; the permeability μi of the alloy improved with the increase of the annealing temperatures below 460℃; when the alloy was annealed above 480℃, the poor magnetic properties were considered to be caused by larger saturation magnetostriction.展开更多
As a new solid state welding,pinless friction stir welding（PFSW） can be used to join thin-wall structures.In this study,four new pinless tools with different groove distributions were designed and manufactured in or...As a new solid state welding,pinless friction stir welding（PFSW） can be used to join thin-wall structures.In this study,four new pinless tools with different groove distributions were designed and manufactured in order to enrich technological storage of PFSW and obtain sound joint with high quality of alclad 2A12-T4 alloy.The results show that the small-obliquity tool is detrimental to the transfer of plasticized materials,resulting in the formation of kissing bond defect.For the through-groove tool or the large-curvature tool,bigger flashes form on the joint surface and alclad layer is observed in the nugget zone（NZ）,deteriorating mechanical properties.Compared with the above-mentioned three tools,using the six-groove tool with rational curvature and obliquity can not only yield sound joint with small flashes and thickness reduction,but also prevent alclad from flowing into NZ,which has potential to weld thin alclad aluminum alloys.Meanwhile,the tensile strength and elongation of joint using the six-groove tool reach the maximum values of 362 MPa and 8.3%,up to 85.1% and 64% of BM.展开更多
文摘At different annealing temperatures, the saturation magnetostrictions and the correlation between the permeability μi and the temperature T （μi-T curves） of the Co66Fe4Mo2Si16B12 alloy were investigated using a small-angle magnetization tester and core tester. The experimental results showed that the μi-T curves had different shapes at different ranges of annealing temperature; the permeability μi of the alloy improved with the increase of the annealing temperatures below 460℃; when the alloy was annealed above 480℃, the poor magnetic properties were considered to be caused by larger saturation magnetostriction.
基金supported by the National Natural Science Foundation of China(No.51204111)the Natural Science Foundation of Liaoning Province(No.2014024008)the Aeronautical Science Foundation of China(No.2014ZE54021)
文摘As a new solid state welding,pinless friction stir welding（PFSW） can be used to join thin-wall structures.In this study,four new pinless tools with different groove distributions were designed and manufactured in order to enrich technological storage of PFSW and obtain sound joint with high quality of alclad 2A12-T4 alloy.The results show that the small-obliquity tool is detrimental to the transfer of plasticized materials,resulting in the formation of kissing bond defect.For the through-groove tool or the large-curvature tool,bigger flashes form on the joint surface and alclad layer is observed in the nugget zone（NZ）,deteriorating mechanical properties.Compared with the above-mentioned three tools,using the six-groove tool with rational curvature and obliquity can not only yield sound joint with small flashes and thickness reduction,but also prevent alclad from flowing into NZ,which has potential to weld thin alclad aluminum alloys.Meanwhile,the tensile strength and elongation of joint using the six-groove tool reach the maximum values of 362 MPa and 8.3%,up to 85.1% and 64% of BM.