La_(4)NiLiO_(8)-coated NCM622 samples were prepared through a sol-gel method,and the electrochemical performance as cathode materials was investigated.It is revealed that part of the introduced La^(3+)ions produce a c...La_(4)NiLiO_(8)-coated NCM622 samples were prepared through a sol-gel method,and the electrochemical performance as cathode materials was investigated.It is revealed that part of the introduced La^(3+)ions produce a coating layer on the surface of NCM622 particles,while the rest occupy the 3b position of the lattice.The optimized sample exhibits a capacity retention of 96.54%after 100 cycles under 1C rate with a discharge specific capacity of 117.54 mAh·g^(-1)under 5C rate,much higher than those of the unmodified sample.The results show that the addition of La^(3+)ion can greatly improve the cyclic stability and the rate performance of NCM622.展开更多
In order to avoid the formation ofηphase(W_(6)Co_(6)C or W_(3)Co_(3)C)that adversely affects the sintering process and its products in the preparation process of ultra-fine WC-Co powder,a technical route of prereduct...In order to avoid the formation ofηphase(W_(6)Co_(6)C or W_(3)Co_(3)C)that adversely affects the sintering process and its products in the preparation process of ultra-fine WC-Co powder,a technical route of prereduction of WO_(3)-Co_(3)O_(4)to WO_(2)-Co and then deep reduction carbonization to WC-Co powder has been proposed.This study mainly investigates the influence of gas partial pressure on the pre-reduction process of WO_(3)-Co_(3)O_(4)under a mixed atmosphere of H_(2)-C_(2)H_(4)-Ar at 600℃and establishes the kinetic equations of pre-reduction and carbon evolution.The results indicate that increasing the partial pressure of hydrogen is conducive to the rapid and complete conversion of WO_(3) to WO_(2).High carbon content can be generated by the deposition of C_(2)H_(4),and it hinders the diffusion of the reducing gas;WO_(3)still cannot be completely reduced to WO_(2)as the partial pressure of C_(2)H_(4) increases to 60%.For the carbon evolution of C_(2)H_(4),the carbon amount is positively related to the H_(2)partial pressure,but it shows the highest amount and evolution rate when the ethylene partial pressure is 20%.Based on the reduction rate curves of WO_(3) and carbon evolution rate curves of C_(2)H_(4),the rate equations of pre-reduction and carbon evolution of WO_(3)-Co_(3)O_(4)system at 600℃are established.The pre-reduction reaction belongs to the first-order reaction,and its equation is expressed as follows:r=-(dw_(WO_(3)))/dt=(9±0.15)×10^(-2)×P_(H_(2))^(0.44)P_(C_(2)H_(4))&(0.57)The carbon deposition rate equation of C_(2)H_(4) can be expressed as follows:r=-(dc_C)/dt=r_f-r_b≌7.35×10^(-2)×P_(C_(2)H_(4))^(0.31)展开更多
基金Funded by the Guangdong Key R&D Program(Nos.2020B 0909040001 and 2019B090909003)。
文摘La_(4)NiLiO_(8)-coated NCM622 samples were prepared through a sol-gel method,and the electrochemical performance as cathode materials was investigated.It is revealed that part of the introduced La^(3+)ions produce a coating layer on the surface of NCM622 particles,while the rest occupy the 3b position of the lattice.The optimized sample exhibits a capacity retention of 96.54%after 100 cycles under 1C rate with a discharge specific capacity of 117.54 mAh·g^(-1)under 5C rate,much higher than those of the unmodified sample.The results show that the addition of La^(3+)ion can greatly improve the cyclic stability and the rate performance of NCM622.
基金the National Natural Science Foundation of China(22078326,21878305,21908227)。
文摘In order to avoid the formation ofηphase(W_(6)Co_(6)C or W_(3)Co_(3)C)that adversely affects the sintering process and its products in the preparation process of ultra-fine WC-Co powder,a technical route of prereduction of WO_(3)-Co_(3)O_(4)to WO_(2)-Co and then deep reduction carbonization to WC-Co powder has been proposed.This study mainly investigates the influence of gas partial pressure on the pre-reduction process of WO_(3)-Co_(3)O_(4)under a mixed atmosphere of H_(2)-C_(2)H_(4)-Ar at 600℃and establishes the kinetic equations of pre-reduction and carbon evolution.The results indicate that increasing the partial pressure of hydrogen is conducive to the rapid and complete conversion of WO_(3) to WO_(2).High carbon content can be generated by the deposition of C_(2)H_(4),and it hinders the diffusion of the reducing gas;WO_(3)still cannot be completely reduced to WO_(2)as the partial pressure of C_(2)H_(4) increases to 60%.For the carbon evolution of C_(2)H_(4),the carbon amount is positively related to the H_(2)partial pressure,but it shows the highest amount and evolution rate when the ethylene partial pressure is 20%.Based on the reduction rate curves of WO_(3) and carbon evolution rate curves of C_(2)H_(4),the rate equations of pre-reduction and carbon evolution of WO_(3)-Co_(3)O_(4)system at 600℃are established.The pre-reduction reaction belongs to the first-order reaction,and its equation is expressed as follows:r=-(dw_(WO_(3)))/dt=(9±0.15)×10^(-2)×P_(H_(2))^(0.44)P_(C_(2)H_(4))&(0.57)The carbon deposition rate equation of C_(2)H_(4) can be expressed as follows:r=-(dc_C)/dt=r_f-r_b≌7.35×10^(-2)×P_(C_(2)H_(4))^(0.31)